Method for preparing high-efficiency oil absorption material by utilizing bambusa emeiensis

An oil-absorbing material and high-efficiency technology, applied in chemical instruments and methods, plant raw materials, chemical post-treatment of fibers, etc., can solve problems such as the limitation of the coupling degree of additives and fibers, the limitation of the strength of oil-absorbing materials, and the complexity of preparation methods. Achieve the effects of cheap raw materials, fast oil absorption rate, and simple preparation process

Inactive Publication Date: 2018-05-04
SUZHOU BD ENVIRONMENTAL PROTECTION
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Inorganic materials such as activated carbon, expanded graphite, peat, silica, organically modified clay, etc., have been seldom used because of their low oil absorption rate and difficulty in recycling after oil absorption; organic synthetic materials include polypropylene, polyurethane foam, acrylate They have good lipophilicity and oil absorption efficiency, but their expensive cost and refractory property limit their application; natural polymer materials, because of their high oil absorption rate, have a wide range of sources, low prices, And biodegradable, relatively safe has become the focus of research
[0003] Because natural fibers are generally short and thin, and the strength is weak, the oil-absorbing materials prepared by natural fibers have poor mechanical properties. In the prior art, additives are often used to improve the fiber strength of oil-absorbing materials, but the preparation method is usually complicated. , and the degree of coupling between additives and fibers is limited, which greatly limits the improvement of the strength of oil-absorbing materials prepared from natural fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] This embodiment provides a method for preparing high-efficiency oil-absorbing materials by using Cizhu, the method is as follows:

[0022] S1: Cut the fresh Cizhu into 10cm length bamboo slices, then soak the bamboo slices in a softening solution, the softening solution is 100 parts by weight of water, 10 parts by weight of milk soap, 2 parts by weight of mineral oil and 10 parts by weight of emulsifier.

[0023] Putting the bamboo chips soaked in the softening solution into a vacuum tank with a vacuum degree of -0.05MPa for softening treatment, the softening treatment time is 30min, wherein a microwave generator is provided in the vacuum tank, and the microwave frequency produced by the microwave generator is 200MHz;

[0024] S2: Rinse the softened bamboo chips with deionized water, and use a fiber splitter to make the bamboo chips into a fiber bundle state;

[0025] S3: Weigh the bamboo chips in the fiber bundle state and put them into a pressure tank, add a reactio...

Embodiment 2

[0032] This embodiment provides a method for preparing high-efficiency oil-absorbing materials by using Cizhu, the method is as follows:

[0033] S1: fresh Cizhu is cut into 12cm long bamboo slices, then the bamboo slices are soaked in a softening solution, the softening solution is 100 parts by weight of water, 12 parts by weight of milk soap, 3 parts by weight of mineral oil and 15 parts by weight of emulsifier.

[0034] Putting the bamboo chips soaked in the softening solution into a vacuum tank with a vacuum degree of -0.02MPa for softening treatment, the softening treatment time is 30min, wherein a microwave generator is provided in the vacuum tank, and the microwave frequency produced by the microwave generator is 400MHz;

[0035] S2: Rinse the softened bamboo chips with deionized water, and use a fiber splitter to make the bamboo chips into a fiber bundle state;

[0036] S3: Weigh the bamboo chips in the fiber bundle state and put them into a pressure tank, add a reac...

Embodiment 3

[0043] This embodiment provides a method for preparing high-efficiency oil-absorbing materials by using Cizhu, the method is as follows:

[0044]S1: fresh Cizhu is cut into 15cm long bamboo slices, and then the bamboo slices are soaked in a softening solution, the softening solution is 100 parts by weight of water, 15 parts by weight of milk soap, 5 parts by weight of mineral oil and 20 parts by weight of emulsifier.

[0045] Putting the bamboo chips soaked in the softening solution into a vacuum tank with a vacuum degree of -0.01MPa for softening treatment, the softening treatment time is 30min, wherein a microwave generator is provided in the vacuum tank, and the microwave frequency produced by the microwave generator is 500MHz;

[0046] S2: Rinse the softened bamboo chips with deionized water, and use a fiber splitter to make the bamboo chips into a fiber bundle state;

[0047] S3: Weigh the bamboo chips in the fiber bundle state and put them into a pressure tank, add a r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Breaking strengthaaaaaaaaaa
Breaking strengthaaaaaaaaaa
Breaking strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for preparing a high-efficiency oil absorption material by utilizing bambusa emeiensis. The method comprises the following steps: cutting fresh bambusa emeiensis, softening, and splitting; placing split fiber bundle shaped bamboo chips into a pressure tank, and reacting with a reaction solution at a temperature of 150-180 DEG C for 20-30 minutes so as to obtain bambusa emeiensis fibers; and ball-milling the bambusa emeiensis fibers into bambusa emeiensis fiber powder, reacting the bambusa emeiensis fiber powder with ammonium persulfate, 1,4-butylene glycol diacrylate, triethanolamine and dodecyl methacrylate reaction liquid at a constant temperature of 70-80 DEG C for 2-3 hours, washing and drying the obtained product, thereby obtaining the high-efficiencyoil absorption material. The method disclosed by the invention is simple and low in cost, and the prepared oil absorption material has the advantages of being high in mechanical strength, high in oilabsorption rate and biodegradable.

Description

technical field [0001] The invention relates to the technical field of oil-absorbing materials, in particular to a method for preparing high-efficiency oil-absorbing materials by using bamboo. Background technique [0002] In recent years, in the process of oil extraction, refining, transportation, transfer and use of oil products, crude oil and refined oil leakage incidents have occurred frequently, and the pollution to the water environment has become more and more serious. The development of high-efficiency oil-absorbing materials has always been a concern of people. hotspot. Oil-absorbing materials can generally be divided into inorganic materials, organic synthetic materials and natural polymer materials. Inorganic materials such as activated carbon, expanded graphite, peat, silica, organically modified clay, etc., have been seldom used because of their low oil absorption rate and difficulty in recycling after oil absorption; organic synthetic materials include polypro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F289/00C08F222/14C08F220/18C09K3/32D01C1/00D01B1/10
CPCC09K3/32D01B1/10D01C1/00C08F289/00C08F220/1812C08F222/102
Inventor 王菊华张金龙蒲婷婷王菊霞
Owner SUZHOU BD ENVIRONMENTAL PROTECTION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap