Normal-temperature air drying type single-component water-based acrylic anticorrosion finish paint

A water-based acrylic, self-drying technology, used in anti-corrosion coatings, coatings, polyether coatings, etc., can solve the problems of slow natural drying, large environmental pollution, large VOC emissions, etc., and achieve less chemical reaction and VOC emissions. Low, water resistance and good outdoor durability

Inactive Publication Date: 2019-04-26
镇江禹亨新材料有限公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current acrylic topcoat also has many shortcomings, such as large VOC emissions, large environmental pollution, and slow natural drying.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Normal-temperature air drying type single-component water-based acrylic anticorrosion finish paint
  • Normal-temperature air drying type single-component water-based acrylic anticorrosion finish paint
  • Normal-temperature air drying type single-component water-based acrylic anticorrosion finish paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A kind of preparation method of normal temperature self-drying type one-component waterborne acrylic acid anticorrosion finish paint, it is characterized in that, preparation steps are as follows:

[0041] (1) To prepare a toughening agent, put polyamide and polyurethane into a mixing device in a weight ratio of 3:2 and mix them, and mix them uniformly to obtain a toughening agent;

[0042] (2) Put water-based acrylic resin, dispersant, defoamer, polyethylene glycol dioleate, toughener, lauryl alcohol ester, and deionized water into the paint let-down reactor for reaction and mixing. The mixing time 1H, mixing speed 550r / min; then put mica powder, talc powder, diatomaceous earth, titanium dioxide into the paint let-down reaction kettle and stir and mix, stirring time 1H, stirring speed 750r / min, after stirring evenly, the finished product is obtained.

[0043] The composition includes in parts by weight:

[0044] 30 parts water-based acrylic resin

[0045] Mica powder...

Embodiment 2

[0078] Compared with Embodiment 1, the differences of this embodiment are:

[0079] A kind of preparation method of normal temperature self-drying type one-component waterborne acrylic acid anticorrosion finish paint, it is characterized in that, preparation steps are as follows:

[0080] (1) To prepare a toughening agent, put polyamide and polyurethane into a mixing device in a weight ratio of 3:2 and mix them, and mix them uniformly to obtain a toughening agent;

[0081] (2) Put water-based acrylic resin, dispersant, defoamer, polyethylene glycol dioleate, toughener, lauryl alcohol ester, and deionized water into the paint let-down reactor for reaction and mixing. The mixing time 2H, mixing speed 600r / min; then put mica powder, talc powder, diatomaceous earth, titanium dioxide into the paint let-down reactor and stir and mix, stirring time 3H, stirring speed 900r / min, the finished product is obtained after stirring evenly.

[0082] The composition includes in parts by weigh...

Embodiment 3

[0095] Compared with Embodiment 1, the differences of this embodiment are:

[0096] A kind of preparation method of normal temperature self-drying type one-component waterborne acrylic acid anticorrosion finish paint, it is characterized in that, preparation steps are as follows:

[0097] (1) To prepare a toughening agent, put polyamide and polyurethane into a mixing device in a weight ratio of 3:2 and mix them, and mix them uniformly to obtain a toughening agent;

[0098] (2) Put water-based acrylic resin, dispersant, defoamer, polyethylene glycol dioleate, toughener, lauryl alcohol ester, and deionized water into the paint let-down reactor for reaction and mixing. The mixing time 1.5H, mixing speed 580r / min; then put mica powder, talc powder, diatomaceous earth, titanium dioxide into the paint let-down reaction kettle and stir and mix, stirring time 2H, stirring speed 800r / min, the finished product is obtained after stirring evenly.

[0099] The composition includes in part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention provides normal-temperature air drying type single-component water-based acrylic anticorrosion finish paint. The normal-temperature air drying type single-component water-based acrylic anticorrosion finish paint is characterized by being prepared from the components in parts by weight: 30-65 parts of water-based acrylic resin, 11-15 parts of mica powder, 2-5 parts of a dispersing agent, 1-5 parts of a defoaming agent, 2-5 parts of talcum powder, 5-10 parts of polyethylene glycol dioleate, 0.5-3 parts of kieselguhr, 0.5-6 parts of a flexibilizer, 0.5-5 parts of texanol ester alcohol, 1-5 parts of titanium dioxide, and 15-30 parts of deionized water. The water-based acrylic resin is adopted as a base material, the special composite flexibilizer is adopted, excellent ageing resistance is achieved, weather resistance is high, an experiment shows that ultraviolet light aging resistance can reach 600 h, a coating is flat and bright, the excellent adhesive capacity to a bottom layer is achieved, water resistance and outdoor durability are good, and excellent properties of natural drying and quick drying are achieved.

Description

technical field [0001] The invention relates to a paint, in particular to a normal-temperature self-drying one-component water-based acrylic anti-corrosion finish paint. Background technique [0002] There are also some paints for spraying on the surface of objects in the prior art, but the spraying effect is not very satisfactory, and there are shortcomings such as poor appearance quality, easy corrosion, wear, and poor outdoor weather resistance, thereby affecting the appearance quality and image of the object. Moreover, traditional metal coatings are all solvent-based products with high VOC (volatile organic compound) content. During the process of manufacturing, construction, drying, and curing to form a film, the VOC emitted into the air will seriously pollute the environment. With the increasingly stringent environmental protection regulations, the coating industry has gradually developed in the direction of pollution-free, pollution-free, energy-saving, environmentall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D171/02C09D5/08C09D7/20C09D7/65
CPCC08K2003/2241C08L2205/035C09D5/08C09D133/00C09D7/20C09D7/65C08L71/02C08L77/00C08L75/04C08K3/34C08K7/26C08K3/22C08K13/04
Inventor 吕壮志张文俊马玉鹏
Owner 镇江禹亨新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap