High-corrosion-resistance pre-hydrated mineral impermeable material and preparation method thereof

An anti-seepage material and prehydration technology, applied in the field of anti-seepage materials, can solve the problems of unsatisfactory anti-seepage effect and poor corrosion resistance of sheet materials, and achieve the improvement of tensile strength, corrosion resistance and stability sexual effect

Pending Publication Date: 2019-04-05
中国非金属矿工业有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a high corrosion-resistant pre-hydration anti-seepage material to at least solve the technical problems of poor corrosion resistance of mineral anti-seepage material surface material and unsatisfactory anti-seepage effect of sheet material in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-corrosion-resistance pre-hydrated mineral impermeable material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The high-corrosion-resistant pre-hydration mineral anti-seepage material of this embodiment is composed of a basalt fiber layer, a mineral anti-seepage layer and an anti-seepage membrane arranged in sequence from top to bottom;

[0034] The basalt fiber layer is a grid-like material made of basalt fibers, and the inner layer is also attached with polyester filaments; the polyester filaments are attached to one side of the basalt fibers during the basalt weaving process, and the polyester filaments and basalt fibers The weight ratio is 1:10. The mass per unit area of ​​the basalt fiber layer is 800g / m 2 ;

[0035] The mineral anti-seepage layer includes the following components: 40 parts by weight of bentonite; 30 parts by weight of kaolin; 6 parts by weight of high molecular polymer; 60 parts by weight of water. The mass per unit area of ​​the mineral anti-seepage layer is 2000g / m 2 ; Wherein, the bentonite is sodium ion bentonite, and the content of montmorillonite ...

Embodiment 2

[0042] The high-corrosion-resistant pre-hydration mineral anti-seepage material of this embodiment is composed of a basalt fiber layer, a mineral anti-seepage layer and an anti-seepage membrane arranged in sequence from top to bottom;

[0043] The basalt fiber layer is a grid-like material made of basalt fibers, and the inner layer is also attached with polyester filaments; the polyester filaments are attached to one side of the basalt fibers during the basalt weaving process, and the polyester filaments and basalt fibers The weight ratio is 1:15. The mass per unit area of ​​the basalt fiber layer is 2000g / m 2 ;

[0044] The mineral anti-seepage layer includes the following components: 80 parts by weight of bentonite; 10 parts by weight of kaolin; 3 parts by weight of high molecular polymer; 40 parts by weight of water. The mass per unit area of ​​the mineral anti-seepage layer is 3000g / m 2 ; Wherein, the bentonite is sodium ion bentonite, and the content of montmorillonite...

Embodiment 3

[0051] The high-corrosion-resistant pre-hydration mineral anti-seepage material of this embodiment is composed of a basalt fiber layer, a mineral anti-seepage layer and an anti-seepage membrane arranged in sequence from top to bottom;

[0052] The basalt fiber layer is a grid-like material made of basalt fibers, and the inner layer is also attached with polyester filaments; the polyester filaments are attached to one side of the basalt fibers during the basalt weaving process, and the polyester filaments and basalt fibers The weight ratio is 1:20. The mass per unit area of ​​the basalt fiber layer is 1400g / m 2 ;

[0053] The mineral anti-seepage layer includes the following components: 60 parts by weight of bentonite; 20 parts by weight of kaolin; 10 parts by weight of high molecular polymer; 20 parts by weight of water. The mass per unit area of ​​the mineral anti-seepage layer is 4000g / m 2 ; Wherein, the bentonite is sodium ion bentonite, and the content of montmorillonit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Mass per unit areaaaaaaaaaaa
Mass per unit areaaaaaaaaaaa
Login to view more

Abstract

The invention provides a high-corrosion-resistance pre-hydrated mineral impermeable material. The high-corrosion-resistance pre-hydrated mineral impermeable material comprises a basalt fiber layer, amineral impermeable layer and an impermeable membrane which are sequentially arranged from top to bottom, the basalt fiber layer is a latticed material woven by basalt fibers; the mineral impermeablelayer comprises bentonite, kaolin and high-molecular polymers; the impermeable membrane is an HDPE (high-density polyethylene) membrane. The invention further provides a preparation method of the high-corrosion-resistance pre-hydrated mineral impermeable material. The high-corrosion-resistance pre-hydrated mineral impermeable material has the advantages of high corrosion resistance, high tensile strength and an excellent impermeable effect.

Description

technical field [0001] The invention belongs to the technical field of anti-seepage materials. Specifically, the invention relates to a high-corrosion-resistant prehydration mineral anti-seepage material and a preparation method thereof. Background technique [0002] At present, mineral anti-seepage materials containing bentonite on the market are mainly used in municipal (garbage landfill), water conservancy, environmental protection, artificial lakes and underground waterproofing of buildings, anti-seepage engineering and other fields. The colloidal system, under the restriction of the upper and lower layer materials, makes the bentonite expand from disorder to order, and the continuous water absorption and expansion make the bentonite layer itself compact, thereby achieving the waterproof effect. [0003] For example, the Chinese patent document CN102922813A discloses a pre-hydration bentonite waterproof blanket, which is composed of a face cloth, a pre-hydration bentonit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B9/00B32B9/04B32B27/32B32B37/10B32B38/16
CPCB32B5/02B32B9/00B32B9/045B32B9/047B32B27/32B32B37/10B32B38/164B32B2323/043B32B2318/00B32B2262/10B32B2307/7265B32B2307/714
Inventor 刘玉芹陈小东郑玉琴段亚萍管俊芳马新华杨启帆
Owner 中国非金属矿工业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap