A kind of betaine type amphoteric surfactant and preparation method thereof

A technology of surfactant and betaine, which is applied in the field of betaine-type amphoteric surfactant and its preparation, can solve the problems of low content of active substances, difficult reduction of acid value, and increased production cost, and achieve mild performance and low production cost. Low, the effect of increasing productivity

Active Publication Date: 2018-09-18
PANJIN LIAOHE OILFIELD YULONG RUIDA PETROLEUM TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Mainly there are the following problems: 1) the acid value of the amidation reaction is difficult to reduce, so that the yield is on the low side and the production cost is higher; 2) most of them use mixed oil acids as raw materials for production, but this type of oil acids contains more impurities, and the properties Unstable, also have methyl oleate as raw material for production, but further increase the production cost; 3) The purification process is relatively simple, and the active substance content of the obtained product is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of betaine type amphoteric surfactant and preparation method thereof
  • A kind of betaine type amphoteric surfactant and preparation method thereof
  • A kind of betaine type amphoteric surfactant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The preparation method of above-mentioned betaine type amphoteric surfactant comprises the following steps:

[0036] 1) Amidation reaction: Melt natural oil acid, add 3-dimethylaminopropylamine, mix well, add catalyst to carry out

[0037] For amidation reaction, add 4A molecular sieve after reacting for 5-7 hours, continue the reaction, and remove unreacted

[0038] 3-dimethylaminopropylamine and natural oleic acid to obtain alkyl amidopropyl dimethyl tertiary amine;

[0039] 2) Quaternization reaction: Add alkyl amidopropyl dimethyl tertiary amine and sodium chloroacetate to the reactor, add water until the sodium chloroacetate dissolves

[0040] solution is complete, then add isopropanol, adjust the pH value to 7-8, carry out quaternization reaction, and remove isopropanol after the reaction is completed.

[0041] propanol, water and unreacted sodium chloroacetate to obtain a betaine-type amphoteric surfactant.

[0042] Preferably, the structural formula of the na...

Embodiment 1

[0052] A kind of preparation method of betaine type amphoteric surfactant comprises the following steps:

[0053] 1) Amidation reaction: Add 25.6475g of palmitic acid into a three-necked flask equipped with a reflux condenser, raise the temperature to 80°C to slowly melt the palmitic acid, and then add 10.728g of 3-dimethylaminopropylamine dropwise while stirring (The molar ratio of palmitic acid to 3-dimethylaminopropylamine is 1:1.05), after 30 minutes of dripping, 0.177g of KOH was added as a catalyst, and the temperature was raised to 160°C for amidation reaction. After 6 hours of reaction, 10g of 4A was added Molecular sieves, continue to react for 5h, after the completion of the reaction, first remove unreacted 3-dimethylaminopropylamine and by-product water in the crude product by distillation under reduced pressure, and then use 1% Na 2 CO 3 The solution was washed to remove unreacted palmitic acid to obtain palmitamidopropyl dimethyl tertiary amine with a yield of 93...

Embodiment 2

[0060] A kind of preparation method of betaine type amphoteric surfactant comprises the following steps:

[0061] 1) Amidation reaction: Add 22.84g of myristic acid into a three-necked flask equipped with a reflux condenser, raise the temperature to 80°C to slowly melt the myristic acid, and then add 10.73g of 3-dimethylamine dropwise while stirring Dimethylaminopropylamine (the molar ratio of myristic acid to 3-dimethylaminopropylamine is 1:1.05), drop it in 30 minutes, then add 0.17g of NaOH as a catalyst, raise the temperature to 160°C, and carry out amidation reaction. After 6 hours of reaction, add 10g of 4A molecular sieves, continue to react for 5h, after the completion of the reaction, first remove the unreacted 3-dimethylaminopropylamine and by-product water in the crude product by distillation under reduced pressure, and then use 1% Na 2 CO 3 The solution was washed to remove unreacted myristic acid to obtain myristamidopropyldimethyl tertiary amine with a yield of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a betaine-type amphoteric surfactant and a preparation method thereof. The preparation method of the betaine-type amphoteric surfactant comprises the following steps: 1) amidation reaction: under the action of a catalyst, natural oil acid and 3‑ Dimethylaminopropylamine is subjected to amidation reaction, and the water generated by the reaction is removed in time by using 4A molecular sieves to obtain alkylamidopropyl dimethyl tertiary amine; 2) quaternization reaction: alkylamidopropyl dimethyl tertiary amine Perform quaternization reaction with sodium chloroacetate in a solvent to obtain a betaine-type amphoteric surfactant. The amphoteric surfactant group of the invention contains amide bonds, which changes the performance of the molecule, has better foam stability, mild performance, and its emulsifying performance is obviously better than that of the lauryl betaine surfactant. The preparation method of the invention has simple process, low production cost, green and natural raw materials, and absorbs water produced in the amidation reaction process through 4A molecular sieves, thereby improving the yield.

Description

technical field [0001] The invention relates to a betaine type amphoteric surfactant and a preparation method thereof. Background technique [0002] Amphoteric surfactants refer to surfactants that have one or more positive and negative charge centers (or dipole centers) connected by bridge chains (hydrocarbon chains, fluorocarbon chains, etc.) in the same molecular structure. Good biodegradability, low toxicity, antistatic. Amphoteric surfactants first appeared in the 1930s, and were gradually developed and applied later. However, the research and development of amphoteric surfactants in my country started relatively late, and there is a big gap in variety and output compared with other developed countries. [0003] Domestic surfactants are mainly anionic surfactants and nonionic surfactants. These two types of surfactants will pollute the environment and are generally difficult to biodegrade. Alkyl amidopropyl betaine is a new type of high-efficiency amphoteric surfactan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07C233/36C07C231/12B01F17/28C09K23/28
CPCC07C231/02C07C231/12C07C233/36C09K23/00
Inventor 尚小琴王信锐刘鹏刘汝峰江慧华陈浩亮
Owner PANJIN LIAOHE OILFIELD YULONG RUIDA PETROLEUM TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com