Method for preparing antimony-free burnthrough-resistant waterborne flame-retardant adhesive for fabric coatings

A flame retardant adhesive and coating technology, applied in textiles and paper making, etc., can solve the problems of reduced burn through resistance, reduced flame retardant performance, and high flame retardant cost, and achieve good burn through resistance and good burn through resistance. , good carbonization effect

Inactive Publication Date: 2019-12-31
嘉兴市新加新化工有限公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Secondly, the carbonization is not good. When the polyester fabric is coated with this kind of flame retardant adhesive, it is easy to burn through. Sponge padding behind sofa release, sparking fire
[0006] Chinese patent application number 93115328..X discloses a flame retardant coating that can be used for fabric coating, Chinese patent application number CN20048002553.X discloses a kind of flame retardant for general fabric coating, Chinese patent application number CN101498105 .B, announced a kind of flame-retardant glue that is used for fabric coating, and these flame-retardant glues are coated on fabric, and fabric is very easy to be burnt through, thereby ignites the sponge covered behind fabric, although increase these flame-retardant The coating amount of glue may also pass the test, but the flame retardant cost is higher
[0007] Chinese patent application number 201610907466.9 discloses a fire-resistant water-based flame-retardant adhesive for textile use. Although it does not contain antimony and is not easy to burn-through, however, after coating this water-based flame-retardant adhesive on the fabric, wash it with 40 ° C water After soaking for 30 minutes, the flame retardant performance decreased, and the burn-through resistance decreased extremely. Again, there was a phenomenon of melting dripping, and the melting dripping was very easy to burn and scald

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing antimony-free burnthrough-resistant waterborne flame-retardant adhesive for fabric coatings
  • Method for preparing antimony-free burnthrough-resistant waterborne flame-retardant adhesive for fabric coatings
  • Method for preparing antimony-free burnthrough-resistant waterborne flame-retardant adhesive for fabric coatings

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] A method for preparing antimony-free burn-through-resistant water-based flame-retardant adhesive for fabric coating, step 1, raw material preparation, calculated by weight, including:

[0029]

[0030]

[0031] The total weight of raw materials is 100 parts;

[0032] The water-based resin in step 1 includes one or more of ethylene-vinyl acetate copolymer emulsion, acrylate emulsion, polyurethane emulsion, styrene-butadiene emulsion and nitrile emulsion, and the solid content of the water-based resin is 20%-60%;

[0033] Flame retardants in step 1 include hexabromocyclododecane (HBCD), decabromodiphenyl ether, decabromodiphenylethane, three (2,3-dibromopropyl) isocyanurate, bromine Triazine, ethylene bis-tetrabromophthalimide, tetrabromobisphenol A, octabromoether, methyl octabromoether, ammonium polyphosphate (APP), guanidine phosphate, amidinourea phosphate, melamine cyanide Urate (MCA), melamine phosphate, melamine pyrophosphate, chlorine ester resin, chlorinat...

Embodiment 1

[0048] A preparation method of antimony-free water-based flame-retardant adhesive for fabric coating,

[0049] Step 1, raw material preparation, calculated by weight, including:

[0050]

[0051]

[0052] The total weight of raw materials is 100 parts

[0053] Step 2, the preparation of polyvinyl alcohol solution,

[0054] In a container with a stirring device and a heating device, add 6 parts of polyvinyl alcohol, add 30 parts of water, start the agitator, stir at a slow speed for 1-4 hours, start the heating device, raise the temperature to 50-95 ° C, continue Stir for 2 hours to fully dissolve the polyvinyl alcohol. Continue to stir at a slow speed, add bactericide, defoamer and crosslinking agent to obtain polyvinyl alcohol aqueous solution, and discharge for later use;

[0055] Step 3, preparation of powder flame retardant aqueous dispersion,

[0056] In a container with a stirring device, add 10 parts of water, add the dispersant and wetting agent in the auxili...

Embodiment 2

[0062] A method for preparing antimony-free water-based flame-retardant adhesive for fabric coating, step 1, raw material preparation, calculated by weight, including:

[0063]

[0064] Step 2, the preparation of polyvinyl alcohol solution,

[0065] Add the polyvinyl alcohol (PVA 2488) in step 1 into the container with stirring device and heating device, add 30 parts of water, start the agitator, and stir at a slow speed for 1-4 hours. Start the heating device, raise the temperature to 80-95°C, continue to stir for 2 hours to fully dissolve the polyvinyl alcohol, add the crosslinking agent, bactericide and defoamer in the auxiliary agent in step 1, and continue to stir for 10-30 minutes. Prepare polyvinyl alcohol aqueous solution, stand-by;

[0066] Step 3, preparation of powder flame retardant aqueous dispersion,

[0067] In a container with a stirring device, add 15 parts of the water in step 1 to the dispersant and wetting agent in the auxiliary agent in step 1, stir f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of waterborne flame-retardant adhesives for fabric coatings and particularly relates to a method for preparing an antimony-free burnthrough-resistant waterborne flame-retardant adhesive for the fabric coatings. The method includes: step one, raw material preparation, to be specific, preparing, by weight, 20-40 parts of waterborne resin, 20-40 parts of aflame retardant, 2-10 parts of polyvinyl alcohol, 0.2-5 parts of auxiliary agents and 5-50 parts of water, wherein the total weight parts of the raw materials are 100. A finished product is preparedby procedures of polyvinyl alcohol solution preparation, powdery flame retardant aqueous dispersion preparation, phosphate flame retardant pretreatment, mixing and filtration. The method for preparingthe antimony-free burnthrough-resistant waterborne flame-retardant adhesive for the fabric coatings has advantages that without use of antimony trioxide, harms of residual heavy metals in antimony trioxide to human health are reduced; by adoption of polyvinyl alcohol as a carbonizing agent, excellent carbonization performance, burnthrough resistance and dripping resistance of fabrics are achieved, and the adhesive is especially applicable to the fabric flame-retardant coatings of mattresses, sofas, furniture covers, carpets, protective garments and the like.

Description

technical field [0001] The invention relates to the technical field of antimony-free water-based flame-retardant adhesive for fabric coating, in particular to a preparation method of antimony-free burn-through-resistant water-based flame-retardant adhesive for fabric coating. Background technique [0002] In recent years, with the progress of society and the improvement of people's living standards, the consumption of various civil and industrial textiles has increased rapidly, especially various interior decoration fabrics such as curtains, curtains, wall coverings, carpets, furniture cloth and bedding And the demand for tent fabrics and automotive interior fabrics is also increasing day by day. At the same time, the number of fires caused by textile fires has also continued to increase, causing serious economic losses and casualties. Therefore, it is very meaningful to reduce the loss of life and property by flame-retardant treatment of textiles to delay the spread of fir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/04D06N3/14D06N3/10D06N3/00
CPCD06N3/0059D06N3/0061D06N3/0063D06N3/04D06N3/042D06N3/10D06N3/14D06N2209/067
Inventor 吕东青吕向成刘振轩
Owner 嘉兴市新加新化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com