Electric aluminium

A technology of anodizing aluminum and titanium dioxide, applied in the field of anodizing aluminum, can solve problems such as insufficient performance and insufficient tolerance

Active Publication Date: 2017-10-17
ANHUI JIYOU NEW MATERIAL CO LTD
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Based on this, it is necessary to provide a kind of anodized aluminum for the problem that the performance of the traditional anodized aluminum is not good enough after hot stamping, and the tolerance to the environment is not enough.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electric aluminium

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The present invention also provides a preparation method of electrochemical aluminum, comprising the following steps:

[0036] S100, providing the base film;

[0037] S200, coating the release layer on the base film, the coating speed is 80m / min, the coating temperature is 100°C, and the dry coating amount is 0.2~1.0g / m 2 ;

[0038] S300, coating the color layer on the release layer, the coating speed is 100m / min, the coating temperature is 120°C, and the dry coating amount is 0.6~1.2g / m 2 ;

[0039] S400, vacuum aluminum plating on the base film coated with release layer and color layer, the aluminum plating speed is 80m / min, and the dry coating amount is 0.2~0.5g / m 2 ;as well as

[0040]S500, coating the product obtained by vacuum aluminum plating with an adhesive layer, the coating speed is 100m / min, the coating temperature is 110°C, and the dry coating amount is 0.6-1.2g / m 2 .

Embodiment 1

[0042] Components:

[0043] Base film: select the gram weight as 18g / m 2 , PET (polyethylene terephthalate) with a thickness of 12u is the base film layer.

[0044] Water-based release layer: 2.5 parts of ethylene vinyl acetate copolymer modified polypropylene wax, 3 parts of modified oxidized polyethylene wax with silicon hydroxyl group, 0.1 part of silicone defoamer, 25 parts of ethanol, 25 parts of deionized water;

[0045] Water-based color layer: 25 parts of water-based acrylic emulsion, 8 parts of water-based magenta, 10 parts of modified cellulose, 5 parts of alumina-coated titanium dioxide (particle size 60nm), 0.2 parts of silicone defoamer, 35 parts of deionized water;

[0046] Water-based adhesive layer: 25 parts of water-based acrylic resin, 5 parts of water-based terpene resin, 5 parts of fumed silica (particle size 70nm), 30 parts of deionized water, and 0.3 parts of silicone defoamer.

[0047] preparation:

[0048] Add 25 parts of ethanol and 25 parts of deio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Gram weightaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to electric aluminium comprising a base film layer, a release layer, a color layer, an aluminized layer and an adhesive layer which are sequentially arranged in a laminating mode. The release layer comprises, by weight, 2-5 parts of liquid wax, 1-3 parts of plate release wax, 20-30 parts of ethyl alcohol and 20-30 parts of deionized water, wherein the plate release wax is modified oxidized polyethylene wax with silicon hydroxyl. The modified oxidized polyethylene wax is added in the release layer to serve as the plate release wax, the modified oxidized polyethylene wax has the silicon hydroxyl (Si-OH), the friction resisting property of the release layer can be improved, and thus the release layer has smooth and full hand feelings and accordingly has the good stripping property; and meanwhile the modified oxidized polyethylene wax can be matched with the liquid wax mutually, so that the release layer has good acid resistant, alkali resistant and hard-water resistant properties, and the uniformity of smearing of the color layer on the release layer can be further improved. By adjusting the adding amount of the modified oxidized polyethylene wax, the electric aluminium can have different degrees of the friction resisting property and the acid resistant, alkali resistant and hard-water resistant properties, and accordingly the application requirement can be better met.

Description

technical field [0001] The invention relates to the technical field of tipping paper, in particular to anodized aluminum. Background technique [0002] Anodized aluminum hot stamping patterns are more and more widely used in packaging and printing because of their special metallic luster and eye-catching effects. In recent years, they have been gradually developed and utilized by printing manufacturers. The current trend of high-end tipping paper production, while improving the aesthetics and grades of products, it also adds a lot of value to printing manufacturers. [0003] Anodized aluminum is composed of polyester film (PET) and multi-layer chemical coatings coated on its surface. Different coatings play different roles in anodized aluminum hot stamping. The release layer is mainly to ensure that the anodized aluminum can be transferred from the substrate during the hot stamping process, while the color layer is mainly for decoration, and the aluminum coating is mainly t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B41M5/42B41M5/44C09J133/00C09J11/04C09J11/08
CPCB41M5/426B41M5/44C09J11/04C09J11/08C09J133/00C08L45/00C08K3/36
Inventor 俆善水郭飞杨江涛杨立新曹萼余永恒杨二果郑丰魏怀玉赵荣艳王超王云龙姜亚洲余四军
Owner ANHUI JIYOU NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com