High-strength light-weight brick and preparation method of same

A lightweight brick, high-strength technology, applied in the field of building materials, can solve the problems of poor wear resistance and thermal insulation, and achieve the effect of improving thermal shock resistance, good thermal conductivity and mechanical properties.

Active Publication Date: 2018-04-27
铜仁筱启环保科技有限公司
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The main technical problem to be solved by the present invention is to provide a high-strength lightweight brick and its preparation method in view of the shortcomings of traditional lightweight bricks in terms of mechanical properties, thermal shock resistance, wear resistance and thermal insulation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength light-weight brick and preparation method of same

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0025] Put sepiolite and organic acid in a single-necked flask at a mass ratio of 1:100, and place the single-necked flask in a magnetic stirrer with a digital display speed measurement and constant temperature, and heat and stir at a temperature of 100°C and a speed of 500r / min. Mix for 50 minutes to obtain a mixed solution, then place the mixed solution in a rotary evaporator, and concentrate under reduced pressure for 50 minutes at a temperature of 80°C, a pressure of 800 kPa, and a rotational speed of 80 r / min to obtain a concentrated solution, and then place the concentrated solution in In an oven, at a temperature of 110°C, dry to constant weight to obtain a dried material, and then put the dried material in a ball mill to pulverize to obtain a modified sepiolite; mix agar powder and water in a mass ratio of 1:100 Add it into a beaker, stir and mix with a glass rod for 30 minutes, let it stand for swelling for 4 hours, then move the beaker into a magnetic stirrer with a d...

example 2

[0027] Put sepiolite and organic acid in a single-necked flask at a mass ratio of 1:100, and place the single-necked flask in a magnetic stirrer with a digital display speed measurement and constant temperature, and heat and stir at a temperature of 100°C and a speed of 500r / min. Mix for 50 minutes to obtain a mixed solution, then place the mixed solution in a rotary evaporator, and concentrate under reduced pressure for 50 minutes at a temperature of 80°C, a pressure of 800 kPa, and a rotational speed of 80 r / min to obtain a concentrated solution, and then place the concentrated solution in In an oven, at a temperature of 110°C, dry to constant weight to obtain a dried material, and then put the dried material in a ball mill to pulverize to obtain a modified sepiolite; mix agar powder and water in a mass ratio of 1:100 Add it into a beaker, stir and mix with a glass rod for 30 minutes, let it stand for swelling for 4 hours, then move the beaker into a magnetic stirrer with a dig...

example 3

[0029] Put sepiolite and organic acid in a single-necked flask at a mass ratio of 1:100, and place the single-necked flask in a magnetic stirrer with a digital display speed measurement and constant temperature, and heat and stir at a temperature of 100°C and a speed of 500r / min. Mix for 50 minutes to obtain a mixed solution, then place the mixed solution in a rotary evaporator, and concentrate under reduced pressure for 50 minutes at a temperature of 80°C, a pressure of 800 kPa, and a rotational speed of 80 r / min to obtain a concentrated solution, and then place the concentrated solution in In an oven, at a temperature of 110°C, dry to constant weight to obtain a dried material, and then put the dried material in a ball mill to pulverize to obtain a modified sepiolite; mix agar powder and water in a mass ratio of 1:100 Add it into a beaker, stir and mix with a glass rod for 30 minutes, let it stand for swelling for 4 hours, then move the beaker into a magnetic stirrer with a d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-strength light-weight brick and a preparation method of same and belongs to the technical field of building materials. The method includes steps of: 1) heating, stirringand mixing sepiolite and organic acid according to mass ratio of 1:50-1:100, and performing pressure reducing concentration, drying and crushing to prepare modified sepiolite; 2) stirring and mixingfly ash, a cementing material, bauxite, the modified sepiolite, coke, sawdust, gypsum, papermaking black liquid, a sodium fluoride solution, nano iron powder, sludge, fiber granular materials, agar liquid, magnesia, volcanic ash, magnesium chloride and water to prepare mixture slurry; 3) injecting the mixture slurry into a mould, allowing the mould to stand, demolding the mixture, and performing high pressure steam curing to obtain a brick green body; 4) performing nitrogen charging high-temperature sintering to the green body to obtain the high-strength light-weight brick. The high-strength light-weight brick has excellent mechanical performance, thermal shock resistance and heat preservation function; besides, wear resistance is also improved.

Description

technical field [0001] The invention discloses a high-strength lightweight brick and a preparation method thereof, belonging to the technical field of building materials. Background technique [0002] Lightweight bricks generally refer to foam bricks, which are used in normal indoor partition walls, which can effectively reduce the load on the floor and have a good sound insulation effect. The strength products use high-quality platy corundum and mullite as aggregates, sillimanite composite as the matrix, and special additives and a small amount of rare earth oxides are mixed and mixed, and then formed by high pressure and fired at high temperature. Ordinary lightweight heat-insulating refractory bricks are made of clay, high-alumina high-strength floating pearl bricks, low-iron mullite, high-alumina poly light-weight heat-insulating firebricks, and diatomite heat-insulating firebricks. [0003] Although the traditional ceramic tile decoration has many advantages, such as g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/06C04B38/00C04B33/132C04B33/135C04B33/13
CPCC04B33/13C04B33/1321C04B33/1352C04B33/1355C04B38/0022C04B38/0675C04B2235/3217C04B2235/3445C04B2235/405C04B2235/444C04B2235/445C04B2235/6022C04B2235/6562C04B2235/6567C04B2235/661Y02P40/60
Inventor 黄彬彬殷磊陈一水
Owner 铜仁筱启环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com