Composite preparing method for improving mechanical property of 6XXX aluminum alloy coiled material

A technology of mechanical properties and aluminum alloys, applied in metal rolling, manufacturing tools, temperature control, etc., can solve problems such as large energy consumption, save costs, reduce aging treatment temperature, reduce cryogenic energy consumption and aging treatment energy. consumption effect

Active Publication Date: 2019-10-25
CENT SOUTH UNIV
View PDF7 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the lower the cryogenic temperature, the greater the energy consumption

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite preparing method for improving mechanical property of 6XXX aluminum alloy coiled material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The implementation of the present invention will be described in detail below in conjunction with the drawings and examples.

[0020] The invention discloses a compound preparation method for improving the mechanical properties of 6XXX aluminum alloy coils, the main principle of which is to effectively combine fine grain strengthening and precipitation strengthening to realize performance enhancement of 6XXX aluminum alloy coils. Cryogenic rolling is carried out at around -100°C to refine the grain size of 6XXX aluminum alloys, and at the same time, avoid the primary inclusions in 6XXX aluminum alloys at too low temperature to become brittle and form micro-crack sources during rolling deformation. At the same time, aging treatment is carried out at 95-125°C to effectively ensure that the ultra-fine grain structure produced by cryogenic rolling deformation does not recrystallize. However, it reduces the dislocation density in the aluminum alloy and realizes the generation...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite preparing method for improving the mechanical property of a 6XXX aluminum alloy coiled material. The 6XXX aluminum alloy coiled material treated through solution treatment and ageing is put into a deep cooling box, cooling nitrogen is adopted for cooling, the temperature is -110 DEG C to -90 DEG C, a deep cooling roller is started, the temperature of the rolleris controlled to range from -110 DEG C to -90 DEG C, the 6XXX aluminum alloy coiled material which is evenly cooled is subjected to deep cooling rolling, the 6XXX aluminum alloy coiled material obtained after deep cooling rolling is put into the deep cooling box gain, cooling nitrogen is adopted for cooling, repeated operation is carried out until the whole rolling reduction rate reaches 70 to 90%, the rolled 6XXX aluminum alloy coiled material is subjected to ageing treatment in a heating furnace, the ageing treatment temperature is controlled to range from 95 to 125 DEG C, and the heat preservation time is 12 to 40 hours. Deep cooling rolling about -100 DEG C and low-temperature ageing treatment is adopted, the material strength is improved while the ageing treatment temperature is reduced, the deep cooling treatment energy consumption is saved, and the manufacturing cost is reduced, and the mechanical property of the obtained 6XXX aluminum alloy coiled material exceeds that of an alloy strip prepared through ultra-low-temperature deep cooling rolling and room temperature cold rolling.

Description

technical field [0001] The invention belongs to the technical field of metal material rolling, in particular to a composite preparation method for improving the mechanical properties of 6XXX aluminum alloy coils. Background technique [0002] 6XXX aluminum alloys are the most used aluminum alloys in automobiles. However, since the strength of the current 6XXX aluminum alloys is directly related to the aging treatment process of the 6XXX alloys. Generally, the aging treatment is carried out for a long time in the temperature range of 150°C to 200°C. Since the aging treatment temperature is high and the time is very long, if the aging treatment temperature can be lowered, it has important economic significance for energy saving. [0003] At the same time, the ultra-fine-grained 6XXX aluminum alloy material has very good strength, and its application in automobile lightweight is of great significance. For parts with the same strength requirements, we can reduce the thickness...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21B3/00B21B37/74B21B37/58C22F1/04C21D9/573
CPCB21B3/00B21B37/58B21B37/74B21B2003/001C21D9/573C22F1/04
Inventor 喻海良刘粤王晗
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com