A process for producing fuel oil and chemical raw materials using coal and biomass
A chemical raw material and biomass technology, which is applied in the field of co-smelting of coal and biomass, can solve the problems of unrealized pulping and mixing production technology, low liquefaction efficiency, limited coal powder content, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0090] Preparation of the first catalyst:
[0091] (1) selecting biochar as the first biochar carrier;
[0092] (2) Loading the first active component on the first biomass carbon carrier to prepare the first catalyst.
[0093] Wherein, the first active component is iron oxide, and the first active component accounts for 50% of the mass of the first biochar carrier in terms of the mass of metal elements;
[0094] The specific steps of loading in step (2) are: mixing the aqueous solution of the first active component with the first biochar carrier to prepare a suspension, adding a precipitant to precipitate the first active component on the first biochar carbon carrier, then washed and dried to obtain the first catalyst; wherein, the precipitating agent is an aqueous solution of at least one of ammonia water or alkali metal carbonates, bicarbonates, and hydroxides, and the precipitation The process temperature is controlled at 90°C and the pH value is 9.
[0095] Preparati...
Embodiment 2
[0099] A process for producing fuel oil and chemical raw materials by utilizing coal and biomass, comprising the following steps:
[0100] Pretreatment of coal raw materials:
[0101] (1) Take lignite, dry and dehydrate it, pulverize to a median particle size of 50 μm, and then send it to a briquetting machine for extrusion molding at a molding pressure of 5 MPa to obtain lignite compressed material.
[0102] (2) Send the compressed lignite material into a ball mill for pulverization to obtain a pulverized lignite material with a median particle size of 30 μm for use.
[0103] Preparation and liquefaction of biomass coal water slurry:
[0104] After deashing the above-mentioned pulverized lignite material, mix it with biochar loaded with iron oxyhydroxide and a vulcanizing agent to obtain a mixture, and add the mixture to the mixture of animal oil and water to form the biomass coal-water slurry. Hydrogen gas is introduced into the biomass coal-water slurry to react, and ...
Embodiment 3
[0108] A process for producing fuel oil and chemical raw materials by utilizing coal and biomass, comprising the following steps:
[0109] Pretreatment of biomass raw materials:
[0110] (1) Take the reed, dry and dehydrate it until the water content is 1wt%, and then send it into the jet mill for crushing to obtain the primary crushed reed material with a particle size of D 50 is 200 μm.
[0111] (2) Send the reed primary pulverized material into a briquetting machine or a plodder for extrusion molding with a molding pressure of 3 MPa to obtain a reed compressed material.
[0112] (3) The reed compressed material is sent into the jet mill, and secondary pulverization is carried out to obtain the reed secondary pulverization material, particle size D 50 40 μm, set aside.
[0113] Pretreatment of coal raw materials:
[0114] (1) Take Shendong long-flame coal, dry and dehydrate it, and then send it to a ball mill for crushing to obtain primary crushed material of Shendon...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
viscosity | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com