Oral repair material and preparation method thereof

A technology for oral restoration and zinc oxide, applied in the oral field, can solve the problems of not having both mechanical properties and processing properties, and limiting the scope of clinical applications.

Inactive Publication Date: 2017-06-30
朱一军
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current ceramic materials often cannot have both mechanical properties and processing properties, which limits the scope of clinical applications.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oral repair material and preparation method thereof
  • Oral repair material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] An oral restorative material, in terms of mass percentage, comprising the following components: 8% zinc oxide, 1% cerium oxide, 0.5% tantalum oxide, 2% borax, 1% polyether ether ketone, 2% sodium fluoride, monofluoride Sodium phosphate 2%, sodium stannate 2%, nano-montmorillonite 8%, triethylenediamine 0.1%, resorcinol monobenzoate 0.1%, and the balance is zirconia.

[0026] The preparation method of the above-mentioned oral restorative material, the specific steps are as follows:

[0027] (1) Dissolve zirconium oxychloride in ethanol, and then add zinc oxide, cerium oxide and tantalum oxide at 60°C; the molar amount of zirconium oxychloride is obtained by converting the formula quantity of zirconia, and zirconium oxychloride and The mass volume ratio of ethanol is 1g:30mL;

[0028] (2) Cool to 25°C, add polyethylene glycol 400 (the amount added is 1% of the mass of zirconium oxychloride), ultrasonically wash, and put it into a high-pressure reactor for reaction (react...

Embodiment 2

[0031] An oral restorative material, in terms of mass percentage, comprising the following components: 12% zinc oxide, 2% cerium oxide, 1% tantalum oxide, 3% borax, 3% polyether ether ketone, 4% sodium fluoride, monofluoride Sodium phosphate 4%, sodium stannate 3%, nano-montmorillonite 10%, triethylenediamine 0.2%, resorcinol monobenzoate 0.2%, and the balance is zirconia.

[0032] The preparation method of the above-mentioned oral restorative material, the specific steps are as follows:

[0033] (1) Dissolve zirconium oxychloride in ethanol, and then add zinc oxide, cerium oxide and tantalum oxide at 80°C; the molar amount of zirconium oxychloride is obtained by converting the formula quantity of zirconia, and zirconium oxychloride and The mass volume ratio of ethanol is 1g:40mL;

[0034] (2) Cool to 25°C, add polyethylene glycol 400 (the amount added is 1.5% of the mass of zirconium oxychloride), ultrasonically wash, put it into a high-pressure reactor for reaction (reactio...

Embodiment 3

[0037] An oral restorative material, in terms of mass percentage, comprising the following components: 9% zinc oxide, 1.2% cerium oxide, 0.6% tantalum oxide, 2.2% borax, 1.5% polyether ether ketone, 2.5% sodium fluoride, monofluoride Sodium phosphate 2.5%, sodium stannate 2.2%, nano-montmorillonite 8.2%, triethylenediamine 0.1%, resorcinol monobenzoate 0.1%, and the balance is zirconia.

[0038] The preparation method of the above-mentioned oral restorative material, the specific steps are as follows:

[0039] (1) Dissolve zirconium oxychloride in ethanol, and then add zinc oxide, cerium oxide and tantalum oxide at 60°C; the molar amount of zirconium oxychloride is obtained by converting the formula quantity of zirconia, and zirconium oxychloride and The mass volume ratio of ethanol is 1g:30mL;

[0040] (2) Cool to 25°C, add polyethylene glycol 400 (the amount added is 1% of the mass of zirconium oxychloride), ultrasonically wash, and put it into a high-pressure reactor for r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
refractive indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses an oral repair material and a preparation method thereof. The oral repair material comprises the following components in percentage by mass: 8-12% of zinc oxide, 1-2% of cerium oxide, 0.5-1% of tantalum oxide, 2-3% of borax, 1-3% of polyetheretherketone, 2-4% of sodium fluoride, 2-4% of sodium monofluorophosphate, 2-3% of sodium stannate, 8-10% of nanometer montmorillonite, 0.1-0.2% of triethylene diamine, 0.1-0.2% of resorcinol monobenzoate and the balance of zirconium oxide. The zirconium oxide is used as a main material, the zinc oxide is used as an auxiliary material, and the cerium oxide and the tantalum oxide are also added, so that the basic mechanical strength of the obtained oral repair material is ensured; the borax achieves a bactericidal effect; the polyetheretherketone improves the wear resistance and the corrosion resistance of the oral repair material; the sodium fluoride, the sodium monofluorophosphate and the sodium stannate are coordinated to improve the bactericidal effect; the nanometer montmorillonite facilitates uniform dispersion of the components so as to improve the mechanical properties of the obtained material; the triethylene diamine and the resorcinol monobenzoate help to improve the light stability of the product.

Description

technical field [0001] The invention relates to an oral restorative material, in particular to an oral restorative material and a preparation method thereof. It belongs to the field of dental technology. Background technique [0002] Oral restoration refers to the treatment of soft and hard tissue defects in the oral cavity and maxillofacial region using artificial restorations, and also includes the treatment of periodontal disease and temporomandibular joint disease through restoration methods. With the improvement of living standards and the diversification of diet, there are more and more patients with tooth loss caused by dental caries, periodontitis and tooth damage in my country. Therefore, the development of oral restorative materials and products has higher and higher requirements both in quantity and quality. [0003] The structure, color and texture of ceramic materials are similar to human teeth, and they have good biocompatibility. They are the most commonly u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/48C04B35/626A61K6/02A61K6/00
CPCA61K6/71A61K6/74A61K6/76A61K6/818C04B35/48C04B35/62605C04B35/62645C04B2235/3201C04B2235/3229C04B2235/3251C04B2235/3284C04B2235/3293C04B2235/3409C04B2235/349C04B2235/445C04B2235/447
Inventor 朱一军
Owner 朱一军
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com