Preparation method of heat-preservation and heat-insulation tent composite fabric

A composite fabric, thermal insulation technology, applied in the field of textile fabrics, can solve the problems of high thermal conductivity and achieve the effects of high melting temperature, strong tolerance, good mechanical properties and flexibility

Pending Publication Date: 2019-11-22
肖时云
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The technical problem to be solved by the present invention: Aiming at the problem of high thermal conductivity of existing tent fabrics, a preparation method of thermal insulation tent composite fabric is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] In parts by weight, weigh 10 parts of ethyl orthosilicate, 5 parts of polyimide, 20 parts of absolute ethanol, 1 part of hydrochloric acid solution with a mass fraction of 1%, 0.5 parts of N,N-dimethylformaldehyde Amide, 0.80 parts by mass fraction of 2% ammonia water, 60 parts of deionized water, mixed ethyl orthosilicate, absolute ethanol and deionized water, and magnetically stirred at a stirring speed of 300r / min for 8min to obtain the reaction solution A , add 1% hydrochloric acid solution and polyimide into the reaction solution A, continue to stir for 25 minutes to obtain the reaction solution B, hydrolyze the reaction solution B at a water bath temperature of 30°C for 30 minutes, and obtain the mixed solution. Add N,N-dimethylformamide and ammonia water with a mass fraction of 2% in the mixed solution dropwise, control the dropping rate to 0.025mL / min, and magnetically stir at a stirring rate of 500r / min for 1h to obtain a mixed sol; The sol was replaced in n-bu...

Embodiment 2

[0032] In parts by weight, weigh 15 parts of ethyl orthosilicate, 8 parts of polyimide, 25 parts of absolute ethanol, 2 parts of 1% hydrochloric acid solution, 0.6 parts of N,N-dimethylformaldehyde Amide, 1.0 parts of ammonia water with a mass fraction of 2%, 70 parts of deionized water, mixed ethyl orthosilicate, absolute ethanol and deionized water, and magnetically stirred at a stirring speed of 350r / min for 9min to obtain the reaction solution A , add 1% hydrochloric acid solution and polyimide into the reaction solution A, and continue to stir for 28 minutes to obtain the reaction solution B. The reaction solution B is hydrolyzed at a water bath temperature of 32°C for 40 minutes to obtain a mixed solution. Add N,N-dimethylformamide and ammonia water with a mass fraction of 2% in the mixed solution dropwise, control the dropping rate to 0.028mL / min, and magnetically stir for 1h at a stirring speed of 600r / min to obtain a mixed sol; The sol was replaced in n-butanol and n-...

Embodiment 3

[0034] In parts by weight, weigh 20 parts of tetraethyl orthosilicate, 10 parts of polyimide, 30 parts of absolute ethanol, 3 parts of 1% hydrochloric acid solution, 0.7 parts of N, N-dimethylformaldehyde Amide, 1.2 parts of ammonia water with a mass fraction of 2%, 80 parts of deionized water, mixed ethyl orthosilicate, absolute ethanol and deionized water, and magnetically stirred at a stirring speed of 400r / min for 10min to obtain the reaction solution A , add 1% hydrochloric acid solution and polyimide into the reaction solution A, and continue to stir for 30 minutes to obtain the reaction solution B. The reaction solution B is hydrolyzed at a water bath temperature of 35°C for 50 minutes to obtain a mixed solution. Add N,N-dimethylformamide and ammonia water with a mass fraction of 2% in the mixed solution dropwise, control the dropping rate to 0.030mL / min, and magnetically stir for 2h at a stirring rate of 700r / min to obtain a mixed sol; The sol was replaced in n-butanol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a heat-preservation and heat-insulation tent composite fabric, and belongs to the technical field of textile fabrics. Polyimide modified silicon dioxide aerogel is used as a coating, a fabric prepared from polyurethane modified polybenzimidazole fibers is used as base cloth, the coating is coated between the two layers of base cloth, and the heat-preservation and heat-insulation tent composite fabric is prepared through hot pressing and has good weather resistance, flame retardance, water resistance, ultraviolet resistance and other functions. The polybenzimidazole fiber has outstanding high temperature resistance and good waterproof performance; the silicon dioxide aerogel has the obvious characteristics of a nanometer material; good optical performance, sound absorption performance, chemical stability, environmental protection performance and excellent heat preservation and heat insulation performance are realized; polyimide has good mechanical property and flexibility and low thermal conductivity, and the prepared film has good flexibility and can be bent and folded, so that the polyimide modified silicon dioxide aerogel has goodmechanical property and thermal insulation property.

Description

technical field [0001] The invention relates to a preparation method of a thermal insulation tent composite fabric, which belongs to the technical field of textile fabrics. Background technique [0002] With the improvement of people's living standards, the rapid development of tourism has driven the development of outdoor textiles, and the demand for outdoor camping tents is increasing. The requirements for tent textiles are also getting higher and higher. In addition to basic waterproof and tear-resistant properties, tent textiles also require higher performance such as thermal insulation, UV protection, radiation protection, and infrared stealth. [0003] Lining the tent with a film insulation material with good thermal insulation performance is a simple and effective measure to improve the thermal insulation performance of the tent. This requires that the thermal insulation material must not only have good thermal insulation performance, but also have Very good foldabil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B5/02B32B5/26B32B37/06B32B37/08B32B37/10D06M15/564D06N3/14D06N3/00D06M101/30
CPCB32B27/02B32B27/12B32B27/28B32B37/06B32B37/08B32B37/10B32B2262/02B32B2307/304D06M15/564D06M2101/30D06N3/0015D06N3/14
Inventor 肖时云
Owner 肖时云
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com