Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Preparation method of Taichi stone cellulose fiber

A cellulose fiber and tai chi stone technology, which is applied in the chemical characteristics of fibers, rayon manufacturing, viscose rayon and other directions, can solve the problem of not showing the preparation method of tai chi stone cellulose fiber, etc., to ensure smoothness and smoothness. Comfort, small size, well-distributed effect

Inactive Publication Date: 2018-07-27
SATERI JIUJIANG FIBER CO LTD +1
View PDF10 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These two patents are elaborations on the application of Taichi Stone polyester fiber field, and do not show the preparation method of Tai Chi Stone cellulose fiber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment

[0020]Specific embodiment: 98% sulfuric acid and Tai Chi stone are heated to 50-90 ° C and washed for 1-3 hours according to the ratio of 5-9% (w / w), filtered through a 100-500 mesh filter screen, and then added 2-10 times the mass Wash three times with several deionized water for 10-30min; after drying at 100-200 ℃ for 1-5h, add 2-5 times the mass of deionized water at room temperature, and grind at 50-600rpm for 1-3h with a nano high-speed stirring ball mill , and then under nitrogen protection, calcined at 400-600℃ for 1-4h, 600-800℃ for 1-4h, 800-1200℃ for 1-4h, 1200-1500℃ for 1-3h, and then added to 2- 5 times the mass concentration of 0.1-2% non-foam dispersant sodium polyacrylate dispersant aqueous solution and 0.1-2% cellulose-based viscosity-adjusting auxiliary are added at a stirring speed of 100-300 rpm. By pre-spinning injection, the suspension of Taiji stone, which has the functions of far-infrared, anti-ultraviolet, antibacterial, and the functions of improving h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of Taichi stone cellulose fiber. According to the method, a Taichi stone suspension with far infrared, uvioresistant and antibacterial functions and a cellulose sulfonate solution are mixed uniformly by injection before spinning, and a finished product is obtained by wet spinning and aftertreatment; according to the obtained Taichi stone cellulose fiber,Taichi stone content is 1%-8% (w / w), far infrared emission rate is higher than or equal to 90%, UPF (ultraviolet protection factor) is larger than or equal to 50, bacteriostasis rate is higher than or equal to 99%, breaking strength is larger than or equal to 2.5 cN / dtex, elongation at break is larger than or equal to 15%, color fastness to washing is higher than or equal to level 4, and the Taichi stone cellulose fiber can convert high-frequency beta waves (14-30 Hz) in human brain waves into brain wave theta waves (4-8 Hz) and alpha waves (8-14 Hz) with low frequency spectra. The Taichi stone cellulose fiber not only has excellent far infrared, uvioresistant and antibacterial functions, but also has functions of relieving depression and improving sleep, breaking strength and elongationat break are higher, performance is lasting and stable, besides, the technology is mature, the process is simple and easy to control, and industrial production is facilitated.

Description

technical field [0001] The invention specifically relates to a preparation method of taiji stone cellulose fiber. Background technique [0002] Taiji stone is a natural ore, silicic quartz ore, except that it contains 87.53% SiO 2 In addition, it also contains a large amount of K 2 O, CaO, TiO 2 and other oxides and various trace metal mineral elements such as titanium, potassium and germanium. Nano Tai Chi particles with a diameter of 97-189.2nm can refine water molecules, improve human blood microcirculation, promote cell activity, increase metabolism, and relax mood; Converted into low-spectrum brain waves theta wave (4~8Hz) and alpha wave (8~14Hz), the function of relieving depression and improving sleep; also has excellent anti-ultraviolet function, its line protection factor UPFAV reaches 232.87, UPF level 50 +; In addition, the Tai Chi stone also has good antibacterial function, the antibacterial rate of Klebsiella pneumoniae is 99.8%, and the bacteriostatic rate ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F2/08D01F1/10
CPCD01F1/103D01F2/08
Inventor 张文涛林荣银王荣华陈小荣王兵吕志军顾宇鹭刘兰燕
Owner SATERI JIUJIANG FIBER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products