Aluminum alloy door frame

An aluminum alloy and aluminum alloy-based technology, applied in the field of aluminum alloys, can solve the problems of surface damage, unsightly appearance, and short service life of aluminum alloy door frames, and achieve the effects of saving production costs, shortening production cycles, and reducing energy consumption.

Inactive Publication Date: 2017-08-11
合肥市旺友门窗有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because it is directly made of aluminum alloy, it is very easy to be scratched by foreign objects during use, resulting in damage to the surface of the aluminum alloy door frame, unsightly appearance and short service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] An aluminum alloy door frame, comprising an aluminum alloy base material and a functional coating coated on the surface of the aluminum alloy base material, characterized in that the aluminum alloy base material is formulated according to the following parts by weight: 5 grams of silicon, 6 grams of nickel, and 5 grams of chromium , 1 gram of copper, 0.5 gram of iron, 1 gram of manganese, 1 gram of magnesium, 1 gram of zinc, 0.5 gram of titanium, 150 ppm of calcium, and the rest is aluminum;

[0033] The functional coating includes 20 grams of butadiene rubber, 20 grams of filler, 8 grams of plasticizer, and 3 grams of coupling agent. The filler is formulated according to the following mass percentages: 30% of alumina-titanium dioxide composite material, 20% of manganese dioxide and Silicon dioxide 10%; the lubricant is silicone oil, the coupling agent is isopropyl trioleate acyloxy titanate, and the plasticizer is diethylene glycol di-m-toluate.

[0034] The above-ment...

Embodiment 2

[0053] An aluminum alloy door frame, comprising an aluminum alloy base material and a functional coating coated on the surface of the aluminum alloy base material, characterized in that the aluminum alloy base material is formulated according to the following parts by weight: 8 grams of silicon, 10 grams of nickel, and 8 grams of chromium , 2 grams of copper, 1 gram of iron, 2 grams of manganese, 2 grams of magnesium, 2 grams of zinc, 1 gram of titanium, 200 ppm of calcium, 0.2 grams of lead, 0.05 grams of cadmium, and the rest is aluminum;

[0054] The functional coating includes 50 grams of butadiene rubber, 50 grams of filler, 10 grams of plasticizer, and 10 grams of coupling agent. The filler is formulated according to the following mass percentages: 60% of alumina-titanium dioxide composite material, 40% of manganese dioxide and Silicon dioxide 40%; the lubricant is silicone oil, the coupling agent is isopropyl trioleate acyloxy titanate, and the plasticizer is diethylene ...

Embodiment 3

[0074] An aluminum alloy door frame, comprising an aluminum alloy base material and a functional coating coated on the surface of the aluminum alloy base material, characterized in that the aluminum alloy base material is formulated according to the following parts by weight: 7 grams of silicon, 8 grams of nickel, and 6 grams of chromium , 3 grams of copper, 0.8 grams of iron, 1.5 grams of manganese, 1.5 grams of magnesium, 1.5 grams of zinc, 0.8 grams of titanium, 150 ppm of calcium, 0.1 grams of lead, 0.3 grams of cadmium, and the rest is aluminum;

[0075] The functional coating includes 35 grams of butadiene rubber, 35 grams of filler, 9 grams of plasticizer, and 7 grams of coupling agent. The filler is formulated according to the following mass percentages: 45% of alumina-titanium dioxide composite material, 30% of manganese dioxide and Silicon dioxide 25%; lubricant is silicone oil, coupling agent is isopropyl trioleate acyloxy titanate, and plasticizer is diethylene glyc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an aluminum alloy door frame. The aluminum alloy door frame comprises an aluminum alloy base material and a functional coating with which the surface of the aluminum alloy base material is coated. The aluminum alloy base material is prepared from, by weight, 5-8 parts of silicon, 6-10 parts of nickel, 5-8 parts of chromium, 1-2 parts of copper, 0.5-1 part of iron, 1-2 parts of manganese, 1-2 parts of magnesium, 1-2 parts of zinc, 0.5-1 part of titanium, smaller than or equal to 200 ppm of calcium, 0-0.2 part of lead, 0-0.05 part of cadmium and the balance aluminum. The functional coating is prepared from 20-50 parts of butadiene rubber, 20-50 parts of filler, 8-10 parts of plasticize and 3-10 parts of coupling agent. The filler is prepared from, by mass, 30-60% of aluminum oxide-titanium dioxide composite, 20-40% of manganese dioxide and 10-40% of silicon dioxide. The lubricating agent is organic silicon oil, the coupling agent is isopropyl trioleate trioleate, and the plasticizer is diethylene glycol dimethyl benzoate. The aluminum alloy door frame is high in surface strength, good in corrosion resistance and scraping resistance and attractive in appearance.

Description

technical field [0001] The invention relates to the technical field of aluminum alloys, in particular to an aluminum alloy door frame. Background technique [0002] Aluminum alloy materials are widely used in various structures due to their small specific gravity, good durability and easy processing. The aluminum alloy door frame is a door frame component made of surface-treated aluminum alloy profiles through blanking, drilling, milling, tapping, manufacturing and other processing processes, and then used with connectors, sealing materials and opening and closing hardware accessories Assembled. Because it is directly made of aluminum alloy, it is very easy to be scratched by foreign objects during use, causing the surface of the aluminum alloy door frame to be damaged, the appearance is not beautiful, and the service life is short. Contents of the invention [0003] The object of the present invention is to solve the problems in the prior art and provide an aluminum all...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E06B1/52C22C21/00C22C21/02C23C4/04C23C4/12
CPCE06B1/52C22C21/00C22C21/02C23C4/04
Inventor 朱明超
Owner 合肥市旺友门窗有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap