Process of electron beam cold bed furnace for recycling and remelting TC11 scraps

An electron beam cooling bed furnace, TC11 technology, applied in the field of titanium alloy ingot preparation, can solve problems such as difficulty in the amount and method of adding Al element, volatilization loss of Al element, and chemical composition cannot meet the standard, etc., to solve the problem of Al element The amount of addition is difficult to control, easy to operate, and the effect is good.

Active Publication Date: 2017-05-31
QINGHAI JUNENG TITANIUM IND CO LTD
View PDF7 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the main alloying element Al in TC11 scrap is much larger than the matrix element, if it is directly remelted, the Al element will inevitably be volatilized and lost in a large area, so that the chemical composition of the final TC11 ingot cannot meet the standard
The supplementary amount and supplementary method of Al element are so difficult that the technology of recovering remelted TC11 scrap from electron beam cooling hearth furnace has not yet been reported.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process of electron beam cold bed furnace for recycling and remelting TC11 scraps
  • Process of electron beam cold bed furnace for recycling and remelting TC11 scraps
  • Process of electron beam cold bed furnace for recycling and remelting TC11 scraps

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0038] A process for recovering and remelting TC11 shavings in an electron beam cooling hearth furnace, comprising the following process: material preparation→titanium frame weldingcutting of Al plates→swinging materials→dryingsmelting in the furnace. The process steps include: Step 1: Combined with the size of the material box, select a thin titanium plate to weld a titanium frame and weigh it; Step 2: According to the bulk density of the TC11 scrap, estimate the weight of the TC11 scrap that can be contained in the titanium frame, and calculate Add the amount of Al plate and cut it according to the requirements; Step 3: Put the TC11 scraps and Al plates into the titanium frame, and dry the material; Step 4: Send the dried material into the electron beam cooling bed Furnace for smelting, one smelting to get TC11 titanium alloy.

[0039] Further, the welding of the titanium frame in step 1 includes the following steps:

[0040] Step 11: Select a titanium plate with a purity...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a process of an electron beam cold bed furnace for recycling and remelting TC11 scraps, and belongs to the technical field of titanium alloy preparation. The method comprises the steps that S1, in combination with the size of a material box, a thin titanium plate is selected to be welded into a titanium frame, and weighing is carried out; S2, the weight of the TC11 scraps capable of being contained in the titanium frame is estimated according to the stacking density of the TC11 scraps, the adding amount of an A1 plate is calculated, and cutting is carried out according to requirements; S3, the TC11 scraps and the A1 plate are stacked to be placed in the titanium frame, and materials are dried; and S4, the dried materials are fed into the electron beam cold bed furnace for smelting, and TC11 titanium alloy is obtained through one time of smelting. The reliable, practical and efficient treatment scheme for recycling and remelting the TC11 scraps at low cost is provided, meanwhile, the process is coherent in technological process, convenient and fast to operate and thorough in treatment, and the need of recycling and remelting the TC11 scraps of an electrode incapable of being pressed can be met.

Description

technical field [0001] The invention relates to a process for recovering and remelting TC11 scrap, in particular to a process for recycling and remelting TC11 scrap in an electron beam cooling hearth furnace, belonging to the technical field of titanium alloy ingot preparation. Background technique [0002] The economic development model of recycling renewable resources and continuous recycling of materials is currently becoming a global trend, and the renewable resource recycling industry that follows the path of sustainable development has become a key support object of the state. Titanium alloy waste is a renewable resource, and its comprehensive utilization saves a lot of energy compared with the development of primary mines. TC11 alloy has a high melting point, strong corrosion resistance, high specific strength, and good plasticity. It is an ideal aerospace engineering structural material. From TC11 rough ingot to light ingot, the amount of chips generated by drilling ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22B9/22C22B34/12
CPCC22B9/228C22B34/1295
Inventor 唐增辉张志斌周武杜彬薛倩芸王福清
Owner QINGHAI JUNENG TITANIUM IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products