A kind of basalt fiber wood-based panel and its preparation method

A technology of basalt fiber and wood-based panels, which is applied to manufacturing tools, building structures, floors, etc., can solve the problems of easy aging and environmental protection, low strength of wood-based panels, and many manual operations, and achieves improved reuse rate and scope of application. Good, less human and material effects

Active Publication Date: 2022-03-29
SICHUAN QIANYI COMPOSITE MATERIAL CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention provides a basalt fiber-based panel and a preparation method thereof, which are used to solve the problems in the prior art: the manufactured panel has low strength, is easy to deform, is easy to age, and has poor environmental protection performance, and there are many manual operations on the production line. , resulting in low work efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of basalt fiber wood-based panel and its preparation method
  • A kind of basalt fiber wood-based panel and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] A preparation method of basalt fiber-based panel,

[0055] S1: Stir and mix the chopped basalt fiber and the binder according to a certain ratio to obtain a mixture;

[0056] S2: performing steel strip pressure molding on the mixture;

[0057] The strip pressurization includes

[0058] It includes a steel belt pressing mechanism, and the steel belt pressing mechanism includes:

[0059] A transmission assembly, the transmission assembly includes a transmission wheel and a steel belt 20, and the steel belt 20 is transmitted under the drive of the transmission wheel;

[0060] A straight section 60 is provided on the conveying assembly, and a pressurizing assembly is provided inside the straight section 60, and the mixture is pressurized and formed by the pressurizing assembly. , the pressure wheel 40 is provided with an oil outlet and an oil inlet, and the oil outlet and the oil inlet are connected to the hot oil pool through a conduit.

[0061] S3: Extruded and trunca...

Embodiment 2

[0064] A preparation method of basalt fiber-based panel,

[0065] S1: Stir and mix the chopped basalt fiber and the binder according to a certain ratio to obtain a mixture;

[0066] S2: The mixed material is subjected to steel strip pressure molding to obtain a basalt fiber-based panel.

[0067] The strip pressing device includes

[0068] Two said steel belt pressing mechanisms, the two said steel belt pressing mechanisms are arranged up and down and leave a gap for the mixture to pass through, and the distance between the gaps can be adjusted;

[0069] The transmission directions of the two steel belt pressurizing mechanisms are coordinated so that the mixture is extruded when the mixture passes through, such as figure 2 shown in;

[0070] S3: Extruded and truncated to obtain a basalt fiber-based panel.

[0071] The specific extrusion operation is: as figure 2 As shown in , the mixed material is conveyed in the conveying direction until it is delivered to the straight ...

Embodiment 3

[0087] A method for preparing a basalt fiber-based panel, the artificial panel comprising the following components: by mass percentage, the binder is 7%; basalt chopped fiber is 93%;

[0088] S1: Stir and mix the chopped basalt fiber and the binder according to the above ratio to obtain a mixture;

[0089] S2: performing steel strip pressure molding on the mixture;

[0090] S3: Extruded and truncated to obtain a basalt fiber-based panel.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a basalt fiber man-made panel, which comprises the following steps: stirring and mixing basalt chopped fibers and a binder according to a certain proportion to obtain a mixture; subjecting the mixture to steel belt pressure molding to obtain basalt Fiber-based panels. In the present invention, the basalt fiber wood-based panel is prepared by mixing the basalt chopped fiber and the binder. The wood-based panel is environmentally friendly and economical, and has chemical resistance, high temperature resistance, flame retardancy, fire resistance, oxidation resistance, radiation resistance and heat insulation. In terms of performances such as sound insulation, filtration, compressive strength and shear strength, due to the existing traditional man-made boards; the basalt fiber man-made boards prepared by the present invention have high product recyclability, improve the reuse rate, and reduce waste products. Even after being scrapped, the basalt chopped fibers can become soil or sand during subsequent degradation, and the reuse rate is high; the process of the invention is more simplified, and corresponding economic costs can be saved for enterprises.

Description

technical field [0001] The invention relates to the technical field of basalt fiber, in particular to a basalt fiber-based panel and a preparation method thereof. Background technique [0002] Wood-based panels are boards or molded products that are made of wood or other non-wood plants, separated into various unit materials by certain mechanical processing, and glued with or without adhesives and other additives. [0003] The existing patent ZL2015103091327 is a method for preparing basalt fiber boards, which includes the following steps: 1) processing basalt fibers into basalt fiber yarns, and processing the basalt yarns into basalt fiber plate-like fabrics with a network structure; The mold release agent is sprayed on the inner surface of the mold, and then the basalt fiber plate-like fabric obtained in step 1) is placed in the mold, and the thermosetting resin powder is filled into the basalt fiber plate-like fabric; 3) the heating function of the mold is turned on, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C13/06C04B26/12C04B26/14B28B1/52B28B3/20E04F15/02E04F15/18E04F15/20E04B9/04
CPCC03C13/06C04B26/122C04B26/14B28B1/52B28B3/20E04F15/02E04F15/18E04F15/181E04F15/20E04B9/04E04F2290/04E04F2290/041E04F2290/045C04B14/4643
Inventor 陈云郑文衡杜洪魏仕林刘莉游虎
Owner SICHUAN QIANYI COMPOSITE MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com