A kind of conductive silver glue and its preparation method and application

A technology of conductive silver glue and silver nanosheets, which is applied in the field of conductive glue, can solve the problem that the conductive silver glue cannot be stretched, and achieve the effects of simple formula and production process, fast curing speed and high conductivity

Active Publication Date: 2021-01-29
零感科技(深圳)有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of the shortcomings of the prior art described above, the purpose of the present invention is to provide a conductive silver glue and its preparation method and application, to solve the problem that the current conductive silver glue cannot be stretched

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of conductive silver glue and its preparation method and application
  • A kind of conductive silver glue and its preparation method and application
  • A kind of conductive silver glue and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1 Based on the total weight of silver nanosheets and low modulus polymer, silver nanosheets account for 70wt%

[0031] Silver nanosheets with a diameter of about 2 μm and a thickness of 5 to 10 nm were selected as conductive fillers, thermoplastic polyurethane elastomer TPU was used as the elastomeric polymer (Germany BASF 35A polyurethane), and dimethylformamide DMF was used as the organic solvent , TPU and DMF are first mixed in a weight ratio of 1:4, and then silver nanosheets and TPU are mixed in a weight ratio of 7:3. After fully stirring, a flexible sensor and wire for connecting PMDS elastomers can be obtained. Conductive silver paste. The SEM of the conductive silver glue after curing see figure 1 . Put the conductive silver paste between the wire and the flexible sensor electrode, volatilize the DMF at room temperature, and it will be completely volatilized within half an hour. The wire and the electrode are firmly connected, and the contact resist...

Embodiment 2

[0034] Embodiment 2 Based on the total weight of silver nanosheets and low modulus polymers, silver nanosheets account for 80wt%

[0035] Silver nanosheets with a diameter of about 2 μm and a thickness of 5 to 10 nm were selected as conductive fillers, thermoplastic polyurethane elastomer TPU was used as the elastomeric polymer (German BASF 35A polyurethane), dimethylformamide DMF was used as the organic solvent, and TPU Mix it with DMF at a weight ratio of 1:1.5, and then mix silver nanosheets and TPU at a weight ratio of 8:2. After fully stirring, it is used to 3D print patterned electrodes on flexible substrates. The conductive silver paste formulated with a high molecular polymer carrier with a weight ratio of TPU to DMF of 1:1.5 has increased viscosity, which can not only be smoothly extruded from the 3D printing nozzle, but also will not flow on the printed substrate, ensuring the pattern completeness and accuracy. At the same time, due to the reduced specific gravity o...

Embodiment 3

[0036] Embodiment 3 Based on the total weight of silver nanosheets and low modulus polymer, silver nanosheets account for 90wt%

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to View More

Abstract

The invention provides a conductive silver paste, a preparation method and application thereof. The conductive silver glue includes silver nanosheets and low-modulus high-molecular polymer carriers, and the low-modulus high-molecular polymer carriers include low-modulus high-molecular polymers and organic solvents, and the elasticity of the low-modulus high-molecular polymers Modulus <100MPa, the organic solvent accounts for 60-80% of the total weight of the high molecular polymer carrier, based on the total weight of silver nanosheets and low modulus polymers, silver nanosheets account for 70-90%, low The modulus polymer accounts for 10-30%. The present invention uses a low-modulus high molecular polymer as the adhesive of the conductive silver glue, which is adapted to the modulus of the flexible circuit, and different modulus polymers can satisfy different modulus flexible circuits. Under relatively large strain, the two-dimensional material silver nanosheets in the conductive silver glue can still maintain a good conductive path, so that the conductive silver glue has high tensile properties and electrical conductivity.

Description

technical field [0001] The invention relates to the field of conductive glue, in particular to a conductive silver glue and its preparation method and application. Background technique [0002] In recent years, more and more attention has been paid to flexible, stretchable, and bendable electronic devices, such as curved displays and touch screens, radio frequency identification tags, wearable sensors, implantable medical devices, wristbands, watches, and even mobile phones. Flexibility and bendability are the future development trend of electronic equipment. The traditional method of constructing conductive paths is mainly realized by lead tin soldering or conductive silver glue of epoxy resin system with large modulus. However, lead-tin soldering has serious pollution and high soldering temperature, so it is not suitable for use on flexible substrates. The conductive silver paste of the epoxy resin system is also not suitable for flexible electronic components due to its...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J9/02C09J175/04H01B1/22
CPCC08K2003/0806C08K2201/011C09J9/02C09J175/04H01B1/22C08K7/00C08K3/08
Inventor 李中勇彭争春
Owner 零感科技(深圳)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com