Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

Production process of bolts

A production process and bolt technology, applied in the field of nuclear power bolt production process, can solve the problems that the production process cannot meet the requirements, and the requirements of strength, hardness and impact resistance are very strict, and achieve good lubricity, strong corrosion resistance, and phosphating. fine film effect

Inactive Publication Date: 2019-01-04
NINGBO ZEE AUTOMATION EQUIP
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the fasteners used in nuclear power equipment are very demanding in terms of strength, hardness and impact resistance. For fasteners that need to meet nuclear power level 1, 2, and 3 equipment, the existing production process cannot meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The production process of nuclear power bolts, the technological process is blank preparation-heat treatment-flaw detection inspection-surface treatment.

[0023] Using 42CrMoE steel as raw material, the chemical composition mass percentage is: C content 0.405%, Si content 0.23%, Mn content 0.78%, P content 0.012%, S content 0.013%, Cr content 0.94%, Mo content 0.17%, the balance is Fe. Raw material production inspection, blanking, plane chamfering, heat treatment, thread blank diameter grinding, thread rolling.

[0024] The heat treatment process quenches and tempers bolts < 0.5M and bolts ≥ 0.5M respectively. Bolts with a length of less than 0.5M are quenched in a mesh belt furnace with alloy steel quenching oil as the medium, the quenching temperature is 850°C, and the holding time is 2 hours. After quenching, continue tempering in the mesh belt furnace, the tempering temperature is 680°C, and the holding time is 2.5 hours.

[0025] Bolts with a length ≥ 0.5M are ...

Embodiment 2

[0028] The raw materials and process flow of this embodiment are the same as those in Embodiment 1, except that in the heat treatment process, for bolts with a length <0.5M, the quenching temperature is 860° C., and the holding time is 2 hours. After quenching, continue tempering in the mesh belt furnace, the tempering temperature is 630°C, and the holding time is 2.5 hours.

[0029] Bolts with a length ≥ 0.5M are quenched in a pit furnace with mechanical oil as the medium, the quenching temperature is 860°C, and the holding time is 2.5 hours. After quenching, continue to temper in the pit furnace, the tempering temperature is 630°C, and the time is 3 hours.

Embodiment 3

[0031] The process flow of this embodiment is the same as that of Embodiment 1, the difference is the raw materials and heat treatment process.

[0032] Using 42CrMoE steel as raw material, the chemical composition mass percentage is: C content 0.38%, Si content 0.10%, Mn content 0.75%, P content 0.025%, S content 0.015%, Cr content 0.80%, Mo content 0.15%, the balance is Fe.

[0033] For bolts with a length less than 0.5M, the quenching temperature is 860°C and the holding time is 2 hours. After quenching, continue tempering in the mesh belt furnace, the tempering temperature is 620°C, and the holding time is 2.5 hours.

[0034] Bolts with a length ≥ 0.5M are quenched in a pit furnace with mechanical oil as the medium, the quenching temperature is 860°C, and the holding time is 2.5 hours. After quenching, continue to temper in the pit furnace, the tempering temperature is 620°C, and the time is 3 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention mainly discloses a production process of bolts. 42CrMoE steel is adopted as a raw material, and the steps of blank preparation, thermal treatment, surface treatment and flaw detection are carried out, wherein the raw material 42CrMoE is prepared from, by mass, 0.38%-0.48% of C, 0.10%-0.40% of Si, 0.75%-1.00% of Mn, smaller than or equal to 0.025% of P, smaller than or equal to 0.015%of S, 0.80%-1.15% of Cr, 0.15%-0.30% of Mo and the balance Fe. The produced products meet the requirements of nuclear power first-level, second-level and third-level equipment, and the strength, hardness and impact force resistance all meet standards.

Description

technical field [0001] The invention relates to a production process of fasteners, in particular to a nuclear power bolt production process meeting the requirements of nuclear power level 1, 2 and 3 equipment. Background technique [0002] A nuclear power plant is a power facility that uses the thermal energy generated by one or several power reactors to generate electricity or generate electricity and heat. The fuel used in nuclear power plants is uranium. The nuclear fuel made of uranium is fissioned in the "reactor" equipment to generate a large amount of heat energy, and then the water under high pressure is used to take out the heat energy and generate steam in the steam generator. Push the steam turbine to rotate together with the generator, and electricity is continuously generated and sent to all directions through the grid. [0003] In order to ensure the safety of nuclear power plants, the strictest defense measures conceivable should be taken in terms of design a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/02C22C38/04C22C38/22C21D1/18C21D9/00
CPCC22C38/02C21D1/18C21D9/0093C22C38/04C22C38/22
Inventor 刘建军
Owner NINGBO ZEE AUTOMATION EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com