Anti-yellowing photocuring liquid acrylic glue and preparation method thereof

An acrylic adhesive and anti-yellowing technology, applied in adhesives, non-polymer organic compound adhesives, etc., can solve problems such as aging, easy yellowing, and short service life, and achieve moderate curing speed, convenient operation and control, and production low cost effect

Inactive Publication Date: 2017-08-04
东莞市卓翼新材料科技有限公司
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing transparent glue injection layer is prone to yellowing with the prolongation of use time, and it has aged in the environment of wind and rain, and its service life is short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A light-curing anti-yellowing liquid acrylic adhesive, comprising the following raw materials in parts by weight:

[0026] PMMA resin 15 parts

[0027] 40 parts of methyl methacrylate

[0028] Butyl methacrylate 25 parts

[0029] Leveling agent 0.3 part

[0030] 0.5 part of photoinitiator.

[0031] The PMMA resin has a melt index of 3.0g / 10min and a density of 1.17g / cm 3 of methyl hydroxymethacrylate.

[0032] The methyl methacrylate is a methyl methacrylate with a glass transition temperature of 104° C. and a relative density of 0.938.

[0033] The butyl methacrylate is butyl methacrylate with a glass transition temperature of 26° C. and a relative density of 0.887.

[0034] The photoinitiator is 2-hydroxy-2-methyl-1-phenylacetone.

[0035] A preparation method of light-curing anti-yellowing liquid acrylic adhesive. PMMA resin, methyl methacrylate and butyl methacrylate are heated to 65 ° C, kept warm for 2.5 hours and then lowered to room temperature, and a lev...

Embodiment 2

[0037] A light-curing anti-yellowing liquid acrylic adhesive, comprising the following raw materials in parts by weight:

[0038] PMMA resin 18 parts

[0039] 45 parts of methyl methacrylate

[0040] Butyl methacrylate 28 parts

[0041] Leveling agent 0.4 parts

[0042] 0.8 part of photoinitiator.

[0043] The PMMA resin has a melt index of 3.1g / 10min and a density of 1.18g / cm 3 of methyl hydroxymethacrylate.

[0044] The methyl methacrylate is a methyl methacrylate with a glass transition temperature of 104.5° C. and a relative density of 0.939.

[0045] The butyl methacrylate is butyl methacrylate with a glass transition temperature of 26.5° C. and a relative density of 0.888.

[0046] The photoinitiator is composed of 2-hydroxyl-2-methyl-1-phenylacetone, 1-hydroxycyclohexyl phenyl ketone and 2,4,6-trimethylbenzoylphenylphosphonic acid ethyl ester A mixture composed of a weight ratio of 1.5:0.8:1.

[0047] A preparation method of light-curing anti-yellowing liquid ac...

Embodiment 3

[0049] A light-curing anti-yellowing liquid acrylic adhesive, comprising the following raw materials in parts by weight:

[0050] PMMA resin 20 parts

[0051] 50 parts of methyl methacrylate

[0052] Butyl methacrylate 30 parts

[0053] Leveling agent 0.5 parts

[0054] Photoinitiator 1.0 parts.

[0055] The PMMA resin has a melt index of 3.2g / 10min and a density of 1.19g / cm 3 of methyl hydroxymethacrylate.

[0056] The methyl methacrylate is a methyl methacrylate with a glass transition temperature of 105° C. and a relative density of 0.940.

[0057] The butyl methacrylate is butyl methacrylate with a glass transition temperature of 27° C. and a relative density of 0.889.

[0058] The photoinitiator is composed of 2-hydroxyl-2-methyl-1-phenylacetone, 1-hydroxycyclohexyl phenyl ketone and 2,4,6-trimethylbenzoylphenylphosphonic acid ethyl ester A mixture composed in a weight ratio of 2:1:1.

[0059]A preparation method of light-curing anti-yellowing liquid acrylic adhes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melt indexaaaaaaaaaa
Densityaaaaaaaaaa
Glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of advertisement word manufacturing, in particular to anti-yellowing photocuring liquid acrylic glue and a preparation method of the acrylic glue. The acrylic glue comprises the following raw materials in parts by weight: 15-25 parts of PMMA (polymethyl methacrylate) resin, 40-60 parts of methyl methacrylate, 25-35 parts of butyl methacrylate, 0.3-0.7 part of light homogenizer and 0.5-1.5 parts of photoinitiator. The acrylic glue resists yellowing and ageing, is low in viscosity and good in leveling property and defoaming performance, can be cured at room temperature or moderate temperature and is moderate in curing velocity; a cured product is better in toughness and flexibility, good in transparency, smooth and bright in surface strong in adhesion and free from bubbles; and the cured product further has good solvent resistance and excellent moisture resistance and water resistance.

Description

technical field [0001] The invention relates to the technical field of advertising letter making, in particular to a light-curing anti-yellowing liquid acrylic glue and a preparation method thereof. Background technique [0002] Resin cast luminous characters, because the color and light transmittance of the resin can be freely adjusted, make up for the shortcomings of acrylic plate luminous characters in single color selection and non-adjustable light transmittance, and become the new darling of the advertising sign industry. The structure of the common three-dimensional resin casting luminous nameplates on the market includes metal letter shells (made of iron sheet paint, stainless steel, aluminum and other metals), LED light sources and transparent glue injection layers. [0003] The existing transparent glue injection layer is prone to yellowing with the prolongation of use time, and has aged under the use environment of wind and rain, and has a short service life. Con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J4/06C09J4/02
CPCC09J4/06C08F265/06
Inventor 查武唐丽娟
Owner 东莞市卓翼新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More