Anticorrosive chlorinated rubber coating and production process for same

A technology of anti-corrosion coatings and chlorinated rubber, applied in anti-corrosion coatings, rubber derivative coatings, fire-resistant coatings, etc., can solve the problems of low raw material resources and high production costs, achieve easy control of reactions, improve coating properties, and inhibit gelation the formation of the effect

Inactive Publication Date: 2018-12-21
JIANGSU XIN AN NEW MATERIALS TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Chlorinated rubber coating is a kind of high-performance coating. It has developed rapidly in recent years. It is widely used in the field of dry anticorrosion. It is widely used in ships, port facilities, bridge steel structures, chemical equipment, containers and cement buildings. It is free from the erosion of the atmosphere, chemical gases and other media to prolong the service life of the object and play a decorative role; however, there are many problems in the existing chlorinated rubber anti-corrosion coatings, such as few raw material resources and high production costs. During the degradation process, some substances that seriously pollute the air remain

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] This embodiment provides a kind of chlorinated rubber anticorrosion coating, and anticorrosion coating comprises the following components by mass parts:

[0039] Neoprene: 35 parts, chlorinated rubber: 50 parts, refractory material: 7 parts, dispersant: 1 part, xylene: 5 parts, fluorocarbon resin: 10 parts, silicone modified epoxy resin: 12 parts, Panasonic water: 10 parts, barite powder: 1 part, vermiculite powder: 3 parts, surfactant: 1 part, binder: 3 parts, plasticizer: 2 parts, mica iron oxide: 1 part, compound rare earth: 0.02 copies;

[0040] Cerium: 8%, praseodymium: 5%, dysprosium: 8%, holmium: 8%, gadolinium: 10%, yttrium: 5%, the rest is lanthanum, and the sum of the above rare earth components is 100%;

[0041] Silicone-modified epoxy resin includes the following components by mass percentage: methyltriethoxysilane: 25%, deionized water: 5%, dibutyltin dilaurate: 10%, and the balance is epoxy resin, The sum of the above components is 100%.

[0042] In thi...

Embodiment 2

[0048] This embodiment provides a kind of chlorinated rubber anticorrosion coating, and anticorrosion coating comprises the following components by mass parts:

[0049] Neoprene: 40 parts, chlorinated rubber: 60 parts, refractory material: 9 parts, dispersant: 3 parts, xylene: 8 parts, fluorocarbon resin: 15 parts, silicone modified epoxy resin: 14 parts, Panasonic water: 13 parts, barite powder: 3 parts, vermiculite powder: 5 parts, surfactant: 2 parts, binder: 5 parts, plasticizer: 4 parts, mica iron oxide: 3 parts, compound rare earth: 0.04 copies;

[0050] Cerium: 15%, praseodymium: 9%, dysprosium: 11%, holmium: 10%, gadolinium: 13%, yttrium: 9%, the rest is lanthanum, and the sum of the above rare earth components is 100%;

[0051] Silicone-modified epoxy resin includes the following components by mass percentage: methyltriethoxysilane: 35%, deionized water: 10%, dibutyltin dilaurate: 15%, and the balance is epoxy resin, The sum of the above components is 100%.

[0052...

Embodiment 3

[0058] This embodiment provides a kind of chlorinated rubber anticorrosion coating, and anticorrosion coating comprises the following components by mass parts:

[0059] Neoprene: 38 parts, chlorinated rubber: 55 parts, refractory material: 8 parts, dispersant: 2 parts, xylene: 6 parts, fluorocarbon resin: 13 parts, silicone modified epoxy resin: 13 parts, Panasonic water: 12 parts, barite powder: 2 parts, vermiculite powder: 4 parts, surfactant: 2 parts, binder: 4 parts, plasticizer: 3 parts, mica iron oxide: 2 parts, compound rare earth: 0.03 copies;

[0060] Cerium: 11%, praseodymium: 7%, dysprosium: 9%, holmium: 9%, gadolinium: 11%, yttrium: 7%, the rest is lanthanum, and the sum of the above rare earth components is 100%;

[0061] Silicone-modified epoxy resin includes the following components by mass percentage: methyltriethoxysilane: 30%, deionized water: 8%, dibutyltin dilaurate: 13%, and the balance is epoxy resin, The sum of the above components is 100%.

[0062] I...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
flame retardantaaaaaaaaaa
flame retardantaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anticorrosive chlorinated rubber coating, which is prepared from the following components: chloroprene rubber, chlorinated rubber, a refractory material, a dispersant, dimethylbenzene, fluorocarbon resin, organic silicone modified epoxy resin, Songxiashui, baryta powder, vermiculite powder, a surfactant, a binder, a plasticizer, micaceous iron oxide and composite rare earth. The invention also discloses a production process for the anticorrosive chlorinated rubber coating. The production process is simple and easy, the produced anticorrosive material is high in anticorrosive performance and protection performance, the service life of the anticorrosive material is prolonged, and the cost is reduced.

Description

technical field [0001] The invention relates to an anti-corrosion material, in particular to a chlorinated rubber anti-corrosion coating and a production process thereof. Background technique [0002] Chlorinated rubber coating is a kind of high-performance coating. It has developed rapidly in recent years. It is widely used in the field of dry anticorrosion. It is widely used in ships, port facilities, bridge steel structures, chemical equipment, containers and cement buildings. It is free from the erosion of the atmosphere, chemical gases and other media to prolong the service life of the object and play a decorative role; however, there are many problems in the existing chlorinated rubber anti-corrosion coatings, such as few raw material resources and high production costs. During the degradation process, some substances that seriously pollute the air remain. Contents of the invention [0003] The technical problem to be solved by the present invention is to propose a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D115/02C09D111/00C09D127/12C09D163/00C09D183/04C09D5/10C09D7/61C09D7/63C09D7/65
CPCC09D115/02C08K2003/2244C08K2003/3045C08L2201/02C08L2205/035C09D5/10C09D5/18C09D7/61C09D7/63C09D7/65C08L11/00C08L27/12C08L63/00C08L83/04C08L29/04C08L31/04C08L29/06C08K3/30C08K3/08C08K3/36C08K7/26C08K3/22
Inventor 张望
Owner JIANGSU XIN AN NEW MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com