Catalytic hydrating method of alkylene oxide

A technology for catalytic hydration of alkylene oxide and alkylene oxide, which is applied in the field of catalytic hydration of alkylene oxide, can solve problems such as difficulty in separation and purification of functional monomers, impact on final polymer performance, and harsh operating conditions, so as to increase the glass transition temperature , Good heat resistance, high swelling resistance

Active Publication Date: 2019-04-05
CHINA PETROLEUM & CHEM CORP +1
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the monomer synthesis route of this route is long, the operating conditions are harsh, the yield is low and the functional monomer is difficult to separate and purify, and the purity is not high, which affects the performance of the final polymer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Catalytic hydrating method of alkylene oxide
  • Catalytic hydrating method of alkylene oxide
  • Catalytic hydrating method of alkylene oxide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] [Example 1] Preparation of Ion Exchange Resin Catalyst

[0036] Add 47.0 grams of styrene, 2.3 grams of divinylbenzene and 1.6 grams of benzoyl peroxide initiator in a 500 milliliter three-necked flask, and stir and react for 2.0 hours at 60° C.; then add 0.6 grams of multilayer graphene and continue stirring for 1 hours for prepolymerization. 260 mL of deionized water in which 2.0 g of gelatin had been dissolved was added. Adjust the stirring speed, and at the same time gradually raise the temperature to 80°C, and react for 5 hours; then raise the temperature to 90°C, react for 5 hours, and finally raise the temperature to 98°C, and react for 6 hours. After the reaction, pour out the upper liquid, wash with 85°C hot water, then wash with cold water, then filter, put it in an oven to dry at 80°C, sieve, and collect the composite gel with a particle size within the range of 0.35-0.60mm Microsphere A1.

[0037] Chloromethylation of composite gel microspheres: In a 500m...

Embodiment 2

[0042] [Example 2] Preparation of Ion Exchange Resin Catalyst

[0043] Add monomer mixture solution (60.0 gram styrene, 1.0 gram divinylbenzene, 1.6 gram multilayer graphene and 1.0 gram benzoyl peroxide containing initiator in 500 milliliters three-necked flask, this solution is stirred at 70 ℃ earlier reaction for 0.5 hours), start the stirrer, add a mixed solution of 200 milliliters of deionized water and 4 grams of polyvinyl alcohol, heat up to 85°C, react for 3 hours, then heat up to 90°C, react for 9 hours, and finally heat up to 100°C, React for 10 hours. After the reaction, pour out the upper liquid, wash with 85°C hot water, then wash with cold water, then filter, put it in an oven to dry at 80°C, sieve, and collect the composite gel with a particle size within the range of 0.35-0.60 mm Microsphere B1.

[0044] Chloromethylation of composite microspheres: in a 500-ml three-necked flask, add 50 grams of composite microspheres B1 and 200 milliliters of chloroethyl eth...

Embodiment 3

[0049] [Example 3] Preparation of Ion Exchange Resin Catalyst

[0050] Add the monomer mixture solution (42.5 grams of styrene, 2.5 grams of divinylbenzene, 0.1 gram of multilayer graphene and 2.0 grams of benzoyl peroxide containing the initiator in a 500 milliliter three-necked flask, and the solution is stirred at 70° C. reaction for 1.5 hours), add a mixed solution of 200 milliliters of deionized water and 4 grams of polyvinyl alcohol, heat up to 85°C, react for 3 hours, then heat up to 90°C, react for 9 hours, and finally heat up to 100°C, react for 10 hours. After the reaction, pour out the upper liquid, wash with 85°C hot water, then wash with cold water, then filter, put it in an oven to dry at 80°C, sieve, and collect the composite gel with a particle size within the range of 0.35-0.60 mm Microsphere C1.

[0051] Chloromethylation of composite microspheres: In a 250 ml three-necked flask, add 20 g of composite microspheres C1 and 100 ml of 1,4-dichloromethoxybutane, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a catalytic hydrating method of alkylene oxide, comprising the step of under hydration reaction, subjecting alkylene oxide and water to contact with ionized exchange resin, wherein the ionized exchange resin has a structural general formula shown in the description; the symbol herein is gel-type nano composite resin matrix; M<-> is an anion, selected from bicarbonate ions,hydroxyl ions, hydrogen sulfite sulfites, carboxylate ions, and citrate ions; POSS is polyhedral oligomeric silsesquioxane unit; another symbol herein is imidazolium cation; and R is a connective group between the POSS unit and is alkylene or arylene.

Description

technical field [0001] The invention relates to a method for catalytic hydration of alkylene oxide. Background technique [0002] Ion exchange resin is a functional polymer material, rich in ion exchange groups, resistant to acid and alkali solutions and many organic solvents, and has strong solvent stability. Industrially, styrene and divinylbenzene are copolymerized to prepare the matrix of ion exchange resins, and anion exchange resins are prepared through chloromethylation and amination reactions. High molecular polymers represented by ion exchange resins have gradually become the third material besides metal materials and inorganic non-metal materials. And it has a wide range of applications in biomedicine, aerospace, information technology, multifunctional catalysis and other fields. [0003] At the end of the 20th century, Shell, Dow, and SD companies began to study the application of ion exchange resins in catalytic hydration. Lemanski et al. used strong base ion e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G81/02C08F292/00C08F212/08C08F212/36C08F8/30C08F8/24C08G65/26
CPCC08F8/30C08F292/00C08G65/2603C08G65/2672C08G65/2681C08G81/024C08F212/08C08F8/24
Inventor 俞峰萍何文军
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com