High-rupture-strength baking-free brick and production method thereof

A technology of flexural strength and unburned bricks, applied in the field of unburned bricks, can solve the problems of low flexural strength, easy to break, affecting the use efficiency of unburned bricks, etc.

Inactive Publication Date: 2017-12-01
无为县严桥双龙建材厂(普通合伙)
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional unburned brick has low flexural strength, and it is easy to break during transportation and unloading, which affects the use efficiency of unburned bricks. Therefore, it is urgent to design an unburned brick with excellent flexural strength to solve the problem of existing technology. problem in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A non-burning brick with excellent flexural strength proposed by the present invention, its raw materials include by weight: 40 parts of ordinary silicon 42.5 cement, 70 parts of crushed stone, 25 parts of medium sand, 10 parts of nano-calcium carbonate, and 5 parts of mineral powder , 5 parts of nano-silica, 3.5 parts of nano-alumina, 4.5 parts of fly ash, 4 parts of talcum powder, 2.5 parts of ferric chloride, 4.5 parts of magnesium chloride, 3 parts of magnesium oxide, 4 parts of modified carbon fiber, 2.5 parts of asbestos fiber , 3.5 parts of plant straw, 5.5 parts of sepiolite, 5 parts of polystyrene emulsion, 3.5 parts of polyvinyl acetate emulsion, 4.5 parts of styrene-acrylic emulsion, 4 parts of styrene-butadiene emulsion, 4 parts of water reducing agent, 3.5 parts of accelerator , 2 parts of thickener, 3.5 parts of polyvinyl alcohol, 2.5 parts of dispersant, 4.5 parts of diffusing agent, 25 parts of water, 6 parts of silane coupling agent KH-570, 5 parts of mo...

Embodiment 2

[0033] A burn-free brick with excellent flexural strength proposed by the present invention, its raw materials include by weight: 30 parts of ordinary silicon 42.5 cement, 80 parts of gravel, 20 parts of medium sand, 15 parts of nano-calcium carbonate, and 4 parts of mineral powder , 6 parts of nano-silica, 2 parts of nano-alumina, 6 parts of fly ash, 2 parts of talcum powder, 4 parts of ferric chloride, 3 parts of magnesium chloride, 5 parts of magnesium oxide, 2 parts of modified carbon fiber, 5 parts of asbestos fiber , 2 parts of plant straw, 8 parts of sepiolite, 4 parts of polystyrene emulsion, 5 parts of polyvinyl acetate emulsion, 3 parts of styrene-acrylic emulsion, 6 parts of styrene-butadiene emulsion, 3 parts of water reducing agent, 5 parts of accelerator , 1 part of thickener, 5 parts of polyvinyl alcohol, 1 part of dispersant, 6 parts of diffusing agent, 20 parts of water, 8 parts of silane coupling agent KH-570, 4 parts of modified admixture.

[0034] The modif...

Embodiment 3

[0044] A burn-free brick with excellent flexural strength proposed by the present invention, its raw materials include by weight: 50 parts of ordinary silicon 42.5 cement, 60 parts of crushed stone, 30 parts of medium sand, 5 parts of nano-calcium carbonate, and 6 parts of mineral powder , 4 parts of nano-silica, 5 parts of nano-alumina, 3 parts of fly ash, 6 parts of talcum powder, 1 part of ferric chloride, 6 parts of magnesium chloride, 1 part of magnesium oxide, 6 parts of modified carbon fiber, 1 part of asbestos fiber , 5 parts of plant straw, 3 parts of sepiolite, 6 parts of polystyrene emulsion, 2 parts of polyvinyl acetate emulsion, 6 parts of styrene-acrylic emulsion, 2 parts of styrene-butadiene emulsion, 5 parts of water reducing agent, 2 parts of accelerator , 3 parts of thickener, 2 parts of polyvinyl alcohol, 4 parts of dispersant, 3 parts of diffusing agent, 30 parts of water, 4 parts of silane coupling agent KH-570, 6 parts of modified admixture.

[0045] The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-rupture-strength baking-free brick. The high-rupture-strength baking-free brick is prepared from the raw materials including ordinary Portland cement 42.5, gravels, medium sand, nano calcium carbonate, mineral powder, nano silicon dioxide, nano aluminum oxide, coal cash, talcum powder, ferric chloride, magnesium chloride, magnesium oxide, modified carbon fiber, asbestos fiber, plant straw, sepiolite, polystyrene emulsion, polyvinyl acetate emulsion, polyphenyl emulsion, bentyl benzene emulsion, water reducer, accelerator, thickener, polyvinyl alcohol, dispersant, diffusant, water, silane coupling agent KH-570 and modified additives. The invention also discloses a preparation method of the high-rupture-strength baking-free brick. The prepared high-rupture-strength baking-free brick is excellent in rupture strength.

Description

technical field [0001] The invention relates to the technical field of unburned bricks, in particular to an unburned brick with excellent flexural strength and a preparation method thereof. Background technique [0002] Unburned brick is a new type of wall material manufactured by using fly ash, coal slag, coal gangue, tailings slag, chemical slag or natural sand, sea mud, etc. as the main raw materials without high-temperature calcination. The traditional unburned brick has low flexural strength, and it is easy to break during transportation and unloading, which affects the use efficiency of unburned bricks. Therefore, it is urgent to design an unburned brick with excellent flexural strength to solve the problem of existing technology. in the question. Contents of the invention [0003] In order to solve the technical problems existing in the background technology, the present invention proposes an unburned brick with excellent flexural strength and a preparation method ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/32
CPCC04B28/32C04B7/02C04B14/02C04B14/28C04B18/12C04B14/06C04B14/303C04B18/08C04B14/042C04B22/12C04B14/386C04B14/40C04B18/24C04B24/2676C04B24/2623C04B2103/302C04B2103/12C04B2103/44C04B2103/408C04B2103/0068C04B24/42C04B24/18C04B24/122C04B24/34C04B24/383C04B22/064C04B2103/40C04B2103/465C04B2103/50
Inventor 缪碧波
Owner 无为县严桥双龙建材厂(普通合伙)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products