Modified white graphene and polyester composite fiber and preparation method thereof

A white graphene and composite fiber technology, applied in the chemical characteristics of fibers, melt spinning, rayon manufacturing, etc., can solve problems such as the inability to meet functional textiles, polyester fibers do not have functionality, etc., to improve product added value, Anti-ultraviolet performance, good functional effect

Inactive Publication Date: 2019-09-06
常州兴烯石墨烯科技有限公司
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Polyester fiber is a chemical fiber with low cost, good performance and extremely wide uses, but traditional polyester fiber is not functional. With the development of society, traditional polyester can no longer meet people's needs for functional textiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A modified white graphene polyester composite fiber. The raw materials of the composite fiber include: 99% polyester chips, 0.1% white graphene, and 0.9% modifier.

[0035] Modifiers include polyvinyl alcohol or polyethylene glycol.

[0036] White graphene is prepared by the borax-ammonium chloride method.

[0037] The present embodiment also provides the preparation method of this modified white graphene polyester composite fiber, the method comprises:

[0038] Step 1, weighing each raw material in proportion.

[0039] Step 2, drying the polyester slices and white graphene respectively, after drying, the water content of the two is less than 100ppm, and then grinding the polyester slices to obtain a polyester slice powder, the particle size of which is greater than 100 mesh. Add the white graphene powder and modifier to the polyester chip powder and put it into a high-speed mixer for mixing and stirring. The stirring speed is 3000-10000 rpm, and the stirring time is ...

Embodiment 2

[0043] A modified white graphene polyester composite fiber. The raw materials of the composite fiber include 96.9% of polyester chips, 3% of white graphene, and 0.1% of a modifier in terms of mass percentage.

[0044] Modifiers include hydroxypropyl cellulose, sodium lignosulfonate.

[0045] White graphene is prepared by chemical vapor deposition.

[0046] The present embodiment also provides the preparation method of this modified white graphene polyester composite fiber, the method comprises:

[0047] Step 1, weighing each raw material in proportion.

[0048] Step 2, drying the polyester slices and white graphene respectively, after drying, the water content of the two is less than 100ppm, and then grinding the polyester slices to obtain a polyester slice powder, the particle size of which is greater than 100 mesh. Add the white graphene powder and modifier to the polyester chip powder and put it into a high-speed mixer for mixing and stirring. The stirring speed is 3000-1...

Embodiment 3

[0052] A modified white graphene polyester composite fiber. The raw materials of the composite fiber include: 92% polyester chips, 7.5% white graphene, and 0.5% modifier.

[0053] The modifier includes polyvinylpyrrolidone (PVP).

[0054] White graphene is prepared by the borax-urea method.

[0055] The present embodiment also provides the preparation method of this modified white graphene polyester composite fiber, the method comprises:

[0056] Step 1, weighing each raw material in proportion.

[0057] Step 2, drying the polyester slices and white graphene respectively, after drying, the water content of the two is less than 100ppm, and then grinding the polyester slices to obtain a polyester slice powder, the particle size of which is greater than 100 mesh. Add the white graphene powder and modifier to the polyester chip powder and put it into a high-speed mixer for mixing and stirring. The stirring speed is 3000-10000 rpm, and the stirring time is 10-30 minutes to obtain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
water contentaaaaaaaaaa
water contentaaaaaaaaaa
Login to View More

Abstract

The invention discloses a modified white graphene and polyester composite fiber and a preparation method thereof. The composite fiber is prepared from, by mass, 84%-99% of polyester chips, 0.1%-15% ofwhite graphene and 0.1%-1% of a modifying agent. The preparation method includes: step 1, weighing raw materials; step 2, drying the polyester chips and the white graphene, grinding the polyester chips into powder, adding the white graphene powder and the modifying agent into the polyester chip powder, mixing and stirring; step 3, adding the white graphene and polyester mixed powder into a twin-screw extruder, and performing extrusion granulation; step 4, drying modified white graphene and polyester masterbatch, adding into the twin-screw extruder, heating for melting, filtering through a spinning manifold, and spinning to obtain the modified white graphene and polyester composite fiber. The composite fiber prepared according to the method has advantages of antibacterial, far infrared andanti-ultraviolet functions, the added value of polyester can be increased, and a utilization range of polyester fibers is expanded.

Description

technical field [0001] The invention relates to a composite fiber and a preparation method thereof, in particular to a modified white graphene polyester composite fiber and a preparation method thereof. Background technique [0002] "White graphene" is an alias for the nano-flakes obtained after exfoliation of hexagonal boron nitride (English name Hexagonal Boron Nitride, abbreviated as h-BN) whose grains are lamellar structures. Since the structure of hexagonal boron nitride is very similar to that of graphite, it has a hexagonal layered structure, soft texture, strong machinability, and white color. Corresponding to graphene, so hexagonal boron nitride is called "white graphene". [0003] Both hexagonal boron nitride and graphene are layered two-dimensional materials with a thickness of only one atom. , Covalent bonding between heteroatoms of nitrogen. [0004] The highly similar crystal structure gives white graphene and graphene some common characteristics, such as ex...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/92D01F1/10D01D5/08
CPCD01D5/08D01F1/10D01F1/103D01F6/92
Inventor 刘少华林忠义马立国
Owner 常州兴烯石墨烯科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com