Organosilicon acrylate compound waterproof finishing agent emulsion

A technology of silicone emulsion and silicone acrylate, which is applied in fiber treatment, textiles and papermaking, fiber types, etc., can solve the problems of poor washability and poor film fastness on the surface of fabrics, and achieve enhanced water repellency, Reduced surface tension, good film-forming effect

Active Publication Date: 2019-05-14
浙江东进新材料有限公司
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] One-component silicone waterproofing still has some defects, such as poor film fastness on the surface of the fabric, poor washability, etc. Therefore, modifying silicone polymers and polymer emulsions such as acrylates can enhance its waterproofing performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organosilicon acrylate compound waterproof finishing agent emulsion
  • Organosilicon acrylate compound waterproof finishing agent emulsion
  • Organosilicon acrylate compound waterproof finishing agent emulsion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Silicone acrylate composite waterproof finishing agent emulsion is formed by blending silicone emulsion and silicon-containing acrylate emulsion, in terms of mass percentage, 68% of silicone emulsion and 32% of silicon-containing acrylate emulsion; under stirring, the organic Slowly add silicon emulsion into silicon-containing acrylate emulsion, mix well;

[0042] The silicone emulsion is mainly composed of vinyl nano-SiO 2 Sol, polymerizable organosilicon monomer (as shown in the above formula 1), vinyl siloxane emulsion polymerization, the preparation method is as follows:

[0043] 1) Add 80 parts of vinyl siloxane emulsion, 40 parts of water, 2 parts of AEO-9, 1 part of AEO-7 into the emulsifier, slowly add 24 parts of polymerizable silicone monomer under stirring, and keep stirring to emulsify for 0.5 h, into a pre-emulsion;

[0044] 2) 50 parts of vinyl siloxane emulsion, 14 parts of vinyl nano-SiO 2 Add sol, 50 parts of water, and 20% pre-emulsion (volume ratio) ...

Embodiment 2

[0058] Silicone acrylate composite waterproof finishing agent emulsion is formed by blending silicone emulsion and silicon-containing acrylate emulsion. In terms of mass percentage, silicone emulsion is 59%, and silicon-containing acrylate emulsion is 41%. Slowly add silicon emulsion into silicon-containing acrylate emulsion, mix well;

[0059] The silicone emulsion is mainly composed of vinyl nano-SiO 2 Sol, polymerizable organosilicon monomer (as shown in the above formula 1), vinyl siloxane emulsion polymerization, the preparation method is as follows:

[0060] 1) Add 80 parts of vinyl siloxane emulsion, 40 parts of water, 2 parts of AEO-9, 1 part of AEO-7 into the emulsifier, slowly add 24 parts of polymerizable silicone monomer under stirring, and keep stirring to emulsify for 0.5 h, into a pre-emulsion;

[0061] 2) 50 parts of vinyl siloxane emulsion, 14 parts of vinyl nano-SiO 2 Add sol, 50 parts of water, and 20% pre-emulsion (volume ratio) into the reactor, stir an...

Embodiment 3

[0075] Silicone acrylate composite waterproof finishing agent emulsion is formed by blending silicone emulsion and silicon-containing acrylate emulsion, in terms of mass percentage, 52% of silicone emulsion and 48% of silicon-containing acrylate emulsion; under stirring, the organic Slowly add silicon emulsion into silicon-containing acrylate emulsion, mix well;

[0076] The silicone emulsion is mainly composed of vinyl nano-SiO 2 Sol, polymerizable organosilicon monomer (as shown in the above formula 1), vinyl siloxane emulsion polymerization, the preparation method is as follows:

[0077] 1) Add 80 parts of vinyl siloxane emulsion, 40 parts of water, 2 parts of AEO-9, 1 part of AEO-7 into the emulsifier, slowly add 24 parts of polymerizable silicone monomer under stirring, and keep stirring to emulsify for 0.5 h, into a pre-emulsion;

[0078] 2) 50 parts of vinyl siloxane emulsion, 14 parts of vinyl nano-SiO 2 Add sol, 50 parts of water, and 20% pre-emulsion (volume ratio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an organosilicon acrylate compound waterproof finishing agent emulsion. The organosilicon acrylate compound waterproof finishing agent emulsion is prepared from in percentage by mass: 52-68% of an organosilicon emulsion and 32-48% of a silicon-contained acrylate emulsion in a blending mode; the organosilicon emulsion is mainly prepared from vinyl nano SiO2 sol, polymerizable organosilicon monomers, and a vinyl siloxane emulsion in a polymerized mode; and the silicon-contained acrylate emulsion is mainly prepared from acrylate monomers and vinyl siloxane monomers in a polymerized mode through an emulsion. The acrylate emulsion has good film formation, adhesion and weather resistance, and has the compatibility with polar polymers and non-polar polymers, and the acrylate emulsion is in composition with the organosilicon emulsion, the defects that a single-composition organosilicon emulsion has poor film formation fastness and poor washing resistance on the surfacesof fabrics can be overcome. The emulsion can form the organosilicon film with low surface energy, can also change the surface roughness, and enhance the water repellency of the surface synergistically.

Description

technical field [0001] The invention relates to a waterproof finishing agent, in particular to a composite waterproof finishing agent of organosilicon and acrylate, belonging to the field of textile functional finishing agents. Background technique [0002] The technological progress of the textile industry and the development of chemical additives have improved the performance of textiles, especially their functionality. Fabrics with good water resistance are becoming more and more popular. [0003] The principle of textile waterproofing is to use a waterproof finishing agent to finish the textile, reduce the porosity of the fiber of the fabric, make it lower than the diameter of the water molecule, so as to prevent the water molecule from penetrating the fabric and form a good waterproof effect. [0004] Aluminum soaps and paraffin wax finishing agents were mostly used in the waterproof finishing of textiles in the early days, which formed deposited films on the surface o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/356D06M15/263D06M15/643D06M11/79D06M101/32
Inventor 陈明贤孙立新董洪波
Owner 浙江东进新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com