High-gloss and high-impact-resistance ASA/PMMA (Acrylonitrile Styrene Acrylate/Polymethyl Methacrylate) material for automobile and preparation method thereof

A high-impact, high-gloss technology, which is used in the preparation of high-gloss and high-impact automotive ASA/PMMA materials and high-gloss and high-impact automotive ASA/PMMA materials, can solve the problem of poor impact performance and low cost. , the problem of low gloss of the material, to achieve the effect of improving the compatibility effect, low cost and simple process

Inactive Publication Date: 2018-08-10
贵州凯科特材料有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this patent does not solve the problem of low gloss of the material, so it is difficult to be applied in some high gloss parts
[0006] Chinese Patent Publication No. CN105419205A disclosed a high-gloss spray-free PMMA / ASA alloy resin composition and its preparation method on March 23, 2016. The preparation process of the method is relatively simple and the cost is low, but the patent prepared The impact performance of the material is not good, so it is difficult to be applied in some parts that require excellent impact performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-gloss and high-impact-resistance ASA/PMMA (Acrylonitrile Styrene Acrylate/Polymethyl Methacrylate) material for automobile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A preparation method of ASA / PMMA material for high-gloss and high-impact automobiles, comprising the following steps:

[0027] (1) 100 parts of ASA (weight-average molecular mass is 100000g / mol, acrylate percentage content 15%) is taken by weighing; PMMA (weight-average molecular mass is 150000g / mol) 50 parts; Maleic anhydride (mass Percent purity greater than or equal to 99.5%) 5 parts; Dicumyl peroxide 5 parts; 2,4-dichlorobenzoyl peroxide 3 parts; Methyl methacrylate-butadiene-styrene terpolymer 20 Parts; tetrakis-[β-(3.2-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester (antioxidant 1010) 0.25 parts; three (2,4-di-tert-butyl) phenyl phosphite (Antioxidant 168) 0.25 parts; Halogen-free high gloss grease black pigment 0.5 parts. Mix ASA, PMMA, maleic anhydride, 2,4-dichlorobenzoyl peroxide and methyl methacrylate-butadiene-styrene terpolymer for 5 minutes until the appearance is uniform; Cumene, Antioxidant 1010, Antioxidant 168 and Halogen-free high-...

Embodiment 2

[0030] A preparation method of ASA / PMMA material for high-gloss and high-impact automobiles, comprising the following steps:

[0031] (1) 100 parts of ASA (weight-average molecular mass is 300000g / mol, acrylate percentage content 25%) is taken by weighing; PMMA (weight-average relative molecular mass is 100000g / mol) 60 parts; Maleic anhydride (mass Percent purity greater than or equal to 99.5%) 2 parts; dicumyl peroxide 12 parts; 2,4-dichlorobenzoyl peroxide 5 parts; methyl methacrylate-butadiene-styrene terpolymer 15 parts Parts; Tetrakis-[β-(3.2-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester (Antioxidant 1010) 0.5 part; Tris(2,4-di-tert-butyl)phenyl phosphite (Antioxidant 168) 0.5 part; Halogen-free high gloss grease black pigment 1 part. Mix ASA, PMMA, maleic anhydride, 2,4-dichlorobenzoyl peroxide and methyl methacrylate-butadiene-styrene terpolymer for 4 minutes until the appearance is uniform; add di Cumene, Antioxidant 1010, Antioxidant 168 and Halog...

Embodiment 3

[0034] A preparation method of ASA / PMMA material for high-gloss and high-impact automobiles, comprising the following steps:

[0035](1) take by weighing 100 parts of ASA (weight-average molecular mass is 500000g / mol, acrylate percentage content 70%); PMMA (weight-average relative molecular mass is 50000g / mol) 40 parts; Maleic anhydride (mass Percent purity greater than or equal to 99.5%) 8 parts; 8 parts of dicumyl peroxide; 8 parts of 2,4-dichlorobenzoyl peroxide; 10 parts of methyl methacrylate-butadiene-styrene terpolymer Parts; tetrakis-[β-(3.2-di-tert-butyl-4-hydroxyphenyl)propionic acid] pentaerythritol ester (antioxidant 1010) 1 part; halogen-free high-gloss black pigment 2 parts. Mix ASA, PMMA, maleic anhydride, 2,4-dichlorobenzoyl peroxide and methyl methacrylate-butadiene-styrene terpolymer for 3 minutes until the appearance is uniform; add di Cumene, Antioxidant 1010, Antioxidant 168 and Halogen-free high-gloss black pigment, mixed until the appearance is uniform;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
transparencyaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-gloss and high-impact-resistance ASA / PMMA (Acrylonitrile Styrene Acrylate / Polymethyl Methacrylate) material for an automobile and a preparation method thereof. The high-gloss and high-impact-resistance ASA / PMMA material is prepared by the following steps: taking the following raw materials in parts by weight: 100 parts of ASA, 40 to 60 parts of PMMA, 2 to 8 parts ofmaleic anhydride, 3 to 8 parts of 2,4-dichlorobenzoyl peroxide and 10 to 20 parts of impact modifying agent MBS; mixing for 3 to 5min until the appearance is uniform; adding 5 to 12 parts of dicumyl peroxide, 0.5 to 2 parts of antioxidant and 0.5 to 3 parts of halogen-free and high-gloss grease black pigment; carrying out mixing treatment until the appearance is uniform; adding mixed materials into a hopper of a double-screw extruder and melting and extruding, wherein the double-screw extruder has first-region temperature of 170 to 190 DEG C, second-region temperature of 175 to 195 DEG C, thethird-region temperature of 180 to 200 DEG C, the fourth-region temperature of 185 to 200 DEG C and the machine head temperature of 200 to 220 DEG C, the staying time is 2 to 3min and the pressure is10 to 20Mpa; extruding and granulating. The high-gloss and high-impact-resistance ASA / PMMA material disclosed by the invention has the advantages of high gloss, high impact resistance and relatively high weather resistance.

Description

technical field [0001] The invention belongs to the field of polymer materials, and specifically relates to an ASA / PMMA material for high-gloss and high-impact automobiles, and also relates to a preparation method of the ASA / PMMA material for high-gloss and high-impact automobiles. Background technique [0002] Acrylonitrile-acrylate-styrene terpolymer (ASA) is a new type of resin with improved weather resistance compared to ABS. Compared with ABS, because the butadiene component is replaced by acrylate, it is no longer It has an unsaturated structure, so it has excellent weather resistance, which is about 10 times higher than that of ABS. At the same time, its mechanical properties, processing properties, electrical insulation, and chemical resistance are similar to ABS. ASA products can be used outdoors directly. After being exposed to sunlight for 9-15 months, the impact strength and elongation hardly decrease, and the color hardly changes. It can be applied to some ap...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L33/20C08L33/12C08L51/04C08K5/14C08F291/12C08F291/06C08F222/06
CPCC08F265/04C08F265/08C08L33/20C08L2205/02C08L2205/03C08L2205/08C08L2207/53C08L33/12C08L51/04C08K5/14C08F222/06
Inventor 高京靳灵杰刘渝杨荣强雷振刚杨通晓吴俊熊晏安
Owner 贵州凯科特材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com