Ceramic fiber wood plastic and manufacturing method thereof

A technology of ceramic fiber and manufacturing method, applied in the field of ceramic fiber wood plastic and its manufacturing, can solve the problems affecting the safety and life of wood plastic products, fire performance, poor sound insulation performance, and defects in the use performance of wood plastic products, etc. Anti-radiation effect, good thermal insulation performance, improving safety and service life

Inactive Publication Date: 2020-03-27
沈阳科洛环保科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a ceramic fiber wood-plastic and its manufacturing method in order to solve the above problems, which solves the problem that the current wood-plastic products have poor fireproof performance and sound insulation performance. It is necessary to add a fireproof layer or a sound insulation layer on the wood-plastic products before using them, which will cause inconvenience caused by defects in the performance of wood-plastic products, and affect the safety and life of wood-plastic products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic fiber wood plastic and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of ceramic fiber wood plastic, the wood plastic component includes 50 parts of plant fiber, 17 parts of ceramic fiber, 12 parts of porous ceramic particles, 16 parts of thermoplastic resin, 6 parts of glass fiber, 4 parts of flame retardant, surface 5 parts of modifier, 3 parts of stabilizer, 3 parts of foaming agent, 2 parts of foam regulator, 1 part of coupling agent.

[0029] Further, the diameter of the ceramic fibers is between 0.1-10 μm, and the ceramic fibers with a diameter of no more than 4 μm account for 75-90% of the total amount of ceramic fibers.

[0030] Further, the diameter of the porous ceramic particles is between 1.5-3mm.

[0031] Further, the plant fiber is one or more of wood flour, rice husk, crop straw, and waste paper.

[0032] Further, the diameter of the plant fibers is between 1-4 mm, and the plant fibers with a diameter of no more than 2.5 mm account for 65-75% of the total plant fibers.

[0033] Further, the thermoplastic resin is a...

Embodiment 2

[0046] A kind of ceramic fiber wood plastic, the wood plastic component includes 58 parts of plant fiber, 15 parts of ceramic fiber, 10 parts of porous ceramic particles, 18 parts of thermoplastic resin, 5 parts of glass fiber, 5 parts of flame retardant, surface 4 parts of modifier, 4 parts of stabilizer, 5 parts of foaming agent, 3 parts of foam regulator, 1 part of coupling agent.

[0047] Further, the diameter of the ceramic fibers is between 0.1-10 μm, and the ceramic fibers with a diameter of no more than 4 μm account for 75-90% of the total amount of ceramic fibers.

[0048] Further, the diameter of the porous ceramic particles is between 1.5-3mm.

[0049] Further, the plant fiber is one or more of wood flour, rice husk, crop straw, and waste paper.

[0050] Further, the diameter of the plant fibers is between 1-4 mm, and the plant fibers with a diameter of no more than 2.5 mm account for 65-75% of the total plant fibers.

[0051] Further, the thermoplastic resin is a...

Embodiment 3

[0064] A kind of ceramic fiber wood plastic, the wood plastic component includes 40 parts of plant fiber, 20 parts of ceramic fiber, 15 parts of porous ceramic particles, 15 parts of thermoplastic resin, 7 parts of glass fiber, 3 parts of flame retardant, surface 7 parts of modifier, 2 parts of stabilizer, 2 parts of foaming agent, 1 part of foam regulator, and 1 part of coupling agent.

[0065] Further, the diameter of the ceramic fibers is between 0.1-10 μm, and the ceramic fibers with a diameter of no more than 4 μm account for 75-90% of the total amount of ceramic fibers.

[0066] Further, the diameter of the porous ceramic particles is between 1.5-3mm.

[0067] Further, the plant fiber is one or more of wood flour, rice husk, crop straw, and waste paper.

[0068] Further, the diameter of the plant fibers is between 1-4 mm, and the plant fibers with a diameter of no more than 2.5 mm account for 65-75% of the total plant fibers.

[0069] Further, the thermoplastic resin i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a ceramic fiber wood plastic comprising in parts by weight: 35-60 parts of plant fibers, 15-20 parts of ceramic fibers, 10-15 parts of porous ceramic particles, 15-18 parts ofa thermoplastic resin, 5-7 parts of glass fibers, 3-5 parts of a flame retardant, 3-7 parts of a surface modifier, 2-4 parts of a stabilizer, 2-5 parts of a foaming agent, 1-3 parts of a foaming regulator and 1 part of a coupling agent. The beneficial effects are that: by utilizing the advantages of ceramic fibers, wood-plastic products containing the ceramic fiber component are excellent refractory materials; the heat insulation performance and the high-temperature heat insulation performance are good; the use safety is improved and the service life is prolonged; echo absorption and elimination performance of porous ceramic particles is achieved, the sound absorption and insulation performance of the wood-plastic products is improved, the suitable range is wider; at the same time, glass fiber material possesses excellent radiation resistance, so that the wood-plastic products possess radiation resistance; the advantages of simple and feasible process, convenient operation and control,easy realization of batch production, energy saving and environmental protection are achieved.

Description

Technical field: [0001] The invention belongs to the technical field of wood-plastic, and in particular relates to a ceramic fiber wood-plastic and a manufacturing method thereof. Background technique: [0002] Wood-plastic composite material, that is, wood-plastic, wood-plastic composite material contains plastic, so it has a good modulus of elasticity. In addition, because it contains fibers and is fully mixed with plastic, it has the same compression and bending resistance as hardwood. And other physical and mechanical properties, and its durability is significantly better than ordinary wood materials, and its surface hardness is high, generally 2-5 times that of wood. It is a new type of composite material that has boomed in recent years at home and abroad. [0003] At present, the fireproof performance and sound insulation performance of wood-plastic products are poor. Under the condition of high fireproof requirements or sound insulation requirements, it is necessary t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L23/06C08L23/12C08L27/06C08K13/04C08K7/04C08K7/24C08K7/14C08J9/04
CPCC08J9/0061C08J9/0066C08J9/0085C08J9/04C08J2397/02C08J2423/06C08J2423/12C08J2427/06C08K7/04C08K7/14C08K7/24C08K13/04
Inventor 董斌
Owner 沈阳科洛环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com