Preparation method of waterborne adhesive for waterproof corrugated filter material

A technology of water-based adhesives and polyurethane adhesives, which is applied in the direction of adhesive types, ester copolymer adhesives, non-polymer adhesive additives, etc., can solve the problems of high shear strength, production process bottlenecks, filtration The problems such as mutual adhesion between materials can be solved, and the effect of enhancing water resistance, improving production efficiency and high bonding strength can be achieved.

Inactive Publication Date: 2018-10-12
AMERIASIA ACTIVATED CARBON PROD CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The current water-based adhesive has many important advantages. It uses water as the medium, does not use organic solvents, is non-toxic or flammable, is an environmentally friendly product, has no solvent recovery, and has low cost. To bond corrugated filter materials, because the current market products are used to bond corrugated filter materials produced by our company, the adhesive is easily absorbed by corrugated filter materials, resulting in poor bonding strength, or high shear strength, corrugated filter materials Difficult to cut, or the curing time of the glue is long, causing the filter materials to stick to each other during curing, or the water resistance is not good
[0003] Since the existing adhesives are far from meeting the production needs, and the water-based adhesives are widely used
A water-based adhesive suitable for bonding corrugated filter media is hereby developed, hoping to solve the bottleneck of the production process caused by adhesives in the production of corrugated filter media at present, and to provide the possibility for the production of special functional corrugated filter media

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A method for preparing a waterproof corrugated filter material with a water-based adhesive, which consists of the following components in mass percentage: 60% water, 10% polyacrylate, 10% polyurethane adhesive, 10% silica powder, and 5% plasticizer %, thickener 5%.

[0023] This embodiment includes the following steps:

[0024] Step 1: Using deionized water as the dispersion medium, the surfactant composed of polar hydrophilic group and non-polar lipophilic group is mixed with polyacrylate, adding initiator and buffer to emulsify to make polyacrylate Lotion;

[0025] Step 2: Add polyurethane adhesive to the polypropionate emulsion and stir fully to make the polyacrylate emulsion fully react with the polyurethane adhesive to form a uniform liquid;

[0026] Step 3: Add silica powder to the above homogeneous liquid. Silica powder has a porous structure. With sufficient stirring, the viscosity of the liquid increases without deposition of silica powder;

[0027] Step 4: ...

Embodiment 2

[0029] A preparation method of water-based adhesive for waterproof corrugated filter material, which is composed of the following components in mass percentage: 63% of water, 13% of polyacrylate, 8% of polyurethane adhesive, 8% of silica powder, and 4% of plasticizer %, thickener 4%.

[0030] This embodiment includes the following steps:

[0031] Step 1: Using deionized water as the dispersion medium, the surfactant composed of polar hydrophilic group and non-polar lipophilic group is mixed with polyacrylate, adding initiator and buffer to emulsify to make polyacrylate Lotion;

[0032] Step 2: Add polyurethane adhesive to the polypropionate emulsion and stir fully to make the polyacrylate emulsion fully react with the polyurethane adhesive to form a uniform liquid;

[0033] Step 3: Add silica powder to the above homogeneous liquid. Silica powder has a porous structure. With sufficient stirring, the viscosity of the liquid increases without deposition of silica powder;

[00...

Embodiment 3

[0037] A method for preparing a water-based adhesive for a waterproof corrugated filter material, which consists of the following components in mass percentage: 65% water, 15% polyacrylate, 6% polyurethane adhesive, 6% silica powder, and 4% plasticizer %, thickener 4%.

[0038] This embodiment includes the following steps:

[0039] Step 1: Using deionized water as the dispersion medium, the surfactant composed of polar hydrophilic group and non-polar lipophilic group is mixed with polyacrylate, adding initiator and buffer to emulsify to make polyacrylate Lotion;

[0040] Step 2: Add polyurethane adhesive to the polypropionate emulsion and stir fully to make the polyacrylate emulsion fully react with the polyurethane adhesive to form a uniform liquid;

[0041] Step 3: Add silica powder to the above homogeneous liquid. Silica powder has a porous structure. With sufficient stirring, the viscosity of the liquid increases without deposition of silica powder;

[0042] Step 4: Add...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of waterborne adhesive for a waterproof corrugated filter material. The waterborne adhesive for the waterproof corrugated filter material is prepared from,by mass, 60-80% of water, 10-20% of polyacrylate, 5-10% of polyurethane adhesive, 5-10% of silica powder, 1-5% of plasticizer and 1-5% of thickening agent. The preparation method of the waterborne adhesive for the waterproof corrugated filter material is simple; the waterborne adhesive is not easily absorbed by the corrugated filter material, an adhering effect can be achieved simply by using a small quantity of the waterborne adhesive, the bonding strength is high, the water resistance of the adhesive is improved to a certain degree, and more processing modes are provided for post-processingof the corrugated filter material; the surface of the waterborne adhesive is dry and smooth and not attached to the hands, the waterborne adhesive does not harden after being solidified, and the bodyof the waterborne adhesive is soft; when finally cut, the whole waterproof corrugated filter material can be cut, the cutting resistance is low, the waterborne adhesive is not attached to a cutter during cutting, therefore, the waterproof corrugated filter material is cut smoothly under the condition of thick stacks, and the production efficiency is improved.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to a method for preparing a water-based adhesive for a waterproof corrugated filter material. Background technique [0002] The current water-based adhesive has many important advantages. It uses water as the medium, does not use organic solvents, is non-toxic or flammable, is an environmentally friendly product, has no solvent recovery, and has low cost. To bond corrugated filter materials, because the current market products are used to bond corrugated filter materials produced by our company, the adhesive is easily absorbed by corrugated filter materials, resulting in poor bonding strength, or high shear strength, corrugated filter materials Difficult to cut, or the curing time of the glue is long, causing the filter materials to stick to each other during curing, or the water resistance is not good. [0003] Since the existing adhesives are far from meeting production require...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/08C09J175/06C09J11/04
CPCC09J11/04C09J133/08C09J175/06C08L75/06C08K7/26C08L33/08
Inventor 肖永祥张乃明
Owner AMERIASIA ACTIVATED CARBON PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com