Environment-friendly flame retardant fame-retardant nylon 6 and preparation method thereof

An intumescent flame retardant and environmentally friendly technology, which is applied in the field of polymer material modification, can solve the problems of unsustainable flame retardant performance, unenvironmental protection, and large damage to the mechanical properties of the matrix, achieving good flame retardant performance and reducing water absorption. rate, good development potential

Inactive Publication Date: 2017-09-01
陈霞
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the defects in the prior art that the flame retardant performance is not durable, the mechanical properties of the matrix are greatly damaged, and it is not environmentally friendly, the purpose of the present invention is to provide an environmentally friendly phosphorus-nitrogen one-component intumescent flame retardant modified nylon 6 and its preparation method, by introducing a one-component phosphorus-nitrogen intumescent flame retardant with good flame retardancy, environmental protection and water-soluble resistance and an inorganic synergistic flame retardant to jointly flame-retardant nylon 6 to obtain mechanical properties and flame-retardant properties Excellent, safe and environmentally friendly high-performance nylon 6 modified material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] An environmentally friendly phosphorus-nitrogen one-component intumescent flame retardant modified nylon 6, which consists of the following components by weight: 50-90 parts of nylon 6, phosphorus-nitrogen one-component intumescent flame retardant 5- 25 parts, 2-10 parts of inorganic synergistic flame retardant, 2-10 parts of compatibilizer, 1-5 parts of antioxidant.

[0021] Wherein, the one-component phosphorus-nitrogen intumescent flame retardant is selected from one or more combinations of pentaerythritol spirocyclic phosphoryl p-toluidine, polyethylenediamine pentaerythritol bisphosphate and neopentyl glycol cyclophosphoryl melamine; The inorganic synergistic flame retardant is selected from one or more combinations of magnesium hydroxide, sodium antimonate and zinc borate; the compatibilizer is selected from maleic anhydride grafted polypropylene (PP-g-MAH), maleic anhydride One of acid anhydride grafted polyethylene (PE-g-MAH), maleic anhydride grafted ethylene-o...

Embodiment 2

[0025] An environmentally friendly phosphorus-nitrogen one-component intumescent flame retardant modified nylon 6, which consists of the following components by weight: 50 parts of nylon 6, 25 parts of phosphorus-nitrogen one-component intumescent flame retardant, inorganic 10 parts of synergistic flame retardant, 10 parts of compatibilizer, 5 parts of antioxidant.

[0026] Among them, the one-component phosphorus-nitrogen intumescent flame retardant is pentaerythritol spirophosphoryl p-toluidine; the inorganic synergistic flame retardant is magnesium hydroxide; the compatibilizer is maleic anhydride grafted polypropylene (PP-g- MAH); Antioxidant is phenylene diisodecyl phosphite.

[0027] A preparation method of environmentally friendly phosphorus-nitrogen single-component intumescent flame retardant modified nylon 6, comprising the following steps:

[0028] (1) Weigh various raw materials according to the proportion, dry nylon 6 in a vacuum oven at 120°C for 3 hours, and th...

Embodiment 3

[0030] An environmentally friendly phosphorus-nitrogen one-component intumescent flame retardant modified nylon 6, which consists of the following components by weight: 690 parts of nylon, 5 parts of phosphorus-nitrogen one-component intumescent flame retardant, inorganic 2 parts of effective flame retardant, 2 parts of compatibilizer, and 1 part of antioxidant.

[0031] Among them, the one-component phosphorus-nitrogen intumescent flame retardant is polyethylenediamine pentaerythritol diphosphate; the inorganic synergistic flame retardant is sodium antimonate; the compatibilizer is maleic anhydride grafted polyethylene (PE-g- MAH); Antioxidant is polyalkyl bisphenol A phosphite.

[0032] A preparation method of environmentally friendly phosphorus-nitrogen one-component intumescent flame retardant modified nylon 6, comprising the following steps: (1) Weighing various raw materials according to the proportion, drying nylon 6 in a vacuum oven at 90°C for 1 hour , then dry-treat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
limiting oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses environment-friendly phosphorus-nitrogen one-component intumescent flame retardant-modified nylon 6 which is prepared from the following components in parts by weight: 50-90 parts of nylon 6, 5-25 parts of a phosphorus-nitrogen one-component intumescent flame retardant, 2-10 parts of an inorganic synergistic flame retardant, 2-10 parts of a compatilizer and 1-5 parts of an antioxidant. The invention further discloses a preparation method of the environment-friendly phosphorus-nitrogen one-component intumescent flame retardant-modified nylon 6. A safe and environment-friendly high-performance nylon 6-modified material with good mechanical properties and a good flame-retardant property is obtained through introducing environment-friendly common flame-retardant nylon 6 with the good flame-retardant property and water solubility resistance of the phosphorus-nitrogen one-component intumescent flame retardant and the inorganic synergistic flame retardant; and the environment-friendly phosphorus-nitrogen one-component intumescent flame retardant-modified nylon 6 has good development potential and wide application prospects.

Description

technical field [0001] The invention belongs to the field of polymer material modification, and in particular relates to an environment-friendly phosphorus-nitrogen single-component intumescent flame retardant modified nylon 6 and a preparation method thereof. Background technique [0002] Compared with inorganic and metal materials, the flammability of polymer materials has seriously restricted their wider development and application. Therefore, it is of great scientific significance and application value to carry out relevant flame retardant research. Studies have confirmed that it is an effective method to improve the flame retardancy of polymer materials by adding flame retardants; therefore, the development of high-efficiency flame retardants has become a hot spot in the field of flame retardancy of polymer materials. [0003] Nylon 6 has excellent comprehensive properties and occupies an important position in the field of engineering plastics. However, while it has e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08L51/04C08K13/02C08K5/5399C08K5/521C08K3/24C08K3/22C08K3/38
CPCC08L77/02C08K2003/2224C08K2003/387C08K2201/014C08L2201/02C08L51/06C08K3/22C08K5/526C08K5/5399C08K5/521C08K3/24C08K3/38C08K5/1345C08L51/04C08K13/02C08L51/003
Inventor 陈霞
Owner 陈霞
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com