Asphalt waterproofing paint for roads and bridges and preparation method thereof

A kind of asphalt waterproof coating, road and bridge technology, applied in the direction of asphalt coating, coating, conjugated diene coating, etc., can solve the problems of poor storage stability, poor low temperature weather resistance, long drying time, etc., and achieve high elongation at break , high tensile strength, and the effect of simplifying the construction process

Active Publication Date: 2017-09-29
XUZHOU WONIUSHAN NEW WATERPROOF MATERIALS
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The water-emulsified asphalt coating products currently produced in the market generally have low bonding strength (≤1.2MPa), difficulty in one-step film formation (one-step construction thickness ≤0.5mm), slow drying (2-4h), and poor storage stability (5d) Storage stability is 2% to 5%), poor low temperature weather resistance (low temperature flexibility is only -25°C), and other defects, which lead to problems such as easy precipitation during storage, construction needs 3 to 5 times, and long drying time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Asphalt waterproofing paint for roads and bridges and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] According to the second aspect of the present invention, the present invention provides a kind of preparation method of above-mentioned asphalt waterproof coating for road and bridge, and this preparation method comprises:

[0032] 1) melting the asphalt to obtain molten asphalt;

[0033] 2) uniformly mixing the cationic emulsifier with part of the water, and then uniformly mixing with the polymer latex to obtain a soap solution;

[0034] 3) processing the soap liquid and the molten asphalt through a colloid mill to obtain a modified emulsion asphalt;

[0035] 4) uniformly mixing the ultrafine wollastonite powder, thickener and remaining water to obtain a mixed slurry;

[0036] 5) uniformly mixing the modified emulsion asphalt with the mixed slurry to obtain the asphalt waterproof coating for road and bridge.

[0037] Preferably, in step 3), the soap liquid and the molten asphalt are passed into the colloid mill for treatment according to the volume ratio of 5:4 to 5:...

specific Embodiment approach

[0038] According to a kind of preferred embodiment, the preparation method of bituminous waterproof coating for road and bridge of the present invention comprises:

[0039] 1) Raise the temperature of asphalt to 130-140°C to obtain molten asphalt;

[0040] 2) Warm up water accounting for 50-86% by weight of the total amount to 55-60°C, add cationic emulsifier, stir for 0.5-2 hours, then add polymer latex, and stir at high speed for 0.5-2 hours to prepare soap liquid;

[0041] 3) The soap liquid and the molten asphalt are processed through a colloid mill according to the volume ratio of 5:4 to 5:7 to obtain a modified emulsified asphalt;

[0042] 4) Mix the ultrafine wollastonite powder, thickener and remaining water, and stir at high speed for 2-3 hours to obtain a mixed slurry;

[0043] 5) Mix the mixed slurry with the modified emulsified asphalt, and stir at a medium speed for 1-2 hours to obtain the asphalt waterproof coating for road and bridge.

[0044] As mentioned abo...

Embodiment 1

[0053] This implementation is used to illustrate the asphalt waterproof coating for road and bridge of the present invention and its preparation method.

[0054] Raw material composition: 30 parts of asphalt, 0.2 parts of cationic emulsifier, 4 parts of polymer latex, 1 part of thickener, 2 parts of superfine wollastonite powder, and 32 parts of water.

[0055] The preparation process is as follows:

[0056] 1) Add asphalt in the reaction vessel 1, and heat up to 135°C;

[0057] 2) Add 20 parts of water into the reaction vessel 2, heat up to 55°C; add cationic emulsifier in the water, stir for 1 hour until dissolved, then add polymer latex, stir at high speed for 1 hour to form soap liquid;

[0058] 3) The soap liquid in the reaction vessel 2 and the molten asphalt in the reaction vessel 1 are sheared and emulsified through a colloid mill according to the volume ratio of 5:4 to obtain a modified emulsified asphalt, cooled to room temperature, and transferred to The reaction ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of building waterproof materials, and provides asphalt waterproofing paint for roads and bridges and a preparation method thereof. The asphalt waterproofing paint comprises the following raw materials by weight: 28-36 parts of asphalt, 0.2-0.5 part of cationic emulsifier, 4-5 parts of polymer latex, 1-3 parts of a thickening agent, 2-4 parts of superfine wollastonite powder and 20-35 parts of water; and the thickening agent is an association type thickener prepared by polymerization of hydroxyethyl cellulose and polyoxyethylene. The asphalt waterproofing paint has the characteristics of high bonding strength, thick coating construction, fast drying, good storage stability, low temperature and excellent weather resistance.

Description

technical field [0001] The invention belongs to the field of building waterproof materials, relates to a waterproof material used for the surface of roads and bridges with cement concrete as the surface layer, and specifically provides an asphalt waterproof coating for roads and bridges and a preparation method thereof. Background technique [0002] Water-emulsion asphalt coating is an environmentally friendly asphalt-based waterproof coating commonly used in the construction waterproofing industry. It is widely used in waterproofing parts such as roofs, basements, tunnels, road and bridge culverts, garage roofs, and engineering foundations. Its advantages are: cold construction without hot melting, simple and convenient construction process, film formation process is completed by water volatilization and emulsion particle fusion, construction at room temperature, energy saving, no organic solvent escape during construction, less environmental pollution, and engineering cost ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D153/02C09D109/08C09D7/00C09D7/12
CPCC08L2205/03C08L2205/035C09D195/00C08L53/02C08L9/08C08L87/00C08K3/34
Inventor 李善法刘金景吴士玮陈晓文
Owner XUZHOU WONIUSHAN NEW WATERPROOF MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com