Polyarylether ether nitrile modified phenolic resin adhesive and preparation method thereof

A kind of technology of polyarylene ether ether nitrile and phenolic resin glue

Active Publication Date: 2017-08-22
SHANDONG YUSHIJU CHEM CO LTD
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the toughening modification method of phenolic resin is mainly by adding rubber, thermoplastic polymer materials, glass fibers, nano-powder, etc. to phenolic resin, but there are usually some problems in the addition of these materials, including reducing the Adhesion, poor compatibility of additive materials and phenolic resin, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The present invention also includes a preparation method of polyarylether ether nitrile modified phenolic resin adhesive, comprising the following steps:

[0033] ① In parts by weight, mix 100 parts of phenol and 40-50 parts of solid paraformaldehyde, heat to 30-50°C, stir to dissolve, add 8-12 parts of polyarylether ether nitrile, stir for 10-20 minutes, add 0.5-1.5 parts of maleic acid, heat up to 90-110°C, keep warm for 2-4 hours, cool down to 40-60°C, distill and dehydrate under reduced pressure, cool down to 15-25°C to obtain polyarylether ether nitrile modified phenolic resin ;

[0034] ② 50-60 parts of polyarylether ether nitrile modified phenolic resin obtained in step ①, 6-10 parts of polyvinylpyrrolidone, 25-35 parts of nitrile rubber, 0.1-1 part of anti-aging agent and 10-15 parts of methyl acetate Mix and stir evenly, heat up to 60-70°C for 1 hour, cool to normal temperature to obtain polyarylether ether nitrile modified phenolic resin adhesive; the polyvin...

Embodiment 1

[0041] (1) Mix 100kg of phenol and 40kg of solid paraformaldehyde, heat to 30°C, stir to dissolve, add 8kg of polyarylether ether nitrile, stir for 10 minutes, add 0.5kg of maleic acid, heat up to 90°C, and keep warm for 2 hours , lower the temperature to 40°C, distill and dehydrate under reduced pressure, and lower the temperature to 15°C to obtain polyarylether ether nitrile modified phenolic resin;

[0042] (2) 50kg of the polyarylether ether nitrile modified phenolic resin of step (1) gained, K90 polyvinylpyrrolidone 6kg, liquid nitrile rubber 25kg, antioxidant A0.1kg and methyl acetate 10kg mix, stir, be warming up to Insulate at 60°C for 1 hour, and cool to room temperature to obtain a polyarylether ether nitrile modified phenolic resin adhesive.

Embodiment 2

[0044](1) Mix 100kg of phenol and 45kg of solid paraformaldehyde, heat to 40°C, stir to dissolve, add 10kg of polyarylether ether nitrile, stir for 15 minutes, add 1.0kg of maleic acid, heat up to 100°C, and keep warm for 3 hours , cooled to 50°C, dehydrated by vacuum distillation, and cooled to 20°C to obtain polyarylether ether nitrile modified phenolic resin;

[0045] (2) 5kg part of polyarylether ether nitrile modified phenolic resin of step (1) gained, K90 polyvinylpyrrolidone 8kg, liquid nitrile rubber 30kg, antioxidant A0.5kg and methyl acetate 12kg mix, stir, heat up Heat it at 65°C for 1 hour, then cool to room temperature to obtain a polyarylether ether nitrile modified phenolic resin adhesive.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses polyarylether ether nitrile modified phenolic resin adhesive and a preparation method thereof. The polyarylether ether nitrile modified phenolic resin adhesive is technically characterized by being composed of the following substances in parts by weight: 50-60 parts of polyarylether ether nitrile modified phenolic resin, 6-10 parts of polyvinylpyrrolidone, 25-35 parts of butadiene-acrylonitrile rubber, 0.1-1 part of an anti-aging agent and 10-15 parts of methyl acetate. The polyarylether ether nitrile modified phenolic resin adhesive has the advantages that phenolic resin is modified by utilizing polyarylether ether nitrile, so that toughness and bonding performance of the phenolic resin are obviously improved; meanwhile, polyvinylpyrrolidone has good molecular affinity, so that polyarylether ether nitrile, butadiene-acrylonitrile rubber and phenolic resin form a uniform system, and toughness of a material is improved; besides, the polyvinylpyrrolidone has excellent bonding performance, so that coadhesiveness of the phenolic resin adhesive is also further improved.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to a polyarylether ether nitrile modified phenolic resin adhesive and a preparation method thereof. Background technique [0002] The production process of phenolic resin material is simple, the price is cheap, and it has a wide range of applications. It is one of the indispensable polymer materials for my country's industrial development. However, traditional phenolic resins are brittle and easily broken during use, which limits their application in the field of high-performance materials. Therefore, modifying phenolic resin materials to improve their toughness is very important to the development of high-tech fields in my country. At present, the toughening modification method of phenolic resin is mainly by adding rubber, thermoplastic polymer materials, glass fibers, nano-powder, etc. to phenolic resin, but there are usually some problems in the addition of these materials, in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J161/24C09J139/06C09J109/02C08G8/32C08G8/28
CPCC08G8/28C08G8/32C08L2201/08C08L2205/03C09J161/24C08L39/06C08L9/02
Inventor 张彬
Owner SHANDONG YUSHIJU CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap