Functional master batch for improving polyethylene packaging film toughness

A polyethylene packaging and functional masterbatch technology, applied in the field of functional masterbatches, can solve problems such as tensile toughness, weak puncture resistance, easy permanent deformation of the package, and impact on service life, so as to improve puncture resistance and performance Consistency, the effect of improving aging resistance

Inactive Publication Date: 2017-06-09
长兴天晟能源科技有限公司
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems that the existing polyethylene packaging film has weak tensile toughness and puncture resistance, it is easy to be permanently deformed and the package body is broken when it is torn by external force, which affects the service life. The functional masterbatch in polyethylene material can improve the tensile toughness and puncture resistance of polyethylene packaging film, make polyethylene packaging film not easy to deform under external force tearing, and improve the service life of polyethylene packaging film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A functional masterbatch for improving the toughness of polyethylene packaging film, prepared from the following components in parts by weight: 80 g of carrier resin, 20 g of toughening agent, 10 g of low-density polypropylene resin, 1 g of curing agent, and oxidized polyethylene 0.6 g of wax, 0.6 g of white carbon black, 0.5 g of antioxidant 1076, and 0.5 g of coupling agent, wherein the carrier resin is polyethylene resin to improve the compatibility between functional masterbatch and polyethylene material, and the components of toughening agent The weight ratio is: milk fiber: corn fiber: graphene=1:1.2:0.5, the curing agent is preferably aminoethylpiperazine, which has good chemical corrosion resistance, and the coupling agent is preferably a silane coupling agent.

[0022] The preparation method of the functional master batch improving the toughness of polyethylene packaging film comprises the following steps:

[0023] (1) Put the raw material components in parts b...

Embodiment 2

[0030] A functional masterbatch for improving the toughness of polyethylene packaging film, prepared from the following components in parts by weight: 90 g of carrier resin, 22.5 g of toughening agent, 12.5 g of low-density polypropylene resin, 1.5 g of curing agent, and oxidized polyethylene 0.8 g of wax, 0.7 g of white carbon black, 0.65 g of antioxidant 1076, and 0.75 g of coupling agent, wherein the carrier resin is polyethylene resin to improve the compatibility of functional masterbatch and polyethylene materials, and the components of toughening agent The weight ratio is: milk fiber: corn fiber: graphene=1:1.35:0.6, the curing agent is preferably aminoethylpiperazine, which has good chemical corrosion resistance, and the coupling agent is preferably a silane coupling agent.

[0031] The preparation method of the functional master batch improving the toughness of polyethylene packaging film comprises the following steps:

[0032] (1) Put the raw material components in pa...

Embodiment 3

[0039] A functional masterbatch for improving the toughness of polyethylene packaging film, prepared from the following components in parts by weight: 100 g of carrier resin, 25 g of toughening agent, 15 g of low-density polypropylene resin, 2 g of curing agent, and oxidized polyethylene Wax 1.0 g, white carbon black 0.8 g, antioxidant 1076 0.8 g, coupling agent 1.0 g, wherein the carrier resin is polyethylene resin to improve the compatibility of functional masterbatch and polyethylene material, the components of toughening agent The weight ratio is: milk fiber: corn fiber: graphene=1:1.5:0.7, the curing agent is preferably aminoethylpiperazine, which has good chemical corrosion resistance, and the coupling agent is preferably a silane coupling agent.

[0040] The preparation method of the functional master batch improving the toughness of polyethylene packaging film comprises the following steps:

[0041] (1) Put the raw material components in parts by weight into a mixing m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of functional master batches, and discloses a functional master batch for improving polyethylene packaging film toughness. The functional master batch is prepared from the following components in parts by weight: 80-100 parts of carrier resin, 20-25 parts of toughener, 10-15 parts of low-density polypropylene resin, 1-2 parts of curing agent, 0.6-1.0 part of oxidized polyethylene wax, 0.6-0.8 part of white carbon black, 0.5-0.8 part of antioxidant 1076 and 0.5-1.0 part of coupling agent. The carrier resin is a polyethylene resin; and the toughener is composed of milk fibers, corn fibers and graphene. Under the synergic actions of the characteristics of stretching resistance, high strength and scratch resistance of the milk fibers, corn fibers, low-density polypropylene and the like, the functional master batch improves the stretching toughness and puncture resistance of the polyethylene packaging film product, enhances the aging resistance and mold resistance of the polyethylene packaging film product and prolongs the service life of the polyethylene packaging film.

Description

technical field [0001] The invention relates to the field of functional master batches, in particular to a functional master batch for improving the toughness of polyethylene packaging films. Background technique [0002] Polyethylene (PE) is a kind of thermoplastic resin prepared by ethylene polymerization. It has excellent electrical insulation performance, chemical stability, low water absorption and can withstand most acid and alkali corrosion. Therefore, it is one of the preferred materials for making packaging films, especially It is the outer packaging film for the whole beer, canned beverage, and bottled beverage. This kind of packaging film is not easy to be damaged, not afraid of moisture, and is very convenient to use. However, this kind of packaging film has low tensile toughness and unstable puncture resistance. It is prone to permanent deformation and often breaks the package when pulled by an external force, which leads to a short service life. Chinese patent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L67/04C08L89/00C08L33/20C08L23/12C08L23/30C08K13/02C08K3/04C08K3/36C08K5/134B29C47/92B29C48/92
CPCB29C48/92B29C2948/92704C08L23/06C08L2201/08C08L2203/16C08L2205/035C08L2205/16C08L67/04C08L89/00C08L33/20C08L23/12C08L23/30C08K13/02C08K3/04C08K3/36C08K5/1345
Inventor 佘海中
Owner 长兴天晟能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com