Waterproof material for toilet and preparation method of waterproof material

A waterproof material and toilet technology, applied in the field of toilet waterproof material and its preparation, can solve the problems of poor ductility of waterproof mortar, poor joint around the pipeline, leakage around the pipeline, etc., and achieve good chemical stability, specific heat Small thermal conductivity, prevent moisture penetration

Inactive Publication Date: 2017-09-29
HEFEI FENGTENG ENERGY SAVING TECH CO LTD
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the waterproof material commonly used in toilets is waterproof mortar, which mainly has the following defects: first, the waterproof mortar is not well combined with the surrounding pipes after solidification, which is easy to cause leakage around the pipe; second, the waterproof mortar has poor ductility after solidification, and with Minor subsidence and dislocation of the building, the waterproof layer formed by the waterproof mortar will be torn, resulting in water leakage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A waterproof material for toilets, comprising the following raw materials: 70 parts of modified starch, 55 parts of inorganic powder filler, 45 parts of cis-isoamyl rubber, 35 parts of aluminum stearate, 30 parts of fly ash, 25 parts of nanoparticles, 15 parts of organic fiber, 15 parts of simethicone, 10 parts of additives, 5 parts of pigment and 120 parts of water;

[0032] The modified starch comprises the following raw materials in parts: 35 parts of starch, 10 parts of acetic acid solution, 2 parts of gelatin, 2 parts of chitosan, 2 parts of salicylic acid, 2 parts of polyethylene glycol, 1 part of calcium gluconate and 1 part of calcium lignosulfonate;

[0033] The auxiliary agent includes the following raw materials: 2 parts of water reducer, 2 parts of retarder, 2 parts of crystal growth agent, 1 part of film-forming aid, 1 part of plasticizer, 0.2 parts of toughening agent and bactericide 0.2 parts.

[0034] Wherein, the starch is mung bean starch.

[0035] ...

Embodiment 2

[0049]A waterproof material for toilets, comprising the following raw materials: 80 parts of modified starch, 65 parts of inorganic powder filler, 50 parts of cis-isoamyl rubber, 40 parts of aluminum stearate, 35 parts of fly ash, 30 parts of nanoparticles, 25 parts of organic fibers, 20 parts of simethicone, 15 parts of additives, 10 parts of pigments and 150 parts of water;

[0050] The modified starch comprises the following raw materials: 40 parts of starch, 20 parts of acetic acid solution, 8 parts of gelatin, 8 parts of chitosan, 6 parts of salicylic acid, 4 parts of polyethylene glycol, 3 parts of calcium gluconate and 3 parts of calcium lignosulfonate;

[0051] The auxiliary agent includes the following raw materials: 4 parts of water reducer, 4 parts of retarder, 3 parts of crystal growth agent, 2 parts of film-forming aid, 2 parts of plasticizer, 1.2 parts of toughening agent and bactericide 0.8 servings.

[0052] Wherein, the starch is tapioca starch.

[0053] Wh...

Embodiment 3

[0067] A waterproof material for toilets, comprising the following raw materials: 75 parts of modified starch, 60 parts of inorganic powder filler, 47.5 parts of cis-isoamyl rubber, 37.5 parts of aluminum stearate, 32.5 parts of fly ash, 27.5 parts of nanoparticles, 20 parts of organic fibers, 17.5 parts of simethicone, 12.5 parts of additives, 7.5 parts of pigments and 135 parts of water;

[0068] The modified starch comprises the following raw materials in parts: 37.5 parts of starch, 15 parts of acetic acid solution, 5 parts of gelatin, 5 parts of chitosan, 4 parts of salicylic acid, 3 parts of polyethylene glycol, 2 parts of calcium gluconate and 2 parts of calcium lignosulfonate;

[0069] The auxiliary agent includes the following raw materials: 3 parts of water reducer, 3 parts of retarder, 2.5 parts of crystal growth agent, 1.5 parts of film-forming aid, 1.5 parts of plasticizer, 0.7 part of toughening agent and bactericide 0.5 servings.

[0070] Wherein, the starch i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waterproof material for a toilet and a preparation method of the waterproof material and relates to the technical field of waterproof materials. The waterproof material comprises the following raw materials in parts: 70-80 parts of modified starch, 55-65 parts of inorganic powder fillers, 45-50 parts of cis-1,4-polyisoprene rubber, 35-40 parts of aluminum stearate, 30-35 parts of fly ash, 25-30 parts of nano particles, 15-25 parts of organic fibers, 15-20 parts of dimethyl silicone, 10-15 parts of aids, 5-10 parts of pigments and 120-150 parts of water. The waterproof material disclosed by the invention has excellent waterproof, anti-permeability and antibacterial and anti-mold properties, the raw materials are environmental-friendly and high in affinity, water leakage in the toilet can be effectively prevented, and the waterproof material is difficult to age.

Description

technical field [0001] The invention relates to the technical field of waterproof materials, in particular to a waterproof material for toilets and a preparation method thereof. Background technique [0002] At present, the waterproof material commonly used in toilets is waterproof mortar, which mainly has the following defects: first, the waterproof mortar is not well bonded to the periphery of the pipeline after solidification, which may easily cause leakage around the pipeline; second, the ductility of the waterproof mortar is not good after solidification. Small subsidence and dislocation of the building, the waterproof layer formed by the waterproof mortar will be torn, resulting in water leakage. Contents of the invention [0003] The purpose of the present invention is to provide a waterproof material for toilets and its preparation method, which has good water resistance, impermeability, antibacterial and antifungal properties, and the raw materials are environment...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/28C04B20/00C04B22/10C04B24/04C04B111/27
CPCC04B26/285C04B20/008C04B22/10C04B24/04C04B2111/27C04B14/28C04B14/106C04B14/042C04B14/20C04B14/40C04B24/24C04B24/085C04B18/08C04B14/062C04B16/02C04B24/42C04B24/06C04B24/02C04B24/045C04B24/32C04B24/12C04B14/305C04B22/002C04B2103/302C04B24/023C04B14/308C04B14/307
Inventor 吴旭
Owner HEFEI FENGTENG ENERGY SAVING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com