Polyester fiber and preparation method thereof

A technology of polyester fiber and poly pairs, which is applied in the field of polyester fiber and its preparation, can solve the problems of antibacterial and unsatisfactory mechanical properties

Inactive Publication Date: 2018-09-07
长沙小新新能源科技有限公司
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its antibacterial and mechanical properties cannot meet the needs of actual use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyester fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The preparation method of described polyester fiber, comprises the following steps:

[0026] S1: Mix polyoxyethylene, ethoxylated glycerin, nano-silica, carbon nanotubes, chitosan, antibacterial modification additives, mechanical property enhancement additives and silane coupling agent KH-570, and heat up to 80-90°C, keep warm for 20-40min, then add polyethylene terephthalate and mix evenly, stir at 1500-2500r / min for 20-40min to form a polyester composition;

[0027] S2: Drying the polyester composition at 70-80° C. for 20-30 minutes and then melt-spinning it into polyester fibers.

Embodiment 1

[0029] A polyester fiber, in parts by weight, comprising the following raw materials: 74 parts of polyethylene terephthalate, 13 parts of polyoxyethylene, 11.5 parts of nano silicon dioxide, 3.2 parts of rare earth coupling agent, ethoxylated 2.8 parts of glycerin, 5.8 parts of carbon nanotubes, 4.3 parts of chitosan, 25.8 parts of antibacterial modification additives, 21.6 parts of mechanical property enhancement additives, and 2.6 parts of silane coupling agent KH-570.

[0030] The antibacterial modification auxiliary agent is prepared according to the following process: 12.3 parts by weight of 3,4-dihydroxybenzaldehyde, 5.6 parts of diphenylmethane diisocyanate, 11.4 parts of distilled water, 7.2 parts of dibutyltin dilaurate, 4.3 parts Mix 1 part of acetic acid and 5.7 parts of methanol evenly, let it stand at room temperature for 4.2h, then add 3.9 parts of sodium borohydride and mix evenly, stir at 746r / min for 36min, the precipitate obtained after suction filtration is d...

Embodiment 2

[0036] A polyester fiber, in parts by weight, comprising the following raw materials: 60 parts of polyethylene terephthalate, 20 parts of polyoxyethylene, 10 parts of nano silicon dioxide, 4 parts of rare earth coupling agent, ethoxylated 2 parts of glycerin, 9 parts of carbon nanotubes, 3 parts of chitosan, 26 parts of antibacterial modification additives, 18 parts of mechanical property enhancement additives, and 3 parts of silane coupling agent KH-5703.

[0037] The antibacterial modification auxiliary agent is prepared according to the following process: 5 parts by weight of 3,4-dihydroxybenzaldehyde, 8 parts of diphenylmethane diisocyanate, 8 parts of distilled water, 8 parts of dibutyltin dilaurate, 2 parts by weight Mix 1 part of acetic acid and 9 parts of methanol evenly, let it stand at room temperature for 3 hours, then add 5 parts of sodium borohydride and mix evenly, stir at 650r / min for 40 minutes, and the precipitate obtained after suction filtration is dialyzed i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses polyester fiber and a preparation method thereof, and belongs to the technical field of preparation of fiber. The polyester fiber is prepared from the following raw materials of polyethylene terephthalate, polyoxyethylene, nanometer silicon dioxide, ethoxylated glycerin, carbon nanotube, chitosan, an antibacterial modifying additive, a mechanical property enhancing additive, and a silane coupling agent KH-570. The preparation method comprises the following steps of preparing a polyester composition, melting, and spinning, so as to obtain the polyester fiber. The prepared polyester fiber has excellent antibacterial and mechanical properties.

Description

technical field [0001] The invention belongs to the technical field of fiber preparation, and in particular relates to a polyester fiber and a preparation method thereof. Background technique [0002] Due to its excellent properties, polyester is widely used in the fields of fiber, film, plastic and so on. Since its inception, polyethylene terephthalate fiber has a series of excellent properties such as high breaking strength and elastic modulus, moderate resilience, excellent heat setting, good heat resistance and light resistance, acid resistance, alkali resistance and corrosion resistance. The fabric has the advantages of anti-wrinkle, cost-free, and good stiffness, and is widely used in clothing, home textiles and other fields. [0003] The Chinese patent application document "A Polyester Fiber and Its Preparation Method (Application Publication No.: CN105220270A)" discloses a polyester fiber and its preparation method. The polyester fiber contains the following raw mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/88D01F1/10
CPCD01F1/10D01F1/103D01F6/88
Inventor 不公告发明人
Owner 长沙小新新能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap