A process for preparing maleic anhydride by n-butane oxidation

A process method and technology of n-butane, which is applied in the field of reaction process of n-butane oxidation to maleic anhydride, can solve the problems of reducing the effective volume of the reactor, increasing the product yield, reducing the production efficiency, etc. High anhydride yield and the effect of overcoming temperature drop

Active Publication Date: 2022-01-04
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] USP4,855,459 proposes a method for preparing maleic anhydride by oxidation of n-butane, which is carried out by diluting and packing inert silica-alumina balls and catalysts, and reducing the hot spots of reaction by diluting and packing at the hot spots of the reaction tube. temperature, to improve the selectivity of maleic anhydride, the purpose of increasing the yield of maleic anhydride, and at the same time the stability period of the catalyst has been extended, but the unfavorable factor is the addition of inert materials, which reduces the effective volume of the reactor and also reduces the production efficiency
[0014] In the existing fixed-bed n-butane oxidation to maleic anhydride technology, catalysts with different activities are loaded in the reactor along the direction of reactant flow, so that when the catalyst is loaded, the catalytic activity changes along the feed direction according to the reaction requirements, so as to realize the oxidation The method of controlling the reaction, realizing the recycling of reaction tail gas, and increasing the product yield has not been reported so far

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A process for preparing maleic anhydride by n-butane oxidation
  • A process for preparing maleic anhydride by n-butane oxidation
  • A process for preparing maleic anhydride by n-butane oxidation

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] (2) Preparation of vanadium phosphorus oxygen catalyst

[0048] The vanadium phosphorus oxide obtained in step (1) is first shaped, and the shape of the obtained vanadium phosphorus oxygen catalyst can be a compressed tablet, a spherical shape, an extruded rod, etc., and the phase of the obtained catalyst precursor is (VOHPO 4 0.5H 2 o).

[0049] (3) Activation treatment of vanadium phosphorus oxygen catalyst

[0050] The shaped catalyst precursor in step (2) is activated in an atmosphere of nitrogen or inert gas, or in an atmosphere of n-butane / air mixture, to obtain an activated vanadium-phosphorus-oxygen catalyst.

[0051] Wherein in step (3), the activation temperature is generally 350-450°C, preferably 375-425°C; the activation time is generally 5-40 hours, preferably 12-20 hours. The volume space velocity of nitrogen, inert gas or n-butane / air mixed atmosphere is generally 100-2000h -1 , preferably 500~1000h -1 .

[0052] In the present invention, the prepar...

Embodiment 1

[0057] exist figure 1 Add 442.95 kg of isobutanol, 29.53 kg of vanadium pentoxide, 0.3 kg of ferric nitrate hexahydrate, and 0.5 kg of zirconium nitrate into the reaction kettle shown with a stirring device and a reflux condensing device. High reaction temperature and kept at 100±2°C, carry out reflux reaction, keep reflux time for 4 hours, then add 47.50kg of phosphoric acid with a concentration of 85%, the phosphorus / vanadium molar ratio is 1.27, continue to reflux for 8 hours, and the reaction ends. After the reaction solution was cooled to room temperature, it was vacuum filtered, and the filter cake was rinsed with a small amount of isobutanol three times, then the filter cake was placed in an enamel tray and dried naturally at room temperature, dried in an oven at 100°C for 8 hours, and finally dried in a muffle furnace. Calcined at 250°C for 5 hours to obtain a dark brown catalyst precursor.

[0058] Add the catalyst precursor prepared above to graphite powder with a ...

Embodiment 2

[0062] exist figure 1 Add 442.95 kg of isobutanol, 29.53 kg of vanadium pentoxide, 0.3 kg of ferric nitrate hexahydrate, and 0.5 kg of zirconium nitrate into the reaction kettle shown with a stirring device and a reflux condensing device. High reaction temperature and kept at 100±2°C, carry out reflux reaction, keep reflux time for 4 hours, then add 44.13kg of phosphoric acid with a concentration of 85%, the phosphorus / vanadium molar ratio is 1.18, continue to reflux for 8 hours, and the reaction ends. After the reaction solution was cooled to room temperature, it was vacuum filtered, and the filter cake was rinsed three times with a small amount of isobutanol to complete the reaction. The filter cake was put into an enamel dish and air-dried at room temperature, dried in an oven at 100°C for 8 hours, and finally calcined in a muffle furnace at 250°C for 5 hours to obtain a dark brown catalyst precursor.

[0063] Add the catalyst precursor prepared above to graphite powder w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a process for preparing maleic anhydride by n-butane oxidation. Mix n-butane, air and circulating tail gas, and the resulting mixed reaction gas passes through two or more reaction zones in series in parallel, and reacts with the vanadium-phosphorus-oxygen catalyst under oxidation reaction conditions; except for the most downstream reaction zone , each of the reaction zones includes more than two catalyst beds; wherein, according to the contact sequence with the mixed reaction gas, the P / V molar ratio of the catalyst in the downstream reaction zone is lower than the P / V molar ratio of the catalyst in the upstream reaction zone. V molar ratio; and, in each of said reaction zones except the most downstream reaction zone, the P / V molar ratio in the downstream catalyst bed is higher than the P / V molar ratio in the upstream catalyst bed. The method of the invention can give full play to the activity of the catalyst, especially in the tail gas recycling process, it can more compensate for the influence of the conversion rate drop caused by the oxygen content drop in the raw material, reduce the reaction hot spot, and improve the product selectivity.

Description

technical field [0001] The invention relates to a process for preparing maleic anhydride by n-butane oxidation, which can be used in the reaction process of n-butane oxidation for maleic anhydride using a fixed bed process. Background technique [0002] Maleic anhydride, also known as maleic anhydride, is an important organic chemical raw material and the third largest organic anhydride in the world after phthalic anhydride and acetic anhydride. It is widely used in petrochemical, food processing, and pharmaceutical industries. , Building materials and other industries. Its specific applications include the manufacture of unsaturated polyester resins, alkyd resins, maleic acid (maleic acid), fumaric acid (fumaric acid), as well as pesticides, coatings, glass fiber reinforced plastics, lubricating oil additives, paper chemistry Product additives, surfactants, etc. The advent of the new method of maleic anhydride esterification and low-pressure hydrogenation to produce 1,4-b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07D307/60
CPCC07D307/60
Inventor 王海波程谨宋丽芝勾连科侯学伟刘新宇
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products