Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Method for preparing manganese-doped double-perovskite red fluorescent powder

A technology of red fluorescent powder and double perovskite, which is applied in the direction of chemical instruments and methods, luminescent materials, etc., can solve the problems of difficult control of sample particle size, high calcination temperature, and high production cost, so as to facilitate large-scale industrial production, The effect of lowering the calcination temperature and lowering the production cost

Active Publication Date: 2018-11-06
JIANGXI UNIV OF SCI & TECH
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The sol-gel method can achieve doping at the molecular level, and the sintering temperature is relatively low (1300°C), but the reaction cycle is long, requiring several days, and high-temperature calcination is required
The composition of the sample synthesized by the co-precipitation method is relatively uniform, and segregation of the composition rarely occurs, but the particle size of the sample is not easy to control, the process is more complicated, and a subsequent high-temperature calcination stage is also required
The high-temperature solid-phase method has the advantages of simple operation, short reaction cycle, and easy industrial production. However, the calcination temperature for synthesizing the oxide is relatively high (1400°C), which leads to high production costs. At the same time, the particle size of the sample prepared at high temperature is too large. , seriously affecting its luminous efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing manganese-doped double-perovskite red fluorescent powder
  • Method for preparing manganese-doped double-perovskite red fluorescent powder
  • Method for preparing manganese-doped double-perovskite red fluorescent powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Weigh 16.2905g La2O3, 2.0152g MgO, 3.9735g TiO2, 0.0287g MnCO3, and an appropriate amount of NaCl, grind the above raw materials evenly, put them into a high-temperature furnace, heat evenly from room temperature to 800°C, keep warm for 12 hours, and then cool naturally to room temperature, and wash the product with an appropriate amount of absolute ethanol two to three times, dry in an oven, and cool to room temperature naturally, the composition is La2Mg(Ti0.995Mn0.005)O6.

Embodiment 2

[0036] Weigh 11.2905g Y2O3, 2.0152g MgO, 3.9735g TiO2, 0.0287g MnCO3, and an appropriate amount of LiCl, grind the above raw materials evenly, put them into a high-temperature furnace, heat evenly from room temperature to 1000°C, keep warm for 12 hours, and then cool naturally to room temperature, and wash the product with an appropriate amount of absolute ethanol two to three times, dry in an oven, and naturally cool to room temperature, the composition is Y2Mg(Ti0.995Mn0.005)O6.

Embodiment 3

[0038]Weigh 16.2905g La2O3, 4.0690g ZnO, 3.9735g TiO2, 0.0287g MnCO3, and an appropriate amount of KCl, grind the above raw materials evenly, put them into a high-temperature furnace, heat evenly from room temperature to 900°C, keep warm for 12 hours, and then cool naturally After reaching room temperature, add an appropriate amount of absolute ethanol to wash the product two to three times, dry it in an oven, and cool it naturally to room temperature to obtain the composition La2Zn(Ti0.995Mn0.005)O6.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of fluorescent powder preparation and in particular relates to a method for preparing manganese-doped double-perovskite red fluorescent powder. According to the method, chlorides (LiCl, NaCl and KCl) are creatively adopted as cosolvents, and the manganese-doped double-perovskite red fluorescent powder is synthesized under the action of the cosolvents. Compared with a calcination temperature of 1400 DEG C in the prior art, a temperature of only 800-1000 DEG C is need in the method, so that the production cost can be greatly reduced; on the other hand, compared with the prior art that the red light emission efficiency is seriously affected as the calcination temperature is reduced, the red light emission efficiency of the method is not reduced while the calcination temperature is reduced, the calcination temperature can be reduced while the red light emission efficiency is ensured, the characteristic is very unique, and as lamp fluorescent powder, the fluorescent powder can be applied to the field of LED (Light Emitting Diode) lighting and plant growth assistance artificial light sources.

Description

technical field [0001] The invention relates to the technical field of phosphor preparation, in particular to a preparation method of a manganese-doped double perovskite red phosphor. Background technique [0002] Because blue light (400-500nm), red light (620-690nm) and near-infrared light (700-740nm) control the photosynthesis, phototropism and photomorphological changes of plants respectively, the light source not only provides the energy needed for plant growth , and also control thousands of reaction processes in plant cells. Because of this, the greenhouse industry, which controls plant growth through different light sources, has been widely developed in agriculture and gardening, and thus meets the different needs of human beings. Among them, blue and red LED lights for plant growth have been widely studied, but near-infrared LEDs are rarely reported. [0003] When in the center of the octahedral structure, the spin-allowed transition of the 4A2 to 4T1 and 4T2 energ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K11/78C09K11/68
CPCC09K11/684C09K11/7701C09K11/7702C09K11/7707
Inventor 廖臣兴胡美兰游维雄
Owner JIANGXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com