Bathroom wood-based composite material and preparation method thereof

A composite material and wood technology, applied in the field of wood composite materials for bathroom and its preparation, can solve the problems that physical and chemical properties cannot meet, can not meet design requirements, single shape and color, etc. The effect of photo-oxidative degradation and improvement of mechanical properties

Inactive Publication Date: 2018-11-06
FOSHAN WANYANG BIOLOGICAL TECH CO LTD
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention: the material of the plantation forest fast-growing wood is relatively loose and the color is uneven; in addition, some plantation forest wood is prone to discoloration during storage and processing, and its physical and chemical properties cannot meet the requirements of the environment in the bathroom. Moreover, the shape and color are single, cannot meet the design requirements, and are not in harmony with the overall indoor environment. A wood composite material for bathroom and its preparation method are provided.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bathroom wood-based composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0026]Take 1g of silane coupling agent KH-550 and 1g of titanate coupling agent TCA201, add it to 40g of absolute ethanol, stir at 300r / min at 40°C for 1h to obtain the alcoholysis solution of the composite coupling agent, take 1g of calcium sulfate Whiskers, add 20g of composite coupling agent alcoholysis solution, stir at 40°C at 300r / min for 1h, filter to obtain filter residue, put the filter residue in a drying oven, and dry at 105°C for 1h to obtain modified calcium sulfate crystals Whiskers, take 250g polyethylene resin, 400g fast-growing forest wood powder, 20g calcium carbonate, 2g antioxidant, 3g chitosan, 1g stearic acid, 0.2g polyethylene wax, 1g modified calcium sulfate whiskers, add high-speed mixing In the machine, stir at high speed until the temperature is 100°C, keep stirring for 5 minutes and cool to 40°C, then spray 1g of compound coupling agent alcoholysis solution, continue stirring for 10 minutes, and then add it to a parallel twin-screw extruder to extrud...

example 2

[0028] Take 1g of silane coupling agent KH-550 and 1g of titanate coupling agent TCA201, add it to 50g of absolute ethanol, stir at 350r / min at 50°C for 1h to obtain the alcoholysis solution of the composite coupling agent, take 1g of calcium sulfate Whiskers, add 30g of complex coupling agent alcoholysis solution, stir at 50°C at 350r / min for 1h, filter to obtain filter residue, put the filter residue in a drying oven, and dry at 120°C for 2h to obtain modified calcium sulfate crystals Whiskers, get 280g polyethylene resin, 450g fast-growing forest wood powder, 25g calcium carbonate, 2g antioxidant, 3g chitosan, 1g stearic acid, 0.2g polyethylene wax, 1g modified calcium sulfate whiskers, add high-speed mixing In the machine, stir at high speed until the temperature is 110°C, keep stirring for 8 minutes and cool to 45°C, then spray 1g of compound coupling agent alcoholysis solution, continue stirring for 12 minutes, and then add it to a parallel twin-screw extruder to extrude ...

example 3

[0030] Take 2g of silane coupling agent KH-550 and 2g of titanate coupling agent TCA201, add them to 60g of absolute ethanol, stir at 400r / min at 60°C for 2h to obtain the alcoholysis solution of the composite coupling agent, take 2g of calcium sulfate Whiskers, add 40g of composite coupling agent alcoholysis solution, stir at 60°C at 400r / min for 2h, filter to obtain filter residue, put the filter residue in a drying oven, and dry at 150°C for 3h to obtain modified calcium sulfate crystals whiskers, get 300g polyethylene resin, 500g fast-growing forest wood powder, 30g calcium carbonate, 3g antioxidant, 4g chitosan, 2g stearic acid, 0.3g polyethylene wax, 2g modified calcium sulfate whiskers, add high-speed mixing In the machine, stir at high speed until the temperature is 120°C, keep stirring for 10 minutes and cool to 50°C, then spray 2g of compound coupling agent alcoholysis solution, continue stirring for 15 minutes, and then add it to a parallel twin-screw extruder to ext...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a bathroom wood-based composite material and a preparation method thereof, and belongs to the technical field of decorative materials. White carbon black and a coloring material are soaked with a composite coupling agent, extremely high activity is shown by utilizing the unique three-dimensional silica structure, small particle size and large specific surface area of the nanometer white carbon black, the adsorbing effect on pigment particles is strong, the surfaces of the pigment particles are tightly wrapped, and shielding effect is formed, so that pigment attenuationcaused by ultraviolet irradiation is greatly reduced, sudden light oxygen degradation of a core layer part is delayed, excessive generation of chromophores is blocked, light oxygen degradation of thematerial is slowed down, obvious dark color change is avoided, the color of the composite material is improved, the requirement of bathroom indoor environment is met, and the composite material is harmonious with the indoor integrated environment.

Description

technical field [0001] The invention relates to a wooden composite material for bathroom and a preparation method thereof, belonging to the technical field of decorative materials. Background technique [0002] With the continuous development of the country's economic construction and the improvement of people's living standards, the contradiction between the supply of timber resources and the demand is also becoming more serious. Since the country implemented the natural forest protection project, vigorously building artificial forests has become an important way to solve the contradiction between my country's timber supply and demand. How to rationally and effectively utilize plantation forest resources and develop its huge potential will become a key topic for forestry researchers. Plantation fast-growing wood has the characteristics of wide distribution, strong adaptability, and short growth cycle. It usually becomes a material in about 10 years, so the material is loos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08K5/09C08K9/04C08K3/36C08K9/06C08L97/02C08L5/08C08K7/08C08K3/26B32B27/32B32B27/30B32B27/08B32B21/00B32B21/08B29C47/06
CPCC08L23/06B32B21/00B32B21/08B32B27/08B32B27/30B32B27/32B32B2307/306B32B2307/546B32B2479/00C08K2003/265C08L97/02C08L2205/025C08L2205/035C08K5/09C08K9/04C08K9/06C08K3/36C08L5/08C08K7/08C08K3/26
Inventor 刘茂龙张桂芳李静
Owner FOSHAN WANYANG BIOLOGICAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com