High-wear-resistant and high-weatherproof dry powder latex paint and preparation method thereof

A dry powder latex, high wear-resistant technology, applied in the field of decorative materials, can solve the problems of poor wear resistance and weather resistance, difficulty in dispersion, poor leveling, etc., and achieve long service life, good leveling, and excellent wear resistance.

Inactive Publication Date: 2018-12-14
尚晴
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problems of many bubbles, poor leveling, difficult dispersion, poor wear resistance and weather resistance in the dry powder latex paint in the prior art, and propose a kind of high wear resistance and high weather resistance dry powder latex paint and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A kind of high wear-resisting and high-weather-resistant dry powder latex paint proposed by the present invention comprises the following raw materials in parts by weight: 15 parts of white cement, 15 parts of calcium carbonate, 5 parts of ash calcium powder, 10 parts of redispersible latex powder, sodium silicate 2 parts, 5 parts of modified boron carbide, 5 parts of titanium dioxide, 3 parts of far-infrared ceramic powder, 2 parts of wood fiber, 1 part of aluminum dihydrogen phosphate, 1 part of fungicide, 1 part of silane coupling agent, 1 part of defoamer share;

[0025] The bactericide is a chitosan gel loaded with nano-silver and nano-zinc oxide, wherein the mass ratio of nano-silver and nano-zinc oxide is 1:0.3;

[0026] The preparation method of the modified boron carbide is as follows: under ice bath conditions, boron carbide is added to the concentrated sulfuric acid with a mass fraction of 98% while stirring at a speed of 300r / min according to the mass ratio ...

Embodiment 2

[0034] A kind of high wear-resisting and high-weather-resistant dry powder latex paint proposed by the present invention comprises the following raw materials in parts by weight: 25 parts of white cement, 25 parts of calcium carbonate, 7 parts of ash calcium powder, 19.5 parts of redispersible latex powder, sodium silicate 3 parts, 7 parts of modified boron carbide, 7 parts of titanium dioxide, 5 parts of far-infrared ceramic powder, 5 parts of wood fiber, 2 parts of aluminum dihydrogen phosphate, 2 parts of fungicide, 2 parts of silane coupling agent, 2 parts of defoamer share;

[0035] The bactericide is a chitosan gel loaded with nano-silver and nano-zinc oxide, wherein the mass ratio of nano-silver and nano-zinc oxide is 1:0.5;

[0036] The preparation method of the modified boron carbide is as follows: under ice bath conditions, boron carbide is added to the concentrated sulfuric acid with a mass fraction of 98% while stirring at a speed of 400r / min according to the mass ...

Embodiment 3

[0044] A kind of high wear-resisting and high-weather-resistant dry powder latex paint proposed by the present invention comprises the following raw materials in parts by weight: 35 parts of white cement, 35 parts of calcium carbonate, 10 parts of ash calcium powder, 30 parts of redispersible latex powder, sodium silicate 4 parts, 10 parts of modified boron carbide, 10 parts of titanium dioxide, 8 parts of far-infrared ceramic powder, 7 parts of wood fiber, 3 parts of aluminum dihydrogen phosphate, 3 parts of fungicide, 3 parts of silane coupling agent, 3 parts of defoamer share;

[0045] The bactericide is a chitosan gel loaded with nano-silver and nano-zinc oxide, wherein the mass ratio of nano-silver and nano-zinc oxide is 1:0.8;

[0046] The preparation method of the modified boron carbide is as follows: under ice bath conditions, boron carbide is added to concentrated sulfuric acid with a mass fraction of 98% while stirring at a speed of 500r / min according to a mass ratio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of decorative materials, in particular, relates to a high-wear-resistant and high-weatherproof dry powder latex paint and a preparation method thereof, andsolves the problems of many bubbles, poor leveling property, difficult dispersion, poor wear resistance and poor weather resistance of a dry powder latex paint in the prior art. The high-wear-resistant and high-weatherproof dry powder latex paint includes the following raw materials: white cement, calcium carbonate, ash calcium powder, redispersible latex powder, sodium silicate, modified boron carbide, titanium dioxide, far infrared ceramic powder, wood fibers, aluminum dihydrogen phosphate, a bactericide, a silane coupling agent, and a defoamer. The prepared dry powder latex paint has the advantages of safety, environmental protection, zero VOC, stable and uniform performance, strong cohesiveness, high strength after a coating layer is formed, good leveling property, excellent wear resistance, aging resistance and corrosion resistance, fire prevention, flame retardancy, mildew prevention and bacterial resistance, is not easily discolored, has long service life, and can be widely applied in indoor and outdoor wall decoration.

Description

technical field [0001] The invention relates to the technical field of decorative materials, in particular to a dry powder latex paint with high wear resistance and high weather resistance and a preparation method thereof. Background technique [0002] Latex paint, also known as latex paint, is a kind of organic paint, which is prepared by adding pigments, fillers and various additives with synthetic resin as the base material. In recent years, my country's architectural coatings have developed rapidly, and product research and development are also developing in the direction of water-based, high solid content, and low VOC. As an important water-based paint variety, latex paint occupies an absolute share in the paint market, especially the home improvement market, due to its convenient use, easy color matching, and good water resistance. However, because it is a water-based dispersion system with a moisture content of more than 30%, it is not convenient for packaging, trans...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D121/02C09D5/02C09D5/14C09D5/08C09D5/18C09D7/62
CPCC08L2201/02C08L2201/08C09D5/024C09D5/08C09D5/14C09D5/18C09D121/02C08L97/02C08K13/06C08K9/02C08K9/04C08K9/08C08K3/38C08K3/34
Inventor 尚晴
Owner 尚晴
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com