Bright red glaze for ceramics, and preparation method thereof

A technology of bright red and glaze, which is applied in the field of bright red glaze for ceramics and its preparation, can solve the problems of health hazards of operators, leakage of cadmium dust and cadmium dust, and increase of glaze processing cost, etc., so as to improve the quality of processing environment and save energy. Storage costs, the effect of ensuring good health

Active Publication Date: 2020-01-14
临沂晶石陶瓷有限公司
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, during the actual production of the glaze in the above-mentioned technical solution, the inventors observed that the cadmium carbonate used as a flux in the glaze is highly toxic and irritating, requiring storage environment and processing environment. They are all very high, which increases the glaze processing cost to a certain extent, and it is inevitable that some cadmium compounds and cadmium dust will leak during processing, which brings potential harm to the health of operators.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bright red glaze for ceramics, and preparation method thereof
  • Bright red glaze for ceramics, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A bright red glaze for ceramics, which is composed of the following components by weight: 30 parts of potassium feldspar, 18 parts of quartz, 6 parts of marble, 8 parts of kaolin, 6 parts of transparent frit, 50 parts of water, and 2 parts of bright red material , 1 part of red coral stone powder.

[0027] Its preparation method is as follows:

[0028] Step 1, after the red coral stone is crushed, ball milling is carried out, and the powder obtained after ball milling is passed through a 325-mesh standard sieve to obtain red coral stone powder for use;

[0029] Step 2: Mix 30 parts of potassium feldspar, 18 parts of quartz, 6 parts of marble, 8 parts of kaolin, 6 parts of transparent frit, and 50 parts of water, and ball mill it into glaze slurry. The ball milling time is 16 hours, and the magnetic field strength of the glaze slurry is The 10,000 Gauss iron remover removes iron three times, and the glaze slurry passes through a 325-mesh standard sieve;

[0030] Step 3...

Embodiment 2

[0033] A bright red glaze for ceramics, which consists of the following components by weight: 50 parts of potassium feldspar, 38 parts of quartz, 13 parts of marble, 15 parts of kaolin, 10 parts of transparent frit, 70 parts of water, and 8 parts of bright red material , 3 parts of red coral stone powder.

[0034] Its preparation method is as follows:

[0035] Step 1, after crushing the red coral stone, ball milling is carried out, and the powder obtained after ball milling is passed through a 380-mesh standard sieve to obtain red coral stone powder for use;

[0036] Step 2: Mix 50 parts of potassium feldspar, 38 parts of quartz, 13 parts of marble, 15 parts of kaolin, 10 parts of transparent frit, and 70 parts of water, and ball mill it into glaze slurry. The 10,000 gauss iron remover removes iron 5 times, and the glaze slurry passes through a 380-mesh standard sieve;

[0037] Step 3, mix 8 parts of bright red material and 3 parts of red coral stone powder evenly and ball-m...

Embodiment 3

[0040] A bright red glaze for ceramics, which consists of the following components by weight: 45 parts of potassium feldspar, 30 parts of quartz, 10 parts of marble, 13 parts of kaolin, 9 parts of transparent frit, 65 parts of water, and 6 parts of bright red material , 2.5 parts of red coral stone powder.

[0041] Its preparation method is as follows:

[0042] Step 1, after crushing the red coral stone, ball milling is carried out, and the powder obtained after ball milling is passed through a 380-mesh standard sieve to obtain red coral stone powder for use;

[0043] Step 2: Mix 45 parts of potassium feldspar, 30 parts of quartz, 10 parts of marble, 13 parts of kaolin, 9 parts of transparent frit, and 65 parts of water, and ball mill it into glaze slurry. The 10,000 gauss iron remover removes iron 4 times, and the glaze slurry passes through a 380-mesh standard sieve;

[0044] Step 3, mix 6 parts of bright red material and 2.5 parts of red coral stone powder evenly and ball...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a bright red glaze for ceramics, and a preparation method thereof, and relates to the technical field of ceramic glazes, wherein the bright red glaze is prepared from the following components by weight: 30-50 parts of potassium feldspar, 18-38 parts of quartz, 6-13 parts of marble, 8-15 parts of kaolin, 6-10 parts of transparent frit, 50-70 parts of water, 2-8 parts of bright red pigment and 1-3 parts of red corallite powder. According to the invention, cadmium carbonate is replaced with the red corallite powder as the fluxing agent, wherein the main component of the red corallite powder is CaCO3, so that the requirement on the storage environment of the red corallite powder is low, and the storage cost of the raw materials is saved; the red corallite powder has redattribute, so that the use of the bright red pigment is reduced so as to further reduce the cost; by using the red corallite powder to replace cadmium carbonate, the toxic substances such as cadmiumcompounds, cadmium dust and the like cannot be generated in the processing process so as to further improve the processing environment quality and ensure the body health of operators.

Description

technical field [0001] The invention relates to the technical field of ceramic glazes, in particular to a scarlet glaze for ceramics and a preparation method thereof. Background technique [0002] The red in Chinese red porcelain means peace, auspiciousness, celebration, prosperity, longevity, nobility, harmony, reunion, success, etc. It has rich cultural connotations and lofty spiritual realm. With the continuous advancement of technology, Chinese red is gradually Applied to daily life utensils, the red porcelain that could only be enjoyed by the royal family in ancient times gradually entered our modern life. [0003] In the Chinese patent whose authorization notification number is CN102491794B, a kind of scarlet glaze for ceramics is disclosed, which consists of 30-50 parts of potassium feldspar, 20-40 parts of quartz, 5-15 parts of marble, 8-15 parts of kaolin, and transparent frit 6 to 10 parts, 0.1 to 0.5 parts of cadmium carbonate, 4 to 12 parts of scarlet material a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/02C03C8/14
CPCC03C8/02C03C8/14Y02P40/60
Inventor 黄志璇
Owner 临沂晶石陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap