Welded structure refractory and weathering steel with yield strength being no less than 620 MPa and production method thereof

A welding structure and yield strength technology, which is applied in the field of fire-resistant and weather-resistant steel for welded structures, can solve the problems of unsatisfactory welding performance, corrosion resistance, lack of fire resistance, unfavorable steel plate welding and low-temperature toughness, etc., and achieve good cold and hot processing The effect of performance, simple manufacturing process, and ease of mass production

Active Publication Date: 2018-12-21
武汉钢铁有限公司
View PDF18 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is mainly researched and developed for steel for railway vehicles. It is produced by hot rolling and coiling process. The steel contains a large amount of Cr element, which is not conducive to steel plate welding and low temperature toughness. In addition, the steel type does not have fire resistance
[0008] In addition, China Invention Patent Application Nos. CN103695772A and CN103695773A disclose fire-resistant, weather-resistant, and earthquake-resistant building steel with a yield strength of 550 MPa and its production method, and fire-resistant, weather-resistant, and earthquake-resistant building steel with a yield strength of 690 MPa and its production method. The two invention patents The application for construction steel contains C, Si, Mn, P, S, Nb, Ti, Mo, W, Mg, O, in addition to Sb or Zr or a mixture of the two in any proportion, and the rest is Fe and unavoidable Inclusions, after hot metal desulfurization, converter smelting, vacuum treatment, adding Mg element, conventional continuous casting and heating of the billet, segmental rolling, cooling after final rolling, etc., the steel has excellent fire resistance, weather resistance and shock resistance. The overall performance is excellent, but the disadvantages of these two steels are that the welding performance and corrosion resistance are not very ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Welded structure refractory and weathering steel with yield strength being no less than 620 MPa and production method thereof
  • Welded structure refractory and weathering steel with yield strength being no less than 620 MPa and production method thereof
  • Welded structure refractory and weathering steel with yield strength being no less than 620 MPa and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-9

[0045]The embodiment of the present invention prepares a fire-resistant and weather-resistant steel for welded structures with a yield strength ≥ 620 MPa, its components and mass percentages are: C: 0.035-0.075%, Si: 0.13-0.24%, Mn: 1.56-1.82%, P≤0.003%, S≤0.002%, Mo: 0.12~0.23%, W: 0.21~0.40%, Cu: 0.22~0.48%, Ni: 0.21~0.43%, Nb: 0.026~0.048%, V: 0.058~0.077 %, Ti: 0.045~0.068%, Ca: 0.0022~0.0052%, Ta: 0.0028~0.0065%, [N]: 0.0022~0.0057%, [O]: 0.0024~0.0042%, the rest is Fe and unavoidable impurities, Satisfied at the same time: ①(Ca+2Ta) / 3[O]=1.32~1.65, ②4(15C+Mo+2W)+3(Mn+Cu)=11.52~13.61%, ③Pcm(%)=C+Si / 30 +(Mn+Cu) / 20+Ni / 60+Mo / 15+V / 10≤0.20%.

[0046] Its production method includes smelting and pouring into slabs, slab heating, high-pressure water dephosphorization, controlled rolling, laminar cooling and other process steps. The specific process steps are as follows:

[0047] 1) Smelting and pouring into slabs: Smelting and pouring molten iron to form slabs, controlling Ca: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a welded structure refractory and weathering steel with yield strength being no less than 620 MPa and production method thereof, and the welded structure refractory and weathering steel with the yield strength being no less than 620 MPa comprises, by mass, 0.035-0.075% of C, 0.13-0.24% of Si, 1.56-1.82% of Mn, no more than 0.003% of P, no more than 0.002% of S, 0.12-0.23%of Mo, 0.21-0.40% of W, 0.22-0.48% of Cu, 0.21-0.43% of Ni, 0.026-0.048% of Nb, 0.058-0.077% of V, 0.045-0.068% of Ti, 0.0022-0.0052% of Ca, 0.0028-0.0065% of Ta. The welded structure refractory and weathering steel with the yield strength being no less than 620 MPa has good mechanical properties, excellent fire resistance, weather resistance and resistance to laminar tearing, as well as the excellent welding property.

Description

technical field [0001] The invention belongs to the technical field of low-alloy high-strength steel manufacturing, and relates to a fire-resistant and weather-resistant steel for welded structures with a yield strength of 620 MPa and a production method thereof. Background technique [0002] With the continuous development of iron and steel metallurgy technology, structural parts such as columns and beams of steel structures have put forward new requirements for steel plate strength, fire and disaster resistance, corrosion resistance, and earthquake resistance, while ordinary steel structures are poor in the construction industry. The ability to resist fire, disaster and corrosion is facing a severe test. In recent years, metallurgists at home and abroad have actively carried out research on fire-resistant, weather-resistant, and earthquake-resistant steels. The use of fire-resistant and weather-resistant steels can not only make up for the shortcomings of ordinary steel st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/12C22C38/16C22C38/08C22C38/14C21D8/02
CPCC21D8/0205C21D8/0226C21D8/0247C22C38/002C22C38/02C22C38/04C22C38/08C22C38/12C22C38/14C22C38/16
Inventor 童明伟卜勇张开广范巍
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com