A kind of waterproof and oil-proof non-woven fabric and its manufacturing process

A technology of waterproof and oil-proof, production process, applied in the direction of sustainable manufacturing/processing, textile/flexible product manufacturing, non-woven fabrics, etc., can solve the problem of poor waterproof and oil-proof performance of waterproof and oil-proof non-woven fabrics Poor cloth elasticity, easy to lose waterproof and oil-proof performance, etc., achieve good waterproof and oil-proof effect, save manpower and equipment costs, and have good waterproof and oil-proof effect

Active Publication Date: 2021-04-27
FUJIAN GUAN HONG IND
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015] 1. The existing method of preparing waterproof and oil-proof non-woven fabrics is generally to manufacture non-functional non-woven fabrics first, and then immerse the non-woven fabrics in the three-proof finishing agent for impregnation, so as to obtain waterproof and oil-proof non-woven fabrics. High-performance non-woven fabrics, but although there are many kinds of polymers in the method, the waterproof and oil-proof non-woven fabrics obtained have poor waterproof and oil-proof performance, and the waterproof and oil-proof performance (function) is temporary. It is easy to lose the waterproof and oil-proof performance when rubbing against other objects;
[0016] 2. Waterproof and oil-proof non-woven fabrics have poor elasticity, low softness, slightly irritating to the skin, and poor comfort

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of waterproof and oil-proof non-woven fabric and its manufacturing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A waterproof and oil-proof non-woven fabric, which is made of the following raw materials in parts by weight: 65-75 parts of polypropylene, 16-22 parts of maleic anhydride grafted ethylene-octene copolymer, PP-g-AA graft copolymer 8-13 parts of compound, 2-4 parts of amino-modified polysiloxane emulsion, 5-8 parts of polyvinylidene fluoride-hexafluoropropylene copolymer, 4-7 parts of fluorine-containing polyacrylic acid ester, and 9-15 parts of filler.

[0040] Preferably, the waterproof and oil-proof nonwoven fabric is made of the following raw materials in parts by weight: 70 parts of polypropylene, 19.3 parts of maleic anhydride grafted ethylene-octene copolymer, 10.5 parts of PP-g-AA grafted copolymer 3.4 parts of amino-modified polysiloxane emulsion, 6.7 parts of polyvinylidene fluoride-hexafluoropropylene copolymer, 5.2 parts of fluorine-containing polyacrylic acid ester, and 12 parts of filler.

[0041] Preferably, the polypropylene has a melting point of 160-170...

Embodiment 2

[0053] A waterproof and oil-proof non-woven fabric, made of raw materials comprising the following parts by weight: 65 parts of polypropylene, 16 parts of maleic anhydride grafted ethylene-octene copolymer, 8 parts of PP-g-AA graft copolymer, 2 parts of amino-modified polysiloxane emulsion, 5 parts of polyvinylidene fluoride-hexafluoropropylene copolymer, 4 parts of fluorine-containing polyacrylic acid ester, and 9 parts of filler.

[0054] In this embodiment, the polypropylene has a melting point of 160° C. and a melt index of 12 g / 10 min.

[0055] In this embodiment, the maleic anhydride graft ratio of the maleic anhydride grafted ethylene-octene copolymer is 0.9%.

[0056] In this embodiment, the acrylic acid grafting rate of the PP-g-AA graft copolymer is 1.6%.

[0057] In this embodiment, the filler is nano calcium carbonate.

[0058] In the present embodiment, the manufacturing process of the waterproof and oil-proof non-woven fabric includes the following steps:

[0...

Embodiment 3

[0066] A waterproof and oil-proof non-woven fabric, made of raw materials comprising the following parts by weight: 75 parts of polypropylene, 22 parts of maleic anhydride grafted ethylene-octene copolymer, 13 parts of PP-g-AA graft copolymer, 4 parts of amino-modified polysiloxane emulsion, 8 parts of polyvinylidene fluoride-hexafluoropropylene copolymer, 7 parts of fluorine-containing polyacrylic acid ester, and 15 parts of filler.

[0067] In this embodiment, the polypropylene has a melting point of 170° C. and a melt index of 16 g / 10 min.

[0068] In this embodiment, the maleic anhydride grafting ratio of the maleic anhydride grafted ethylene-octene copolymer is 1.2%.

[0069] In this embodiment, the acrylic acid grafting rate of the PP-g-AA graft copolymer is 2.3%.

[0070] In this embodiment, the filler is nano calcium carbonate.

[0071] In the present embodiment, the manufacturing process of the waterproof and oil-proof non-woven fabric includes the following steps: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melt flow indexaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a waterproof and oil-proof non-woven fabric and a manufacturing process thereof. The waterproof and oil-proof non-woven fabric is made of the following raw materials in parts by weight: 65-75 parts of polypropylene, maleic anhydride grafted ethylene-octyl 16-22 parts of vinylene copolymer, 8-13 parts of PP-g-AA graft copolymer, 2-4 parts of amino-modified polysiloxane emulsion, 5-8 parts of polyvinylidene fluoride-hexafluoropropylene copolymer, 4-7 parts of fluorine-containing polyacrylic acid ester, 9-15 parts of filler. The waterproof and oil-proof non-woven fabric of the present invention has a good waterproof and oil-proof effect, and the waterproof and oil-proof effect is long-lasting, and it is not easy to lose the waterproof and oil-proof performance when it is contacted with a solvent or washed or rubbed with other objects afterwards. In addition, it also has good elasticity And softness, non-irritating to the skin, high wearing comfort.

Description

technical field [0001] The invention relates to the technical field of non-woven fabrics, in particular to a waterproof and oil-proof non-woven fabric and a manufacturing process thereof. Background technique [0002] The fibers used in the production of non-woven fabrics are mainly polypropylene (PP) and polyester (PET). In addition, there are nylon (PA), viscose fiber, acrylic fiber, polyethylene fiber (HDPE), and chlorine fiber (PVC). According to application requirements, non-woven fabrics are divided into two categories: disposable application type and durable type. [0003] According to the production process, it is divided into: [0004] 1. Spunlace non-woven fabric: The spunlace process is to spray high-pressure fine water flow onto one or more layers of fiber nets, so that the fibers are entangled with each other, so that the fiber nets can be reinforced and have a certain strength. [0005] 2. Heat-bonded non-woven fabric: heat-bonded non-woven fabric refers to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04H3/005D04H3/11
CPCD04H3/11D04H3/007Y02P70/62
Inventor 陈解忧黄冠儒张洛泓
Owner FUJIAN GUAN HONG IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com