Environmentally-friendly degradable plastic and preparation method thereof

A technology for degrading plastics and environmental protection, applied in the field of plastic processing, can solve the problems of uncontrollable degradation time, unpredictable degradation time, and large use restrictions, and achieve the effect of improving mechanical effects, reducing production costs, and improving high temperature resistance performance.

Inactive Publication Date: 2019-05-03
安徽新利清洁用品有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It belongs to an earlier generation of degradable plastics. Its disadvantage is that the degradation time is difficult to predict due to sunlight and climate changes, so the degradation time cannot be controlled; biodegradable plastics are plastics that can be completely decomposed into low-molecular compounds under the action of microorganisms, but the process It is more complicated; photo / biodegradable plastics have the advantages of both photodegradable plastics and biodegradable plastics, but the cost is relatively high; water-degradable plastics are mainly used in the medical industry, which are easy to disinfect and destroy, and have relatively limited use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An environmentally friendly degradable plastic, the environmentally friendly degradable plastic is made of the following raw materials in parts by weight: 40 parts of polylactide, 12 parts of polybutylene succinate, 4 parts of polyvinyl chloride, 4 parts of plant fiber, 30 parts of grafted starch, 1 part of calcium oxide, 1 part of oligosaccharide, 1 part of nano-silicon dioxide, 1 part of polyaluminum chloride, 0.6 part of sodium bismuthate, 0.4 part of dispersant, 0.2 part of crosslinking agent, plasticizer 1 dose.

[0027] Wherein, the dispersant is a mixture of barium stearate, polyethylene wax and polyethylene glycol with a mass ratio of 2:1:1; the crosslinking agent is benzoyl peroxide; the plasticizer is o-phthalic acid Dicyclohexyl dicarboxylate.

[0028] The preparation method of the environment-friendly degradable plastic comprises the following steps:

[0029] (1) After polylactide, polybutylene succinate and polyvinyl chloride are mixed and mixed under hig...

Embodiment 2

[0035] An environmentally friendly degradable plastic, the environmentally friendly degradable plastic is made of the following raw materials in parts by weight: 50 parts of polylactide, 14 parts of polybutylene succinate, 8 parts of polyvinyl chloride, 10 parts of plant fiber, 40 parts of grafted starch, 3 parts of calcium oxide, 3 parts of oligosaccharides, 1.6 parts of nano silicon dioxide, 2 parts of polyaluminum chloride, 1.6 parts of sodium bismuthate, 0.8 parts of dispersant, 0.5 parts of crosslinking agent, plasticizer 1.2 parts.

[0036] Wherein, the dispersant is a mixture of barium stearate, polyethylene wax and polyethylene glycol with a mass ratio of 2:1:1; the crosslinking agent is dicumyl peroxide; the plasticizer is ortho Butylbenzyl phthalate.

[0037] The preparation method of the environment-friendly degradable plastic comprises the following steps:

[0038] (1) After polylactide, polybutylene succinate and polyvinyl chloride are mixed and mixed under high...

Embodiment 3

[0044] An environmentally friendly degradable plastic, the environmentally friendly degradable plastic is made of the following raw materials in parts by weight: 45 parts of polylactide, 13 parts of polybutylene succinate, 6 parts of polyvinyl chloride, 7 parts of plant fiber, 35 parts of grafted starch, 2 parts of calcium oxide, 2 parts of oligosaccharides, 1.3 parts of nano silicon dioxide, 1.5 parts of polyaluminum chloride, 1.2 parts of sodium bismuthate, 0.6 parts of dispersant, 0.3 parts of crosslinking agent, plasticizer 1.1 parts.

[0045] Wherein, the dispersant is a mixture of barium stearate, polyethylene wax and polyethylene glycol mass ratio of 2:1:1; the crosslinking agent is dicumyl hydroperoxide; the plasticizer is Di-n-octyl phthalate.

[0046] The preparation method of the environment-friendly degradable plastic comprises the following steps:

[0047] (1) After polylactide, polybutylene succinate and polyvinyl chloride are mixed and mixed under high tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an environmentally-friendly degradable plastic and a preparation method thereof, and relates to the technical field of plastic processing. The environmentally-friendly degradable plastic is prepared from, by weight, 40-50 parts of polylactide, 12-14 parts of polybutylene succinate, 4-8 parts of polyvinyl chloride, 4-10 parts of plant fibers, 30-40 parts of grafted starch, 1-3 parts of calcium oxide, 1-3 parts of oligosaccharides, 1-1.6 parts of nano-silica, 1-2 parts of polyaluminum chloride, 0.6-1.6 parts of sodium citrate, 0.4-0.8 part of a dispersant, 0.2-0.5 part ofa crosslinking agent and 1-1.2 parts of a plasticizer. The preparation method overcomes the deficiencies of the prior art, adopts a combination of various biodegradable components to prepare the starch blended plastic in order to make the product effectively and completely degraded, and has the advantages of simple production process, convenience in production and low cost, and is suitable for promotion and production.

Description

technical field [0001] The invention relates to the technical field of plastic processing, in particular to an environmentally friendly degradable plastic and a preparation method thereof. Background technique [0002] Due to its light weight, chemical stability, no rust, good impact resistance and other excellent properties, plastics have replaced most of the basic materials and become commonly used raw materials in people's lives. However, since plastics are not easy to degrade as polymer materials, they cause great harm to the environment. . Facing the increasingly serious problem of white pollution, people hope to find a plastic substitute that can replace the performance of the current plastics without causing white pollution. Degradable plastics have emerged as the times require. This new type of functional plastic is characterized by reaching a certain level After the service life is discarded, under certain environmental conditions, due to obvious changes in its che...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L67/04C08L67/02C08L27/06C08L97/02C08L23/06C08L71/02C08K13/02C08K3/36C08K3/22C08K3/24
Inventor 蔡丰富
Owner 安徽新利清洁用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com