Filtering material capable of releasing ecological negative ions and preparation method thereof

A filter material and negative ion technology, which is applied in the field of filter material that can release ecological negative ions and its preparation, can solve the problem of being unable to remove tiny dust in the air, achieve high-efficiency solid-loading performance, reduce waste water and waste gas, and release high rates Effect

Active Publication Date: 2019-03-22
ZHEJIANG SCI-TECH UNIV
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current filter materials are limited to rough filtration of the air, and cannot remove tiny dust in the air, as well as organic pollutants such as formaldehyde in the air.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Filtering material capable of releasing ecological negative ions and preparation method thereof
  • Filtering material capable of releasing ecological negative ions and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0040] The preparation method of described filter material, comprises the following steps:

[0041] 1) Add negative ion powder, inorganic dispersant and deionized water into a wet high-speed grinder and grind at high speed for 0.5-5 hours to prepare a stable dispersion containing nano negative ion powder with a particle size of 10-100nm.

[0042] Wherein, the inorganic dispersant is:

[0043] One or more mixtures of silicate or polyacrylic acid, the concentration in the dispersion is 0.1-3.0wt%;

[0044] Or one or more mixtures of alkali metal phosphates; the concentration in the dispersion is 0.1-3.0wt%;

[0045] Or several mixtures of silicates and alkali metal phosphates, the concentration in the dispersion liquid is 0.1-3.0wt%.

[0046] The silicate is selected from water glass, KH-550, KH-560 and KH-570; the polyacrylic acid is selected from polyacrylic acid metal salt; the alkali metal phosphate is selected from sodium tripolyphosphate, Sodium hexametaphosphate and so...

Embodiment 1

[0051] A filter material capable of releasing ecological negative ions, the main body of which is an air or water filter substrate of polymer material loaded with nano negative ion powder; the nano negative ion powder accounts for 0.3% of the total mass of the filter material. The average ecological negative ion release of the filter material is 5865 / cm 2 .

[0052] Wherein, the filter substrate is PET fiber.

[0053] The components of the nano-anion powder are selected from tourmaline, opal and silicate rock minerals, and the proportion is 45:35:20.

[0054] The preparation method of described filter material, comprises the following steps:

[0055] 1) Add negative ion powder, inorganic dispersant and deionized water into a high-speed wet grinding machine and grind at high speed for 2 hours to prepare a stable dispersion containing nano negative ion powder with a particle size of about 50 nanometers.

[0056] Among them, the inorganic dispersant is: the concentrations of K...

Embodiment 2

[0061] A filter material capable of releasing ecological negative ions, the main body of which is an air or water filter substrate of polymer material loaded with nano negative ion powder; the nano negative ion powder accounts for 0.5% of the total mass of the filter material. The average ecological negative ion release of the filter material is 8330 / cm 2 .

[0062] Wherein, the filter substrate is PET fiber.

[0063] The components of the nano-anion powder are selected from tourmaline, opal and silicate rock minerals, and the proportion is 45:35:20.

[0064] The preparation method of described filter material, comprises the following steps:

[0065] 1) Add negative ion powder, inorganic dispersant and deionized water into a high-speed wet grinding machine and grind at high speed for 2 hours to prepare a stable dispersion containing nano negative ion powder with a particle size of about 50 nanometers.

[0066] Among them, the inorganic dispersant is: the concentrations of K...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of filtering materials, and discloses a filtering material capable of releasing ecological negative ions and a preparation method thereof. A main body of the filtering material is an air or water body filtering substrate which is loaded with nanometer negative ion powder and is made of a macromolecular material. The preparation method comprises the following steps of (1) mixing negative ion powder, an inorganic dispersant and deionized water, and grinding at high speed, so as to obtain stable dispersing liquid containing the nanometer negative ion powder; (2)adding the stable dispersing liquid into a water-based adhesive, stirring at high speed, and emulsifying, so as to obtain an opened-pore water-based adhesive emulsion containing the nanometer negative ion powder; (3) adopting a gap type spot-spray flow technology, and performing scattering type spot-spray flow operation on the filtering substrate multiple times, so as to obtain the filtering substrate loaded with the nanometer negative ion powder; (4) curing the filtering substrate, so as to obtain the filtering material. The filtering material has the advantages that the immobilizing property is efficient, the load is not liable to fall off, and the release amount of ecological negative oxygen ions can reach 25000 per square centimeter.

Description

technical field [0001] The invention relates to the field of filter materials, in particular to a filter material capable of releasing ecological negative ions and a preparation method thereof. Background technique [0002] At present, the ventilation filter is mainly made of PP, PET and other fiber textiles. It has good acid and alkali resistance, corrosion resistance, low resistance, and can be cleaned repeatedly. The economy is relatively high. In addition, The long and short fibers and dust particles captured by it are easy to clean, the filtration efficiency is not affected by cleaning, and the impact resistance is very good. It is the product of choice for customers. The air conditioning filter has a concave-convex honeycomb structure, which can be widely used in sewage filtration systems and air filtration. It is easy to clean and replace many times, and has a long-lasting effect. Moreover, the air conditioner filter is easy to clean, which is recognized by the major...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01D39/14B01D46/00
CPCB01D39/14B01D46/0036B01D2239/10Y02A50/2351
Inventor 万军民
Owner ZHEJIANG SCI-TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com