Method for preparing two-component vitrified brick backing glue

A vitrified back, two-component technology, applied in the direction of adhesives, polymer adhesive additives, non-polymer adhesive additives, etc. Difficult pasting, low water absorption of vitrified tiles, etc., to achieve the effect of increased contact area, easy pasting, and improved roughness

Inactive Publication Date: 2018-09-04
许水仙
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The main technical problem to be solved by the present invention is that the low water absorption rate of vitrified bricks and the smooth surface make it difficult to stick vitrified brick back glue. Defects that affect the sticking performance of vitrified tile back glue provide a preparation method for vitrified tile back glue

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing two-component vitrified brick backing glue

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0027] Take sugarcane, extract sugarcane juice with a sugarcane juicer to obtain bagasse, weigh 30g of bagasse and place it in a mortar, grind for 20min, pass through a 100-mesh sieve to obtain sugarcane powder, add the sugarcane powder to the conical flask, Add 100mL of sodium hydroxide solution with a mass fraction of 40% into the shaped bottle, heat up to 120°C, cook for 1h, filter and remove the filtrate to obtain the filter residue, put the filter residue in an oven, heat up to 100°C, and dry for 2h to obtain pretreatment Sugarcane powder: Weigh 20g of pretreated sugarcane powder and add it to a beaker, add 10mL of acrylic acid to the beaker, adjust the pH to neutral with a 10% sodium hydroxide solution to obtain a suspension, and mix the suspension with kaolin according to the mass ratio 3:1 mixing, placed in a high-speed disperser, dispersed for 12 minutes at a speed of 2000r / min, to obtain a pre-dispersed suspension; in parts by weight, 70 parts of a pre-dispersed suspe...

example 2

[0029] Take sugarcane, extract the sugarcane juice with a sugarcane juicer to obtain bagasse, weigh 33g of bagasse and place it in a mortar, grind for 23min, pass through a 100-mesh sieve to obtain sugarcane powder, add the sugarcane powder to the Erlenmeyer flask, Add 110mL of sodium hydroxide solution with a mass fraction of 40% into the shaped bottle, heat up to 125°C, cook for 1.5h, filter and remove the filtrate to obtain the filter residue, put the filter residue in an oven, heat up to 105°C, and dry for 2.5h to obtain Pretreatment sugarcane powder: Weigh 23g pretreatment sugarcane powder and add it to a beaker, add 13mL acrylic acid to the beaker, adjust the pH to be neutral with a 10% sodium hydroxide solution to obtain a suspension, and mix the suspension with kaolin according to The mass ratio is 3: 1 and mixed, placed in a high-speed disperser, dispersed at a speed of 2500r / min for 13 minutes, to obtain a pre-dispersed suspension; in parts by weight, 75 parts of the ...

example 3

[0031] Take sugarcane, extract the sugarcane juice with a sugarcane juicer to obtain bagasse, weigh 35g of bagasse and place it in a mortar, grind for 25min, pass through a 100-mesh sieve to obtain sugarcane powder, add the sugarcane powder to the conical flask, Add 100-120mL of sodium hydroxide solution with a mass fraction of 40% in the shaped bottle, heat up to 130°C, cook for 2h, filter and remove the filtrate to obtain the filter residue, put the filter residue in an oven, heat up to 110°C, and dry for 3h to obtain Pretreated sugarcane powder; weigh 20-25g of pretreated sugarcane powder and add it to a beaker, add 15mL of acrylic acid to the beaker, adjust the pH to neutral with a 10% sodium hydroxide solution to obtain a suspension, and mix the suspension with Kaolin is mixed in a mass ratio of 3:1, placed in a high-speed disperser, and dispersed at a speed of 3000r / min for 15 minutes to obtain a pre-dispersed suspension; in parts by weight, 80 parts of the pre-dispersed ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of preparation of building materials and in particular relates to a method for preparing two-component vitrified brick backing glue. The method disclosed by the invention comprises the following steps: treating sugarcane serving as a raw material to obtain pre-dispersed suspension, mixing the pre-dispersed suspension, cotton stalk bark fibers, ammoniumpersulfate, N,N-methylenebis acrylamide and the like, reacting, extracting with acetone, drying to obtain a component A, performing graft copolymerization on acrylic acid and sugarcane fibers, forminga three-dimensional network structure, and producing a water-absorbent resin, wherein the cotton stalk bark fibers easily crimp when meeting water, the water is difficultly squeezed out, the roughness of the vitrified brick can be improved by the cotton stalk bark fibers, and the bricks are conveniently adhered; mixing a cellulose ether and a castor oil polyurethane prepolymer, dispersing to obtain premixed emulsion, adding quick lime, carboxylic butadiene-styrene latex, fly ash and other materials into the pre-dispersed mixture, performing vacuum defoamation to obtain a component B, and performing network interpenetrating on castor oil polyurethane and methyl silicone rubber, thereby obtaining an adhesive with an IPN (Interpenetrating Polymer Network) structure. The network interpenetrating structure is compact in binding, and the application prospects are wide.

Description

technical field [0001] The invention relates to the technical field of building material preparation, in particular to a method for preparing a two-component back glue for vitrified tiles. Background technique [0002] At present, ceramic bricks with high water absorption rate (5% to 10%) used in home decoration, large clubs, supermarkets and interior and exterior decoration of buildings have low strength, single style, and small size, so they are no longer suitable for high-speed development. market needs. At the same time, vitrified bricks have been widely used in the architectural decoration market due to their advantages of low water absorption, high strength, and many specifications and varieties. [0003] Vitrified tiles are commonly known as porcelain polished tiles. Vitrified tiles are made of quartz sand and mud fired according to a certain proportion, and then polished brightly but do not need to be polished. The surface is as smooth and translucent as a glass mir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/04C09J11/08C09J11/04C09J151/00
CPCC08L2205/035C09J11/04C09J11/08C09J151/00C09J175/04C08L1/26C08L83/04C08L91/00C08L13/02C08K7/26C08L97/02
Inventor 许水仙何伟仁张建初
Owner 许水仙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com