Chitosan tetramethylene phosphonium sulphate flame retardant, and preparation method and application thereof

A technology of chitosan tetramethylene sulfuric acid and tetrahydroxymethyl phosphorus sulfate is applied in the field of halogen-free flame retardants, which can solve the problems of poor compatibility, poor degradability, and small molecular weight of flame retardants, and achieves antibacterial properties. performance, good water resistance persistence, good interfacial compatibility

Active Publication Date: 2018-01-12
JILIN INST OF CHEM TECH
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Tetrahydroxymethyl phosphorus sulfate can be used as a permanent flame retardant for polyester-cotton fabrics, and can be used to prepare flame retardants with amines such as urea, thiourea, and melamine, but these flame retardants have small molecular weights, poor compatibility, and Poor degradability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chitosan tetramethylene phosphonium sulphate flame retardant, and preparation method and application thereof
  • Chitosan tetramethylene phosphonium sulphate flame retardant, and preparation method and application thereof
  • Chitosan tetramethylene phosphonium sulphate flame retardant, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] The invention provides a kind of preparation method of chitosan tetramethylene phosphine sulfate flame retardant, comprising following preparation steps:

[0025] Carry out electrostatic adsorption of tetrakis hydroxymethyl phosphorus sulfate and chitosan in water, obtain tetrakis hydroxymethyl phosphorus sulfate / chitosan complex;

[0026] Dehydrating and covalently grafting the tetrakis phosphine hydroxymethyl sulfate / chitosan complex to obtain the chitosan tetramethylene phosphine sulfate flame retardant.

[0027] In the invention, tetrakis hydroxymethyl phosphorus sulfate and chitosan are electrostatically adsorbed in water to obtain tetrakis hydroxymethyl phosphorus sulfate / chitosan complex. In the present invention, the mass ratio of tetrakis hydroxymethyl phosphorus sulfate to chitosan is preferably 1:1 to 5:1, more preferably 2:1 to 4:1; the mass ratio of chitosan to water is The ratio is preferably 1:0.5 to 1:1, more preferably 1:1. In the present invention, t...

Embodiment 1

[0039]At room temperature, weigh 10 g of chitosan, and weigh tetrakis hydroxymethyl sulfate according to the mass ratio of tetrakis hydroxymethyl phosphorus sulfate to chitosan is 5:1, and the mass ratio of water to chitosan is 1:1. Phosphorus, chitosan (viscosity-average molecular weight is 150,000) and water are added to the reaction kettle, stirred until the chitosan is completely dissolved, heated to 90°C, kept stirring for 2 hours, unloaded, and then left to react in an oven. Reaction conditions: 150°C, keep warm for 2h. After that, the temperature was lowered to 80° C., and dried for 12 hours to obtain 40.61 g of chitosan tetramethylene phosphine sulfate solid powder.

Embodiment 2

[0041] At room temperature, weigh 10 g of chitosan, and weigh tetrakis hydroxymethyl sulfate according to the ratio of tetrakis hydroxymethyl phosphorus sulfate to chitosan mass ratio of 4:1 and water to chitosan mass ratio of 1:1. Phosphorus, chitosan (viscosity-average molecular weight is 30,000) and water are added to the reaction kettle, stirred until the chitosan is completely dissolved, heated to 80°C, kept stirring for 3 hours, unloaded, and then left to react in an oven. 140°C, keep warm for 4h. Afterwards, the temperature was lowered to 60° C., and dried for 12 hours to obtain 34.31 g of chitosan tetramethylene phosphine sulfate solid powder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method for a chitosan tetramethylene phosphonium sulphate flame retardant. The preparation method comprises the following steps: performing electrostatic adsorption on tetrakis hydroxymethyl phosphonium sulphate and chitosan in water to obtain a tetrakis hydroxymethyl phosphonium sulphate / chitosan compound; performing dehydration covalent graft reaction on thetetrakis hydroxymethyl phosphonium sulphate / chitosan compound to obtain the chitosan tetramethylene phosphonium sulphate flame retardant. The chitosan tetramethylene phosphonium sulphate flame retardant prepared by the method provided by the invention does not contain halogen, has an antibacterial effect, and is non-toxic, degradable, green and environmentally friendly; the flame retardant is highin molecular weight, keeps linearity, does not have volatility, and has water washing resistance, migration resistance, good compatibility, high stability and good flame retarding effect.

Description

technical field [0001] The invention relates to the technical field of halogen-free flame retardants, in particular to a chitosan tetramethylene phosphine sulfate flame retardant and a preparation method and application thereof. Background technique [0002] Polyacrylonitrile is a flammable polymer material, and it emits toxic cyanide when burned. The flame-retardant polyacrylonitrile materials that have been industrialized in the world are mainly modified by copolymerization of vinyl chloride monomer to improve the flame-retardant performance. However, the halogen flame retardants generate a large amount of smoke during the flame-retardant process and produce a large amount of harmful gases. Environmentally friendly products. [0003] Intumescent flame retardants are usually monomolecular or molecular composite flame retardants based on phosphorus, nitrogen, and carbon elements, of which carbon is the source of carbonization; phosphorus is the source of acid, which acts as...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L33/20C08L5/08C08B37/08
Inventor 刘群丁斌郝凤岭关昶李祥王海东孙晓竹耿伟涛宋传捷宋钰
Owner JILIN INST OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com