Normal-temperature rapid-reaction non-cured rubber asphalt waterproof coating and application thereof

A technology of asphalt waterproof coating and non-curing rubber, applied in asphalt coatings, applications, polyurea/polyurethane coatings, etc., can solve the problems of low peel strength and poor adhesion of substrates, and achieve high peel strength and impact resistance. The effect of good and good application value

Active Publication Date: 2019-07-16
HEBEI YUYANGZELI WATERPROOF MATERIAL
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention proposes a non-curing rubber asphalt waterproof coating with rapid response at room temperature and its application, which solves the problems of poor adhesion and low peel strength of the non-curing rubber asphalt waterproof coating to the substrate in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Normal-temperature rapid-reaction non-cured rubber asphalt waterproof coating and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of normal temperature rapid response type non-curing rubber asphalt waterproof coating, including A component and B component,

[0033] Wherein A component is made up of the component of following weight percent:

[0034] 2 parts of toluene diisocyanate, 10 parts of polyether diol, 1 part of 3-(2,3 glycidoxy) propylmethyldiethoxysilane, 0.5 part of boron nitride, 0.1 part of sorbitol, 90# 20 parts of petroleum pitch, 10 parts of liquid terpene resin, 10 parts of aromatic oil, 10 parts of plasticizer, 1 part of surfactant,

[0035] Component B is made up of the following components by weight percentage:

[0036] 2 parts of amino-terminated polyether D2000, 1 part of chain extender E100, 20 parts of 90# petroleum asphalt, 20 parts of aromatic oil, 1 part of surfactant, 1.3 parts of polyethyleneimine, 0.1 part of rare earth metal catalyst, 0.5 part of nano kaolin ,

[0037] The molecular weight of polyether diol is 2000-8000, and the surfactant has the following ...

Embodiment 2

[0040] A kind of normal temperature rapid response type non-curing rubber asphalt waterproof coating, including A component and B component,

[0041] Wherein A component is made up of the component of following weight percent:

[0042] 10 parts of diphenylmethane diisocyanate, 30 parts of polyether diol, 5 parts of 3-(2,3 glycidoxy) propylmethyldiethoxysilane, 3 parts of boron nitride, 1 part of sorbitol , 40 parts of 100# petroleum asphalt, 20 parts of liquid terpene resin, 20 parts of aromatic oil, 20 parts of plasticizer, 5 parts of surfactant,

[0043] Component B is made up of the following components by weight percentage:

[0044]30 parts of amino-terminated polyether D2000, 5 parts of chain extender E100, 50 parts of 90# petroleum asphalt, 50 parts of aromatic oil, 5 parts of surfactant, 3.5 parts of polyethyleneimine, 0.5 parts of rare earth metal catalyst, 2 parts of nano kaolin ,

[0045] The molecular weight of polyether diol is 2000-8000, and the surfactant has ...

Embodiment 3

[0048] A kind of normal temperature rapid response type non-curing rubber asphalt waterproof coating, including A component and B component,

[0049] Wherein A component is made up of the component of following weight percent:

[0050] 3 parts of diphenylmethane diisocyanate, 10 parts of polyether diol, 2 parts of 3-(2,3 glycidoxy) propylmethyldiethoxysilane, 2 parts of boron nitride, 0.1~ of sorbitol 1 part, 34 parts of 90# petroleum asphalt, 20 parts of liquid terpene resin, 20 parts of aromatic oil, 10 parts of plasticizer, 3 parts of surfactant,

[0051] Component B is made up of the following components by weight percentage:

[0052] 10 parts of amino-terminated polyether D2000, 1 part of chain extender E100, 40 parts of 90# petroleum asphalt, 43.9 parts of aromatic oil, 5 parts of surfactant, 3.2 parts of polyethyleneimine, 0.1 part of rare earth metal catalyst, 1.2 parts of nano kaolin ,

[0053] The molecular weight of polyether diol is 2000-8000, and the surfactant...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of waterproof coatings, and provides a normal-temperature rapid-reaction non-cured rubber asphalt waterproof coating. The coating comprises a component A and a component B; the component A is composed of the following components: 2-10 parts of an isocyanate, 10-30 parts of polyether polyol, 1-5 parts of 3-(2,3-epoxypropoxy)propylmethyldiethoxysilane, 0.5-3 parts of boron nitride, 0.1-1 part of sorbitol, 20-40 parts of petroleum asphalt, 10-20 parts of tackifying resin, 10-20 parts of aromatic oil, 10-20 parts of a plasticizer and 1-5 parts of surfactant; and the component B is composed of the following components: 2-30 parts of amino-terminated polyether, 1-5 parts of an amino chain extender, 20-50 parts of petroleum asphalt, 20-50 parts of aromatic oil, 1-5 parts of a surfactant, 1.3-3.5 parts of polyethyleneimine, 0.1-0.5 part of a catalyst and 0.5-2 parts of nano kaolin. The mass ratio of the component A to the component B is (1-3):1 during application. During using, the component A and the component B are mixed, and then scraping coating or spraying coating construction is carried out by using the mixture. According to the technicalscheme, the problem that a non-cured rubber asphalt waterproof coating in the prior art has poor adhesion and low peeling strength to a substrate is solved.

Description

technical field [0001] The invention belongs to the technical field of waterproof coatings, and relates to a normal-temperature quick-response type non-curing rubber asphalt waterproof coating and an application thereof. Background technique [0002] Nowadays, there are more and more applications of composite waterproofing in waterproofing projects, especially the composite use of non-curing rubber asphalt waterproofing coatings and asphalt waterproofing membranes is becoming more and more prosperous. Non-curing rubber asphalt waterproof coating is a hot-melt polymer rubber modified asphalt waterproof coating with high solid content. It has the characteristics of long-term non-curing, self-healing power, sticky when touched, difficult to peel off, and good low-temperature bonding performance. And other characteristics, can solve the problem that the traditional curing coating can not solve the waterproof layer cracking, fatigue damage or premature aging under high stress sta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D175/08C09D191/00C09D11/04C09D11/06C09D11/08
CPCC08L2201/08C08L2205/035C09D11/04C09D11/06C09D11/08C09D195/00C08L75/08C08L91/00C08L79/02C08K3/34
Inventor 田继斌
Owner HEBEI YUYANGZELI WATERPROOF MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com