A kind of r-t-b series permanent magnet material and its preparation method and application

A technology of R-T-B and permanent magnet materials, which is applied in the fields of magnetic materials, inductor/transformer/magnet manufacturing, magnetic objects, etc. It can solve the problems of over-reliance on performance improvement of sintered NdFeB magnets, achieve high coercive force and reduce production costs , The effect of saving the amount of utilization

Active Publication Date: 2021-08-27
FUJIAN CHANGTING GOLDEN DRAGON RARE EARTH CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to overcome the defect that the performance improvement of sintered NdFeB magnets in the prior art is excessively dependent on heavy rare earth elements, and to provide an R-T-B permanent magnet material and its preparation method and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of r-t-b series permanent magnet material and its preparation method and application
  • A kind of r-t-b series permanent magnet material and its preparation method and application
  • A kind of r-t-b series permanent magnet material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0165] The preparation method of R-T-B series sintered magnet is as follows:

[0166] (1) Melting process: according to the formula shown in Table 1, take the prepared raw materials and put them into a crucible made of alumina, and put them in a high-frequency vacuum induction melting furnace at 5×10 -2 Vacuum melting is carried out at a temperature below 1500°C in a vacuum of Pa.

[0167] (2) Casting process: after vacuum smelting, Ar gas is passed into the smelting furnace to make the air pressure reach 55,000 Pa, and then casting is carried out at 10 2 ℃ / sec-10 4 °C / sec cooling rate to obtain quenched alloy.

[0168] (3) Hydrogen crushing process: Vacuumize the hydrogen crushing furnace where the quenched alloy is placed at room temperature, and then pass hydrogen gas with a purity of 99.9% into the hydrogen crushing furnace to maintain the hydrogen pressure at 0.15 MPa. After fully absorbing hydrogen, Heat up while evacuating to fully dehydrogenate, then cool, and take ...

Embodiment 2- Embodiment 59

[0175] The raw materials were prepared according to the formula shown in Table 1, and the other process conditions were the same as in Example 1 to obtain the R-T-B series sintered magnet.

Embodiment 60

[0177] The sintered body obtained in Example 55 was first subjected to grain boundary diffusion treatment, and then to aging treatment. Wherein, the aging treatment process is the same as in Example 1, and the grain boundary diffusion treatment process is as follows:

[0178] Process the sintered body into a magnet with a diameter of 20mm and a sheet thickness of less than 3mm. The direction of thickness is the orientation direction of the magnetic field. The magnet is dried, and in a high-purity Ar gas atmosphere, the metal with Tb element is sputtered on the surface of the magnet, and the temperature of 850°C is diffused and heat-treated for 24 hours. Cool to room temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an R-T-B permanent magnet material, a preparation method and an application thereof. The R-T-B is a permanent magnet material, which includes the following components: R': 29.5-33.0wt.%, said R' includes R and Pr, Nd; wherein: said R is except for Pr, Nd Rare earth elements, the content of the Pr ≥ 8.85wt.%, the mass ratio of the Nd and the R' <0.5; N: > 0.05wt.%, and ≤ 4.1wt.%, the N is Ti, Zr or Nb; B: 0.90‑1.2 wt.%; Fe: 62.0‑68.0 wt.%. The present invention uses a formula with high Pr content to prepare a sintered permanent magnet product with high coercive force and stable temperature coefficient. The formula of this application can maximize the advantages of Pr and effectively reduce production costs.

Description

technical field [0001] The invention relates to an R-T-B series permanent magnet material and its preparation method and application. Background technique [0002] Nd was discovered by Soviet scientists in 1979 2 Fe 14 Since B, researchers in the United States and Japan have taken the lead in studying the properties of this phase. At present, the phase composed of PrNd (the mass ratio of Pr and Nd is 20:80 or 25:75) has been used in commercial sintering. The production of magnets, due to its advantages of high magnetic energy product and high remanence, has been used in motors, electro-acoustic devices, computer hard disk drives (HDD), military equipment, human magnetic resonance imaging (MRI), microwave communication technology, control It has been widely used in devices, instruments and so on. [0003] With the advancement of science and technology, higher requirements are put forward for the performance of Nd-Fe-B. Many researchers have improved the performance of Nd-F...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F1/057H01F41/02
CPCH01F1/0577H01F41/0253H01F41/0266C22C38/008C22C38/16C22C38/12C22C38/14C22C38/002H01F1/0573H01F41/0293C22C38/005C22C2202/02C22C38/06C22C38/10C22C38/32
Inventor 付刚黄佳莹黄吉祥权其琛
Owner FUJIAN CHANGTING GOLDEN DRAGON RARE EARTH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com