Preparation method for green environment-friendly fireproof coating

A fire-resistant paint, green and environmental protection technology, applied in the field of paint, can solve the problems of poor adsorption of fire-resistant paint paint, consume a lot of manpower, material resources, and can not satisfy users, etc., and achieve the effects of low cost, manpower saving, and convenient configuration.

Inactive Publication Date: 2018-01-26
ZHENJIANG ZEFENGLIN BUILDING MATERIALS CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a kind of green environment-friendly type fireproof paint preparation method, solve the existing fireproof paint paint poor adsorption, after long-term use or by the erosion of water vapor in the air, easy to crack and fall off phenomenon, need It consumes a lot of manpower and material resources to maintain, the cost is high, and it cannot meet the needs of users

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1: a kind of green environmental protection type fireproof paint preparation method, its preparation method is as follows:

[0018] (1) Weigh the following components by weight: 30 parts of ammonium polyphosphate, 15 parts of tributyl phosphate, 3 parts of shell powder, 4 parts of kaolin, 1 part of flame retardant, 3 parts of thickener, and 2 parts of defoamer share;

[0019] (2) Put polydimethylsiloxane and silicone into a reaction kettle at a temperature of 25°C and stir evenly for 5 minutes to obtain a defoamer;

[0020] (3) Put ammonium polyorthophosphate and pentaerythritol into a reaction kettle at a temperature of 25°C and stir evenly for 10 minutes to obtain a flame retardant;

[0021] (4) Put xanthan gum and hydroxycellulose into a reaction kettle at a temperature of 35°C and stir evenly for 5 minutes to obtain a thickener;

[0022] (5) Put ammonium polyphosphate and tributyl phosphate into the reaction kettle, stir for 5 minutes, and the temperatu...

Embodiment 2

[0024] Embodiment 2: a kind of green environmental protection type fireproof coating preparation method, its preparation method is as follows:

[0025] (1) Weigh the following components by weight, 40 parts of ammonium polyphosphate, 20 parts of tributyl phosphate, 6 parts of shell powder, 8 parts of kaolin, 2 parts of flame retardant, 4 parts of thickener, defoamer 3 copies;

[0026] (2) Put polydimethylsiloxane and silicone into a reaction kettle at a temperature of 30°C and stir evenly for 8 minutes to obtain a defoamer;

[0027] (3) Put ammonium polyorthophosphate and pentaerythritol into a reaction kettle at a temperature of 30°C and stir evenly for 15 minutes to obtain a flame retardant;

[0028] (4) Put xanthan gum and hydroxycellulose into a reaction kettle at a temperature of 30°C and stir evenly for 10 minutes to obtain a thickener;

[0029] (5) Put ammonium polyphosphate and tributyl phosphate into the reaction kettle, stir for 10 minutes, and the temperature is 3...

Embodiment 3

[0031] Embodiment 3: a kind of green environmental protection type fireproof coating preparation method, its preparation method is as follows:

[0032] (1) Weigh the following components by weight, 50 parts of ammonium polyphosphate, 25 parts of tributyl phosphate, 9 parts of shell powder, 12 parts of kaolin, 3 parts of flame retardant, 5 parts of thickener, defoamer 4 parts;

[0033] (2) Put polydimethylsiloxane and silicone into a reaction kettle at a temperature of 35°C and stir evenly for 10 minutes to obtain a defoamer;

[0034] (3) Put ammonium polyorthophosphate and pentaerythritol into a reaction kettle at a temperature of 35°C and stir evenly for 20 minutes to obtain a flame retardant;

[0035] (4) Put xanthan gum and hydroxycellulose into a reaction kettle at a temperature of 45°C and stir evenly for 15 minutes to obtain a thickener;

[0036] (5) Put ammonium polyphosphate and tributyl phosphate into the reaction kettle, stir for 15 minutes, and the temperature is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method for a green environment-friendly fireproof coating. The green environment-friendly fireproof coating contains the following components in parts by weight: 30-50 parts of ammonium polyphosphate, 15-25 parts of tributyl phosphate, 3-9 parts of shell powder, 4-12 parts of kaolin, 1-3 parts of fire retardant, 3-5 parts of thickening agent and 2-4 parts of de-foaming agent. The green environment-friendly fireproof coating has the advantages of simple component, convenience in configuration, no pollution, excellent environment-friendly effect, low cost, excellent absorbing effect, difficulty in erosion by the water vapor in air, capability of saving a large amount of manpower and material resources for maintaining and capability of meeting the requirement of the manufacturer.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a preparation method of a green and environment-friendly fireproof coating. Background technique [0002] Paint, traditionally known as paint in China. The so-called paint is coated on the surface of the object to be protected or decorated, and can form a continuous film firmly attached to the object to be coated, usually based on resin, oil, or emulsion, with or without adding pigments, fillers, adding The corresponding additives are viscous liquids prepared with organic solvents or water. However, the existing fire retardant coatings have poor adsorption properties. After long-term use or erosion by water vapor in the air, they are prone to cracking and falling off. It requires a lot of manpower and material resources to maintain, and the cost is high, which cannot meet the needs of use. the needs of the reader. Contents of the invention [0003] The purpose of the presen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/18C09D7/44C09D7/65C09D1/00
Inventor 吴江陈秀兰
Owner ZHENJIANG ZEFENGLIN BUILDING MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com