A kind of fiber with antibacterial and deodorizing properties and preparation method thereof

A fiber and performance technology, applied in the field of fiber with antibacterial and deodorizing properties and its preparation, can solve the problems of inapplicability, and achieve the effects of suppressing sweat odor, good exhaust characteristics, and good toughness

Active Publication Date: 2022-04-01
上海茂腾针织有限公司
View PDF19 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the application of this material is mainly in superabsorbent resins, not suitable for clothing fiber materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of fiber with antibacterial and deodorizing properties and preparation method thereof
  • A kind of fiber with antibacterial and deodorizing properties and preparation method thereof
  • A kind of fiber with antibacterial and deodorizing properties and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Terephthalonitrile as raw material for synthesis of tetrazine polymer

[0031] Dissolve 0.5 g of terephthalonitrile in 10 mL of 80% hydrazine hydrate, and add 0.2 g of sulfur powder. After ultrasonic dispersion, place in a closed pressure vessel. Raise the temperature to 80°C, react for 6 hours, lower the temperature, and ultrasonically disperse. Then heated to 150°C, continued the reaction for 2 days, and filtered to obtain a light red solid sponge.

[0032] Grind the solid matter into pieces, infiltrate with 95% alcohol, ultrasonicate for 5 minutes each, and dry after 4 times. The second spherical pulverizer grinds to extremely fine nano powder, which is ready for use.

Embodiment 2

[0034] Synthesis of Tetrazine Polymer Using Malonylhydrazide as Raw Material

[0035] Dissolve 0.5 g of p-malonylhydrazide in 10 mL of 80% hydrazine hydrate, and add 0.4 g of sulfur powder. After ultrasonic dispersion, place in a closed pressure vessel. Raise the temperature to 80°C, react for 6 hours, lower the temperature, and ultrasonically disperse. Then heated to 150°C, continued the reaction for 2 days, and filtered to obtain a light red solid sponge.

[0036] Grind the solid matter into pieces, infiltrate with 95% alcohol, ultrasonicate for 5 minutes each, and dry after 4 times. The second spherical pulverizer grinds to extremely fine nano powder, which is ready for use.

[0037] Tetrazine Polymer Blends

[0038] PET electrospinning

Embodiment 3

[0040] After mixing 2 parts of the product of Example 1, 96 parts of oil bottle grade PET and 2 parts of a tackifier, they were fully stirred and dissolved in hexafluoroisopropanol to prepare a transparent and uniform electrospinning solution with a concentration of 10%. Use model KH1003 electrospinning apparatus, spinning voltage 25kv, stainless steel needle, advance speed 0.001mm / s, fibers are collected on aluminum foil, receiving distance is 15cm, used for sample testing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a fiber with antibacterial and deodorizing properties, which is characterized in that the raw material contains a tetrazine high molecular polymer, wherein the mass fraction of the tetrazine high molecular polymer in the fiber is 1-5%. This application has good antibacterial effect.

Description

technical field [0001] The invention relates to the technical field of functional fibers, in particular to a fiber with antibacterial and deodorizing properties and a preparation method thereof. Background technique [0002] Clothing and its fiber materials, as an important part of basic necessities of life, have undergone great changes during the development of human civilization and society. With the development of modern science, clothing materials are gradually replaced by synthetic fibers such as polyester (polyester) and acrylic (polyacrylonitrile) from traditional natural fibers such as wool, cotton, and hemp. In recent years, new modified fiber modal Fibers and the like have become popular objects because of their advantages of both natural fibers and synthetic fibers. [0003] Usually, in the processing of fiber fabrics, by choosing different fiber polymer materials, clothing can be endowed with important basic properties such as body feeling, elasticity, lightness...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F1/10D01F6/48D01F6/92C08G73/06
CPCD01F1/103D01F6/92D01F6/48C08G73/0638C08G73/065
Inventor 林资富
Owner 上海茂腾针织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com