Nitrogen containing martensitic stainless steel for cutting tool and manufacturing method of nitrogen containing martensitic stainless steel

A martensitic stainless steel and manufacturing method technology, applied in the field of martensitic stainless steel, can solve problems such as high difficulty, high equipment and manufacturing process requirements, and unfavorable promotion of metallurgical enterprises, and achieve low production costs, low equipment requirements, and reduced margins. The effect of crack risk

Inactive Publication Date: 2018-07-13
WUHAN UNIV OF SCI & TECH
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

"A kind of martensitic stainless steel and its manufacturing method" (CN104471095) patent technology, through the thin strip casting and rolling method, the rapid cooling casting method is used to manufacture martensitic stainless steel with a size of 1mm o

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nitrogen containing martensitic stainless steel for cutting tool and manufacturing method of nitrogen containing martensitic stainless steel
  • Nitrogen containing martensitic stainless steel for cutting tool and manufacturing method of nitrogen containing martensitic stainless steel
  • Nitrogen containing martensitic stainless steel for cutting tool and manufacturing method of nitrogen containing martensitic stainless steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] The present invention will be further described below in conjunction with the accompanying drawings and specific embodiments, which are not intended to limit the protection scope thereof.

[0028] The chemical composition and content of the nitrogen-containing martensitic stainless steel for cutting tools in this specific embodiment are: C is 0.45-0.70wt%; Cr is 13.0-17.0wt%; N is 0.10-0.25wt%; Si is 0.50-0.80wt%. wt%; Mn is 0.40~1.0wt%; Ca is 0.0015~0.0065wt%; V≤0.20wt%, Nb≤0.025wt%; Als≤0.025wt%; Mo≤0.03wt%, P≤0.008wt%; S ≤0.005wt%; the rest is Fe and unavoidable elements. The above chemical composition also satisfies: C+N is 0.60-0.85wt%.

[0029] The chemical composition and content thereof of each embodiment in this specific embodiment are as shown in table 1:

[0030] The chemical composition and content thereof of each embodiment in table 1 this specific embodiment

[0031]

[0032] The manufacturing method of nitrogen-containing martensitic stainless steel...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to nitrogen containing martensitic stainless steel for a cutting tool and a manufacturing method of the nitrogen containing martensitic stainless steel. According to the technical scheme, chemical components of the nitrogen containing martensitic stainless steel for the cutting tool comprise 0.45wt%-0.70wt% of C, 13.0 wt%-17.0wt% of Cr, 0.10wt%-0.25wt% of N, 0.50wt%-0.80wt% of Si, 0.40wt%-1.0wt% of Mn, 0.0015wt%-0.0065wt% of Ca, not larger than 0.20wt% of V, not larger than 0.025wt% of Nb, not larger than 0.025wt% of Als, not larger than 0.03wt% of Mo, not larger than 0.008wt% of P, not larger than 0.005wt% of S and the balance Fe and inevitable elements. Meanwhile, the above chemical components meet the condition that C+N is 0.60-0.85wt%. The manufacturing method ofthe nitrogen containing martensitic stainless steel for the cutting tool comprises the steps of vacuum induction smelting, normal-pressure nitrogen increasing, casting, casting blank heating, rolling,quenching and tempering. The nitrogen containing martensitic stainless steel has the advantages that the alloy components are simple, the process is simple and convenient, the production cost is low,and large-scale production is easy. The manufactured nitrogen containing martensitic stainless steel for the cutting tool is high in hardness and good in toughness.

Description

technical field [0001] The invention belongs to the technical field of martensitic stainless steel. Specifically relates to a nitrogen-containing martensitic stainless steel for cutting tools and a manufacturing method thereof. Background technique [0002] Martensitic stainless steel traditionally used in the manufacture of cutting tools, such as 4-5Cr15MoV series and 9Cr18MoV, after quenching and low-temperature tempering, has a hardness of 56-58HRC, certain toughness and processing performance, and corrosion resistance under general corrosion conditions. Therefore, it has been applied in the cutting tool manufacturing industry. With the continuous advancement of metallurgical technology, the cutting tool manufacturing industry has higher and higher technical and cost requirements for martensitic stainless steel, and puts forward stricter requirements for its structure and performance control, especially for high-end civilian kitchens, machinery Cutting tools manufacture...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/18C22C38/24C22C38/26C22C38/06C22C38/22C22C33/06C21D8/02C21D1/18
CPCC22C38/02C21D1/18C21D8/0205C21D8/0226C21D8/0247C21D2211/008C22C33/06C22C38/001C22C38/04C22C38/06C22C38/18C22C38/22C22C38/24C22C38/26
Inventor 张莉芹吴开明张国宏成林黄刚张弦童明强吴光辉雷金薇
Owner WUHAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap