A kind of preparation method of amino-terminated hyperbranched polysiloxane modified waterborne polyurethane

An amino-terminated hyperbranched, water-based polyurethane technology is applied in the field of preparation of amino-terminated hyperbranched polysiloxane-modified water-based polyurethane, and can solve the problems of insufficient mechanical properties and cohesiveness, severe phase separation, and low emulsion stability. , to increase the two-phase compatibility, increase the interaction, adhesion and excellent mechanical properties

Active Publication Date: 2021-02-19
SHAANXI UNIV OF SCI & TECH
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The invention provides a method for preparing amino-terminated hyperbranched polysiloxane-modified waterborne polyurethane to overcome the problems of severe phase separation, low emulsion stability and insufficient mechanical properties and cohesiveness in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of amino-terminated hyperbranched polysiloxane modified waterborne polyurethane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Step 1: HPSi-NH 2 preparation of

[0018] Add 3.6g of water to 22.14g of kh550, and add 20mL of ethanol to the system, slowly add 10.8g of TMCS dropwise under stirring conditions, and continuously reflux and stir at 50°C for 5h. After the reaction, adjust with sodium ethylate The pH of the system is neutral, and the solid salt generated is removed by high-speed centrifugation, and finally the small molecule ethanol is removed by a rotary evaporator to obtain the amino-terminated hyperbranched polysiloxane HPSi-NH 2 ;

[0019] Step 2: Preparation of HSiPU

[0020] First, add 20g of 1.4-butylene adipate (Mn=2000) and 8.89g of isophorone diisocyanate into a dry three-necked flask after vacuum dehydration, stir evenly, and add 3 drops of catalyst dilauric acid Dibutyltin, react at 75°C for 1.5h; add 1.45g of dimethylolpropionic acid, continue to react for 2.5h, until the -NCO content in the prepolymer remains constant, and obtain a polyurethane prepolymer (PPU);

[0021...

Embodiment 2

[0024] Step 1: HPSi-NH 2 preparation of

[0025] Add 1.8g of water to 22.14g of kh550, and add 20mL of ethanol, slowly add 10.8g of TMCS under stirring conditions, continuously reflux and stir at 50°C for 6h, adjust the pH of the solution to neutral with sodium ethoxide, and centrifuge The salt generated by the reaction was removed by a machine, and the small molecule ethanol was removed by a rotary evaporator to obtain the amino-terminated hyperbranched polysiloxane HPSi-NH 2 ;

[0026] Step 2: Preparation of HSiPU

[0027] First, add 10g of polytetrahydrofuran ether glycol (Mn=1000) and 5.22g of toluene diisocyanate into a dry three-necked flask after vacuum dehydration, stir evenly, add 3 drops of catalyst dibutyltin dilaurate, and react at 75°C 1.5h; add 1.33g dimethylolpropionic acid, continue to react for 2.5h, until the -NCO content in the prepolymer is constant, and obtain the polyurethane prepolymer PPU;

[0028] Then add 0.73g of butylamine to the obtained PPU an...

Embodiment 3

[0030] Step 1: HPSi-NH 2 preparation of

[0031] Add 3.6g of water to 22.14g of kh550, and add 30mL of ethanol, slowly add 15.0g of TMCS under stirring conditions, keep stirring and reflux reaction at 55°C for 5h, adjust the pH of the system to neutral with sodium ethoxide, and centrifuge The generated solid salt was removed by machine, and small molecule ethanol was removed by rotary evaporator to obtain amino-terminated hyperbranched polysiloxane HPSi-NH 2 ;

[0032] Step 2: Preparation of HSiPU

[0033] Add 20g of polyethylene glycol (Mn=2000) and 5.04g of hexamethylene diisocyanate after vacuum dehydration into a dry three-necked flask, stir evenly, add 3 drops of catalyst dibutyltin dilaurate, at 75°C React for 1 hour; add 1.60 g of dimethylolpropionic acid and continue the reaction for 2 hours until the -NCO content in the prepolymer remains constant to obtain PPU;

[0034] Then add 2.40g of pentaerythritol triacrylate to the obtained PPU, react at 80°C for 2h, cool ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of amino-terminated hyperbranched polysiloxane-modified water-based polyurethane. Firstly, 3-aminopropyltriethoxysilane (kh550) and trimethylchlorosilane (TMCS) are used as raw materials and hydrolyzed Condensation preparation of amino-terminated hyperbranched polysiloxanes (HPSi‑NH 2 ). HPSi‑NH 2 As a crosslinking agent, it reacts with polyurethane prepolymer (PPU) to branch and extend the chain to obtain amino-terminated hyperbranched polysiloxane modified waterborne polyurethane (HSiPU). At the same time, the degree of reaction is controlled by adding an end-capping agent during the synthesis process. , the modified waterborne polyurethane has the performance advantages of traditional silicone waterborne polyurethane, and at the same time reduces the phase separation of silicone modified waterborne polyurethane, increases the mechanical properties and bonding properties of the product, and the obtained emulsion has excellent comprehensive properties and can be used as Leather adhesive or water resistant coating.

Description

technical field [0001] The invention relates to the technical field of organosilicon polymers, in particular to a method for preparing amino-terminated hyperbranched polysiloxane-modified waterborne polyurethane. Background technique [0002] With the promotion of environmental protection, it has become a trend to replace solvent-based polyurethane with water-based polyurethane. The modification of waterborne polyurethane for the deficiencies in water resistance and heat resistance has attracted widespread attention. Silicone has the characteristics of hydrophobicity, heat resistance, and stable chemical properties. The preparation method of traditional silicone-modified waterborne polyurethane is briefly described as follows: linear silicone is used as a mixed soft segment to form silicone block modified waterborne polyurethane; Silicone grafting forms silicone side chain waterborne polyurethane; some people modify waterborne polyurethane with small molecule kh550 through ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/61C08G18/28C08G18/48C08G18/73C08G18/66C08G18/76C08G18/75C08G18/42C08G77/04C08G77/06C08G77/388
CPCC08G18/282C08G18/2865C08G18/348C08G18/4238C08G18/4833C08G18/4854C08G18/61C08G18/6659C08G18/672C08G18/73C08G18/755C08G18/7614C08G77/04C08G77/06C08G77/388C08G18/6692C08G18/0823
Inventor 任龙芳牛巧宣
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More