Flux-cored wire used for low-alloy chrome molybdenum heat-resistant steel and application thereof

A heat-resistant steel, low-alloy technology, used in welding media, welding equipment, metal processing equipment, etc., can solve the problem of poor low-temperature impact toughness, poor welding process performance of basic heat-resistant steel flux-cored wire, and inability to perform all-position welding and other problems, to achieve the effect of excellent impact performance and stable impact value

Active Publication Date: 2017-09-05
武汉铁锚焊接材料股份有限公司
View PDF15 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the problems of poor low-temperature impact toughness of the existing acidic heat-resistant steel flux-cored welding wire and poor welding process performance of the basic heat-resistant steel flux-cored welding wire, which prevents all-position welding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flux-cored wire used for low-alloy chrome molybdenum heat-resistant steel and application thereof
  • Flux-cored wire used for low-alloy chrome molybdenum heat-resistant steel and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0036] Embodiment The low-carbon steel sheath of low-alloy chromium-molybdenum heat-resistant steel flux-cored welding wire adopts cold-rolled carbon steel thin steel strip, and the thickness of steel strip is 0.8~0.9mm, and the width is 14mm; 13-16%, that is, the filling rate is 13-16%; the drug core powder is pre-baked, and then the steel strip is formed, powder filled, jointed, reduced and a series of drawing and surface treatment to make a finished drug co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Widthaaaaaaaaaa
Login to View More

Abstract

The invention provides a flux-cored wire used for low-alloy chrome molybdenum heat-resistant steel. The flux-cored wire comprises a low-carbon steel sheath and a flux core which is stuffed in the low-carbon steel sheath. The flux core comprises the following components in percentage by mass: 30-35% of natural rutile, 2-5% of magnesium oxide, 1.5-3% of barium carbonate, 2-3% of elpasolite, 2-5% of potassium titanate, 15-20% of a silicomanganese alloy, 8-10% of chromium, 3.5-5% of ferromolybdenum, 1-2% of ferro-aluminum, 0.5-2.5% of roasted aluminum oxide, 0.5-1% of nickel powder, 0.5-1.5% of magnetite and the balance of iron powder and inevitable impurities. The flux-cored wire has the advantages that deposited metal composition completely accords with stipulation of related national standards, and the all-position welding requirement of the 1-1.25%Cr-0.5%Mo heat-resistant steel can be met; meanwhile, the mechanical performance indexes of deposited metal completely accord with stipulation of related national standards; impact property of the deposited metal is excellent, and specially, low-temperature impact toughness (minus 30 DEG C) is stabilized at more than 50J; and an impact value is stable.

Description

technical field [0001] The invention belongs to the technical field of welding materials, and in particular relates to a low-alloy chromium-molybdenum heat-resistant steel flux-cored welding wire and its application. Background technique [0002] Chromium-molybdenum heat-resistant steel is widely used in cutting-edge industries such as thermal power generation, petrochemical industry, aviation, and atomic energy. The equipment is gradually developing in the direction of large-scale and high-parameters, which requires heat-resistant steel materials and supporting welding materials to have more excellent mechanical properties. At present, the welding methods of chrome-molybdenum heat-resistant steel include manual electrode arc welding, argon tungsten arc welding, gas metal shielded welding and submerged arc welding, among which, the gas metal shielded welding method of flux cored wire has good process performance and good deposition It has many advantages such as high efficie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K35/02B23K35/22
CPCB23K35/02B23K35/0266B23K35/22
Inventor 宋昌宝徐文福王玲艳王哲
Owner 武汉铁锚焊接材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com